UJI KUAT TEKAN DAN POROSITAS MORTAR DENGAN PENAMBAHAN LIMBAH SERBUK KACA

DELLA APRILLIA, . (2021) UJI KUAT TEKAN DAN POROSITAS MORTAR DENGAN PENAMBAHAN LIMBAH SERBUK KACA. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. COVER.pdf.pdf Download (1MB)
	Text 2. BAB 1.pdf.pdf Download (358kB)
	Text 3. BAB 2.pdf.pdf Restricted to Registered users only Download (559kB) | Request a copy
	Text 4. BAB 3.pdf.pdf Restricted to Registered users only Download (484kB) | Request a copy
	Text 5. BAB 4.pdf.pdf Restricted to Registered users only Download (397kB) | Request a copy
	Text 6. BAB 5.pdf.pdf Restricted to Registered users only Download (146kB) | Request a copy
	Text 7. DAFTAR PUSTAKA.pdf.pdf Download (145kB)
	Text 8. LAMPIRAN.pdf.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Pemanfaatan limbah serbuk kaca sebagai bahan alternatif pembuatan mortar dapat meningkatkan kuat tekan dan efektifitas beton. Pembuatan mortar pada penelitian ini menggunakan standar SNI 6882 - 2014 dengan persentase 0%; 2,5%; 5%; 7,5%; 10%, dan 12,5% dari berat asli semen. Penelitian ini bertujuan untuk memanfaatkan limbah kimia serbuk kaca sebagai bahan tambah pembuatan mortar untuk mengetahui titik maksimum kuat tekan dan porositas mortar yang akan dicampur serbuk kaca. Metode penelitian ini adalah eksperimen. Hasil penelitian ini menunjukkan; (1) penambahan serbuk kaca pada senyawa mortar menyebabkan flow table menurun; (2) massa jenis mortar cenderung menurun dengan penambahan serbuk kaca; (3) Proporsi porositas lebih menurun dari pada mortar kontrol, (4) variasi tepat yang dapat digunakan pada pelapisan transram mortar tipe M dengan kuat tekan pada perencanaan 17,2 Mpa, (5) Kuat tekan maksimum ditemukan pada variasi serbuk kaca dengan persentase 12,5% atau 15,1 Mpa; (6) dan serbuk kaca sebagai bahan tambah semen dengan persentase tersebut mempengaruhi konsistensi, massa jenis, porositas, dan kuat tekan mortar. The using of glass powder waste as an alternative substance of mortar manufacture could increase the compressive strength and the effectiveness of concrete. The making of mortar in this research used the standart of SNI 6882 – 2014 with percentages of 0%; 2,5%;5%;7,5%;10%, and 12,5% from the original weight of cement. This study aims at utilizing the chemical waste of glass powder as a material added of the making of mortar for knowing the maximum point of the compressive strength and the porosity of mortar that will be mixed with glass powder. The method of this study was experiment. The results of this research show; (1) the addition of glass powder in mortar’s compound caused the decrease of the flow table; (2) the density of mortar tends to decrease with the addition of glass powder; (3) the proportion of the porosity was more decrease than the control mortar, (4) the exact variations that can be used in the M type of mortar transram’s plastering with the compressive strength in the planning of 17,2 Mpa, (5) the most maximum of the compressive strength was found in the variation of glass powder with the percentage of 12,5% or 15,1 Mpa; (6) and glass powder as a material added of cement with those percentages has affected the consistency, the density, the porosity, and the compressive strength of mortar.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Kusno Adi Sambowo, S.T, Ph.D ; 2). Dra. Rosmawita Saleh, M.Pd
Subjects:	Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 10298 not found.
Date Deposited:	16 Mar 2021 04:44
Last Modified:	16 Mar 2021 04:44
URI:	http://repository.unj.ac.id/id/eprint/14955

Actions (login required)

View Item