PENGARUH JENIS MERK COATING NANO CERAMIC TERHADAP DAYA KILAP, KEKERASAN DAN KETAHANAN PANAS PADA CAT KENDARAAN

DONNI DWIKI RAMADHAN, . (2021) PENGARUH JENIS MERK COATING NANO CERAMIC TERHADAP DAYA KILAP, KEKERASAN DAN KETAHANAN PANAS PADA CAT KENDARAAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (879kB)
[img] Text
BAB I.pdf

Download (329kB)
[img] Text
BAB II.pdf
Restricted to Registered users only

Download (488kB) | Request a copy
[img] Text
BAB III.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB IV.pdf
Restricted to Registered users only

Download (658kB) | Request a copy
[img] Text
BAB V.pdf
Restricted to Registered users only

Download (293kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (195kB)
[img] Text
LAMPIRAN.pdf
Restricted to Registered users only

Download (1MB) | Request a copy

Abstract

Perawatan pada cat kendaraan sangat perlu dilakukan guna memperpanjang usia cat dan mempertahankan keindahan cat kendaraan tersebut. Penelitian ini bertujuan untuk membuktikan Pengaruh Jenis Merk Coating Nano Ceramic Terhadap Daya Kilap, Kekerasan dan Ketahanan Panas Pada Cat Kendaraan. Metode yang digunakan pada penelitian ini adalah eksperimen. Berdasarkan hasil pengujian coating nano ceramic berpengaruh terhadap daya kilap dibuktikan dengan sampel tanpa menggunakan coating nilai kilap sebesar 82,43 GU sedangkan nilai tertinggi sampel menggunakan coating 89,80 GU. Penggunaan coating juga berpengaruh pada kekerasan cat kendaraan dimana sampel tanpa menggunakan coating senilai 73,92 Shore D sedangkan nilai kekerasan tertinggi sampel menggunakan coating sebesar 80,92 Shore D. Coating Nano Ceramic juga berpengaruh terhadap ketahanan panas cat kendaraan dimana pada suhu 80℃ waktu perubahan warna terjadi pada 14 hari dan perubahan fisik terjadi pada 45 hari sedangkan pada suhu 200℃ waktu perubahan warna terjadi pada 120 menit dan perubahan fisik terjadi pada 331,67 menit. Maintenance on vehicle paint is very necessary in order to extend the life of the paint and maintain the beauty of the vehicle paint. This study aims to prove the effect of Nano Ceramic Coating Brand on Glossiness, Hardness and Heat Resistance in Vehicle Paint. The method used in this research is experimental. Based on the test results, the nano ceramic coating has an effect on glossiness as evidenced by the sample without using a coating, the gloss value is 82.43 GU, while the highest value of the sample uses a coating of 89.80 GU. The use of coating also affects the hardness of vehicle paint where samples without using a coating are worth 73.92 Shore D, while the highest hardness values for samples using coating are 80.92 Shore D. Nano Ceramic coating also affects the heat resistance of vehicle paint where at a temperature of 80℃ the color change occurs at 14 days and physical changes occur at 45 days while at 200℃ the color change time occurs at 120 minutes and physical changes occur at 331.67 minutes.

Item Type: Thesis (Sarjana)
Additional Information: 1). Drs. Adi Tri Tyassmadi, M.Pd. ; 2). Dr. Imam Basori, M.T.
Subjects: Teknologi dan Ilmu Terapan > Otomotif, Astronotika
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Users 10077 not found.
Date Deposited: 15 Mar 2021 04:49
Last Modified: 15 Mar 2021 04:49
URI: http://repository.unj.ac.id/id/eprint/14876

Actions (login required)

View Item View Item