KARAKTERISTIK PAVING BLOCK ABU SEKAM PADI DENGAN PENAMBAHAN SERBUK KACA

ANDREANSYAH, . (2021) KARAKTERISTIK PAVING BLOCK ABU SEKAM PADI DENGAN PENAMBAHAN SERBUK KACA. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (204kB)
	Text BAB 2.pdf Restricted to Registered users only Download (338kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (436kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (378kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (124kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (193kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

*ABSTRAK* Kandungan yang dimiliki abu sekam padi memiliki kesamaan seperti yang dimiliki semen yaitu mempunyai kandungan silika yang tinggi. Namun demikian aplikasi abu sekam padi pada bahan bangunan menjadikan karakteristik material yang mudah menyerap air sehingga dapat mengurangi mutu dari bahan. Serbuk kaca memiliki karakteristik zero water absorption dimanfaatkan untuk mengurangi penyerapan air yang tinggi pada material dengan abu sekam padi. Penelitian ini bertujuan untuk mengetahui karakteristik fisik dan mekanik paving block abu sekam padi dengan penambahan serbuk kaca yang divariasikan terhadap berat semen. Metode yang digunakan pada penelitian ini yaitu metode eksperimen pada paving block berbasis abu sekam padi dengan kadar 10% dari berat semen dengan ditambahkan serbuk kaca yang divariasikan sebesar 0%, 2,5%, 5%, 7,5% dan 10% terhadap berat semen. Benda uji di uji pada umur 28 hari sesuai dengan SNI 03-0691-1996. Benda uji berukuran 210 mm x 105 mm x 80 mm. Jenis pengujian yang dilakukan adalah uji tampak dan ukuran, uji kuat tekan, uji ketahanan aus, dan uji daya serap air. Hasil pengujian menunjukkan bahwa penambahan serbuk limbah botol kaca dapat meningkatkan mutu paving block berbasis abu sekam padi. Didapatkan nilai kuat tekan untuk penambahan serbuk kaca 0%, 2,5%, 5%, 7,5%, dan 10% berturut-turut adalah 29,80 MPa, 33,72 MPa, 40,14 MPa, 37,44 MPa, dan 31,75 MPa. Semua paving block termasuk ke dalam mutu A pada pengujian ketahanan aus. Sedangkan pada pengujian pengujian daya serap air, paving block abu sekam padi dengan 0% serbuk kaca tergolong ke dalam mutu C, sedangkan paving block abu sekam padi dengan penambahan 2,5% serbuk kaca tergolong ke dalam mutu B dan untuk variasi 5%, 7,5%, dan 10% masuk dalam klasifikasi mutu A. Kata kunci: Paving Block, Abu Sekam Padi, Serbuk Kaca, Kuat Tekan, Ketahanan Aus, Daya Serap Air.  *ABSTRACT* The content of rice husk ash has similarities as cement has a high silica content. However, the application of rice husk ash in building materials makes the material characteristics that easily absorb water so as to reduce the quality of the material. Glass powder has the characteristic of zero water absorption is used to reduce the absorption of high water in materials with rice husk ash. This study aims to find out the physical and mechanical characteristics of paving blocks of rice husk ash with the addition of glass powder that is variedagainst the weight of cement. The method used in this study is an experimental method on paving blocks based on rice husk ash with a content of 10% of the weight of cement with added glass powder that varies by 0%, 2.5%, 5%, 7.5% and 10% against the weight of cement. Test objects are tested at the age of 28 days in accordance with SNI 03-0691-1996. Test objects are 210 mm x 105 mm x 80 mm in size. The types of tests performed are visible and size tests, press strength tests, wear resistance tests, and water absorption tests. The test results showed that the addition of glass bottle waste powder can improve the quality of paving blocks based on rice husk ash. Obtained strong press values for the addition of glass powder 0%, 2.5%, 5%, 7.5%, and 10% respectively are 29.80 MPa, 33.72 MPa, 40.14 MPa, 37.44 MPa, and 31.75 MPa. All paving blocks are included in the A grade on wear resistance testing. While in testing water absorption, paving block ash husk rice with 0% glass powder classified into quality C, while paving block ash husk rice with the addition of 2.5% glass powder classified into quality B and for variations of 5%, 7.5%, and 10% included in the classification of quality A. Keywords: Paving Block,Rice Husk Ash, Glass Powder, Strong Press, Wear Resistance, Water Absorption

Item Type:	Thesis (Sarjana)
Additional Information:	1) Sittati Musalamah, M.T.; 2) Kusno Adi Sambowo, Ph.D.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 12373 not found.
Date Deposited:	02 Sep 2021 21:51
Last Modified:	02 Sep 2021 21:51
URI:	http://repository.unj.ac.id/id/eprint/19316

Actions (login required)

View Item