PEMANFAATAN PLASTIK JENIS HDPE DAN PET DENGAN PENAMBAHAN TANAH DIATOMAE SEBAGAI AGREGAT RINGAN BUATAN DALAM CAMPURAN BETON RINGAN

ADELIA NURHAZIZA TRI UTAMI, . (2021) PEMANFAATAN PLASTIK JENIS HDPE DAN PET DENGAN PENAMBAHAN TANAH DIATOMAE SEBAGAI AGREGAT RINGAN BUATAN DALAM CAMPURAN BETON RINGAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (488kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (981kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (720kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (344kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (576kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (4MB) | Request a copy

Abstract

*ABSTRAK* Penelitian ini bertujuan untuk mengetahui kuat tekan beton ringan struktur dengan target kuat tekan 20 MPa dan modulus elastisitas beton ringan pada umur beton ringan 28 hari dari agregat ringan buatan DIAHPET terhadap batu apung dengan menggunakan faktor air semen (FAS) 0,39 dan kadar persentase agregat 0%, 25%, 50%, 75% dan 100%. Agregat DIAHPET akan dibuat dari limbah plastik jenis HDPE dan PET dengan penambahan tanah diatomae menjadi agregat kasar ringan buatan dalam campuran beton ringan. Dalam penelitian ini akan menggunakan metode penelitian eksperimen dengan benda uji silinder berdiameter 150 mm dan tinggi 300 mm sebanyak 5 sampel pada tiap variasi persentase subsitusi agregat DIAHPET. Pembuatan campuran beton menggunakan pedoman SNI 03-3449-2002. Hasil penelitian yang didapatkan menunjukkan dengan menggunakan agregat DIAHPET sebagai substitusi terhadap agregat batu apung pada beton ringan dapat meningkatkan kuat tekan dan modulus elastisitas beton. Kuat tekan beton ringan umur 42 hari pada variasi substitusi agregat DIAHPET 0%, 25%, 50%, 75% dan 100% terhadap batu apung berturut-turut adalah 2,55 MPa, 3,33 MPa, 6,02 MPa, 6,58 MPa, 10,33 MPa. Sementara kuat tekan beton ringan dikonversi ke umur 28 hari pada variasi persentase yang sama berturut-turut 2,41 MPa, 3,14 MPa, 5,69 MPa, 6,22 MPa, 9,77 MPa. Sedangkan untuk pengujian modulus elastisitas beton ringan dengan persentase yang sama berturut-turut adalah 245,61 MPa, 422,30 MPa, 480,58 MPa, 568,88 MPa, dan 730,96 MPa. Nilai kuat tekan dan modulus elastisitas maksimum terjadi pada variasi persentase agregat DIAHPET 100%. Kata Kunci: Beton Ringan, Agregat Ringan, Kuat Tekan, Modulus Elastisitas *ABSTRACT* The purpose of this study was to determine the compressive strength of lightweight concrete structures with a target compressive strength of 20 MPa and a modulus of elasticity of lightweight concrete at the age of 28 days lightweight concrete from lightweight aggregate made by DIAHPET against pumice aggregates with the use of water cement factor (FAS) 0.39 and percentage variation aggregates of 0%, 25%, 50%, 75% and 100%. DIAHPET aggregate will be made from HDPE and PET type plastic waste with the addition of diatomaceous earth into artificial lightweight coarse aggregate in a lightweight concrete mixture. In this research will be using the methods of experimental research with cylindrical specimens with a diameter of 150 mm and a height of 300 mm as many as 5 samples in each variation of the percentage of DIAHPET aggregate substitution. Making concrete mix using SNI 03-3449-2002 guidelines. The results obtained showed that using DIAHPET aggregate as a substitution to the pumice aggregate in lightweight concrete can increase the compressive strength and modulus of elasticity of concrete. The compressive strength of lightweight concrete aged 42 days at variations of DIAHPET aggregate substitution of 0%, 25%, 50%, 75% and 100% against pumice are 2.55 MPa, 3.33 MPa, 6.02 MPa, 6, 58 MPa, 10.33 MPa. While the compressive strength of lightweight concrete converted to the age of 28 days on the variation of the same percentage in a row to 2.41 MPa, 3,14 MPa, 5,69 MPa, 6,22 MPa, 9,77 MPa. As for testing the modulus of elasticity of lightweight concrete with the same percentage in a row is 245,61 MPa, 422,30 MPa, 480,58 MPa, 568,88 MPa, and 730,96 MPa. The value of compressive strength and modulus of elasticity maximum occurs on the variation of the percentage of the aggregate DIAHPET 100%. Keywords: Lightweight Concrete, Lightweight Aggregate, Compressive Strength, Modulus of Elasticity

Item Type:	Thesis (Sarjana)
Additional Information:	1) Anisah, M.T. 2) Ririt Aprilin S, M. Sc. Eng.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 12382 not found.
Date Deposited:	02 Sep 2021 22:03
Last Modified:	02 Sep 2021 22:03
URI:	http://repository.unj.ac.id/id/eprint/19349