PENGARUH SUBSTITUSI SEBAGIAN AGREGAT HALUS DENGAN PLASTIK JENIS HDPE DAN LDPE TERHADAP PERSYARATAN MUTU PAVING BLOCK SEBAGAI PENDUKUNG BAHAN AJAR MATA KULIAH PRAKTIK UJI BAHAN

NURA NIDA DWI KURNIA PUTRI, . (2022) PENGARUH SUBSTITUSI SEBAGIAN AGREGAT HALUS DENGAN PLASTIK JENIS HDPE DAN LDPE TERHADAP PERSYARATAN MUTU PAVING BLOCK SEBAGAI PENDUKUNG BAHAN AJAR MATA KULIAH PRAKTIK UJI BAHAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (283kB)
	Text BAB 2.pdf Restricted to Registered users only Download (427kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (497kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (431kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (148kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (218kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (3MB) | Request a copy

Abstract

ABSTRAK (INDONESIA) Meningkatnya pemakaian barang berbahan plastik menyebabkan timbunan limbah plastik karena sifatnya yang sulit terurai. Alternatif daur ulang limbah plastik adalah dengan memanfaatkannya sebagai bahan campuran dalam bahan konstruksi bangunan. Paving block merupakan produk bahan bangunan dari campuran semen, agregat dan air yang digunakan sebagai perkerasan permukaan tanah. Penelitian ini bertujuan untuk mengetahui karakteristik paving block dengan memanfaatkan limbah plastik HDPE dan LDPE sebagai substitusi sebagian pasir sehingga dapat diketahui pengaruhnya terhadap syarat mutu mengacu pada SNI 03-0691-1996. Penelitian ini menggunakan metode eksperimen dengan benda uji paving block berukuran 210 mm x 105 mm x 60 mm berbentuk balok. Pemanfaatan cacahan limbah plastik HDPE dan LDPE sebagai substitusi sebagian agregat halus dengan variasi persentase 0%, 3%, 6%, 9% dan 12%. Pengujian pada benda uji dilakukan pada umur 28 hari sesuai dengan SNI 03-0691-1996 tentang paving block, berupa uji kuat tekan, uji ketahanan aus dan uji penyerapan air. Hasil dari penelitian ini menunjukkan bahwa pengaruh pemanfaatan limbah plastik HDPE dan LDPE terhadap paving block tidak dapat meningkatkan mutunya. Kuat tekan optimum terdapat pada variasi 0% sebesar 36,13 MPa. Untuk kuat tekan variasi 3%, 6%, 9% dan 12% berturut-turut sebesar 19,11 MPa; 18,39 MPa; 13,79 MPa dan 8,67 MPa. Seluruh variasi benda uji masuk ke dalam kelas mutu A untuk pengujian ketahanan aus. Pada uji penyerapan air variasi 3% dan 6% tergolong mutu B sedangkan variasi 9% dan 12% tergolong mutu D. Kata Kunci: Limbah Plastik HDPE, Limbah Plastik LDPE, Agregat Halus, Paving Block ******** ABSTRACT (INGGRIS)The increasing use of goods made of plastic causes piles of plastic waste because it is difficult to decompose. An alternative to recycling plastic waste is to use it as a mixture in building construction materials. Paving block is a product of building materials from a mixture of cement, aggregate and water which is used as a pavement surface. This study aims to determine the characteristics of paving blocks by utilizing HDPE and LDPE plastic waste as a partial substitution of sand so that it can be seen their effect on quality requirements referring to SNI 03-0691-1996. This study uses an experimental method with paving block specimens measuring 210 mm x 105 mm x 60 mm in the form of blocks. Utilization of shredded HDPE and LDPE plastic waste as partial substitution of fine aggregate with varying percentages of 0%, 3%, 6%, 9% and 12%. Tests on the specimens were carried out at the age of 28 days in accordance with SNI 03-0691-1996 regarding paving blocks, in the form of compressive strength tests, wear resistance tests and water absorption tests. The results of this study indicate that the utilization of HDPE and LDPE plastic waste cannot improve its quality. The optimum compressive strength is found at 0% variation of 36.13 MPa. For the compressive strength variations of 3%, 6%, 9% and 12% respectively of 19.11 MPa; 18.39 MPa; 13.79 MPa and 8.67 MPa. All variations of the test object are included in the A quality class for wear resistance testing. In the water absorption test, variations of 3% and 6% are classified as B quality, while 9% and 12% are classified as D quality. Keywords: HDPE Plastic Waste, LDPE Plastic Waste, Fine Aggregate, Paving Block

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Santoso Sri Handoyo, MT ; 2). Drs. Arris Maulana, ST, MT
Subjects:	Pendidikan > Pendidikan Pendidikan > Teori, Penelitian Pendidikan Pendidikan > Pendidikan Kejuruan dan Sekolah Kejuruan Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Teknik Jalan Raya Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 13595 not found.
Date Deposited:	13 Mar 2022 10:35
Last Modified:	13 Mar 2022 10:35
URI:	http://repository.unj.ac.id/id/eprint/23942

Actions (login required)

View Item