PENGARUH PENGGUNAAN ABU DAUN BAMBU SEBAGAI PENGGANTI SEBAGIAN SEMEN TERHADAP KUAT TEKAN BETON SEBAGAI PENDUKUNG BAHAN AJAR MATA KULIAH TEKNOLOGI BETON

AJI FIRMANSYAH, . (2022) PENGARUH PENGGUNAAN ABU DAUN BAMBU SEBAGAI PENGGANTI SEBAGIAN SEMEN TERHADAP KUAT TEKAN BETON SEBAGAI PENDUKUNG BAHAN AJAR MATA KULIAH TEKNOLOGI BETON. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 2.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (3MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (329kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (641kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (8MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui nilai kuat tekan beton dimana penggunaan semen diganti sebagian oleh abu daun bambu dengan target kuat tekan 25 MPa pada umur beton 28 hari dengan mengggunakan faktor air semen (FAS) 0,5 dan kadar persentase abu daun bambu yang digunakan sebesar 0%, 5%, 7%, 9%, dan 11% dari total berat semen. Abu daun bambu yang digunakan berasal dari bambu jenis Andong. Pada penelitian ini menggunakan metode eksperimen dengan benda uji silinder berdiameter 15 cm dan tinggi 30 cm sebanyak 3 sampel pada tiap kadar persentase abu daun bambu. Rancangan campuran beton mengacu pada SNI 03-2834-2000. Hasil yang diperoleh menunjukkan bahwa abu daun bambu dapat meningkatkan kuat tekan beton jika dibandingkan dengan beton kontrol pada penelitian ini walau dalam peningkatakan yang tidak terlalu besar. Kuat tekan beton umur 28 hari pada kadar persentase abu daun bambu 0%, 5%, 7%, 9%, dan 11% secara berturut-turut adalah 16,448 MPa ; 18,768 MPa ; 18,297 MPa ; 14,958 MPa ; dan 12,827 MPa. The purpose of this study was to determine the compressive strength of concrete using bamboo leaf ash as a partial replacement of cement with a target compressive strength of 25 MPa at the age of 28 days with the use of water cement factor (FAS) 0,5 and variation percentage levels of bamboo leaf ash that be used are 0%, 5%, 7%, 9%, and 11% of the total weight of cement. The The amboo leaf ash used comes from Andong bamboo species. In this study use the experimental method with cylindrical specimens with a diameter of 15 cm and a height of 30 cm as many as 3 samples in each percentage level of bamboo leaf ash. Concrete mix design refers to SNI 03-2834-2000. The results obtained indicate that bamboo leaf ash can increase the compressive strength of concrete when compared to the control concrete in this study even though the increase is not too large. The compressive strength of concrete at the age of 28 days at 0%, 5%, 7%, 9%, and 11% percentages levels of bamboo leaf ash were 16,448 MPa ; 18,768 MPa ; 18,297 MPa ; 14,958 MPa ; dan 12,827 MPa.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Anisah, MT 2). Dr. Santoso Sri Handoyo, MT
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 13364 not found.
Date Deposited:	02 Mar 2022 01:02
Last Modified:	02 Mar 2022 01:02
URI:	http://repository.unj.ac.id/id/eprint/23164

Actions (login required)

View Item