KARAKTERISTIK SIFAT MEKANIK DAN STRUKTUR MIKRO PELAT BAJA KARBON RENDAH PASKA PERLAKUAN PANAS

ISKANDARSYAH WICAKSONO, . (2021) KARAKTERISTIK SIFAT MEKANIK DAN STRUKTUR MIKRO PELAT BAJA KARBON RENDAH PASKA PERLAKUAN PANAS. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (2MB)
[img] Text
BAB 1.pdf

Download (232kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (672kB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (259kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (501kB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (221kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (289kB)
[img] Text
LAMPIRAN.pdf
Restricted to Registered users only

Download (884kB) | Request a copy

Abstract

Baja karbon rendah termasuk logam yang banyak digunakan karena baja ini memiliki keuletan yang tinggi dan mudah di bentuk, tatapi kekuatan dan kekerasannya rendah. Untuk memperluas penggunaan baja karbon rendah, diperlukan peningkatan sifat mekaniknya terutama dari segi kekuatan dan kekerasan. Salah satu cara untuk meningkatkan sifat mekanik tersebut dapat dilakukan melalui proses perlakuan panas. Pada penelitian ini material yang digunakan yaitu pelat baja karbon rendah yang dilakukan perlakuan panas menggunakan furnace hingga suhu 950°C. Ketika mencapai suhu 950°C, kemudian ditahan selama 15 menit agar suhu pemanasan merata. Setelah itu dilakukan variasi media pendinginan aquadest, minyak goreng, oli 10W-40, dan didalam tungku pintu terbuka. Selanjutnya dilakukan beberapa pengujian, yaitu pengujian komposisi kimia pada material sebelum dilakukan perlakuan panas untuk mengetahui unsur yang terdapat pada material, pengujian tarik untuk mengetahui tegangan – regangan, dan pengujian struktur mikro untuk mengetaui struktur yang terbentuk. Hasil penelitian menunjukkan bahwa sampel dalam pengujian ini menggunakan jenis baja karbon rendah dengan unsur karbon 0,0524%. Kekuatan tarik paling tinggi terdapat pada sampel baja karbon rendah yang tidak dilakukan perlakuan panas dengan nilai kekuatan tarik sebesar 375,75 MPa, sedangkan pada baja dengan media pendingin aquadest 351,07 MPa, oli 10W-40 332,71 MPa, minyak goreng 318,35 MPa, dan tungku pintu terbuka 208,48 MPa. Untuk nilai regangan tertinggi terdapat pada media pendinginan didalam tungku pintu terbuka yaitu 38,77%, diikuti tanpa perlakuan panas 36,93%, media aquadest 28,81%, media oli 27,28%, dan minyak goreng 25,49%. Pada pengamatan struktur mikro pada material sebelum dan sesudah dilakukan perlakuan panas hanya didapatkan ferit dan perlit. Low carbon steel is a metal that is widely used because this steel has high ductility and is easy to machine, but has low strength and hardness. To expand the use of carbon steel improvements in strength and hardness is required. One of the ways to improve these mechanical properties can be done through a heat treatment process. In this study, the materials used were plate low carbon steel which is heat treated using a furnace up to 950°C. When it reaches a temperature of 950°C, then it is holding time for 15 minutes, so that the heating temperature is evenly distributed. After that, it was by a variation cooling media of aquadest, vegetable oil, synthetic oil 10W-40, and furnace with open lid. Furthermore, testing the chemical composition of the material before heat treatment is carried out to determine the elements present in the material, tensile testing to determine stress – strain, and microstructure testing to determine the structure formed. The results showed that the material used was low carbon steel with 0,0524 wt%C. The highest stress was found in the low carbon steel sample which raw material with a stress value of 375,75 MPa, while in steel with cooling media aquadest 351,07 MPa, oil 10W-40 332,71 MPa, vegetable oil 318,35 MPa, and furnace with open lid 208,48 MPa. For the highest strain found in a furnace with open lid of 38,77%, follow by before heat treatment 36,93%, aquadest 28,81%, and lowest of strains found in the vegetable oil 25,49%, In observing the microstructure only ferrite and pearlite of material before and after heat treatment.

Item Type: Thesis (Sarjana)
Additional Information: 1). Ferry Budhi Susetyo, M.T., M.Si. ; 2). Drs. H. Syamsuir. M.T.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Users 10140 not found.
Date Deposited: 15 Mar 2021 04:36
Last Modified: 15 Mar 2021 04:36
URI: http://repository.unj.ac.id/id/eprint/14847

Actions (login required)

View Item View Item