PEMANFAATAN CAMPURAN FLY ASH DAN LDPE SEBAGAI SUBTITUSI AGREGAT HALUS PADA PAVING BLOCK (Implementasi Mata Kuliah Praktek Uji Bahan Program Studi Pendidikan Teknik Bangunan Universitas Negeri Jakarta)

PUTRI RAHMADINI UTAMI, . (2022) PEMANFAATAN CAMPURAN FLY ASH DAN LDPE SEBAGAI SUBTITUSI AGREGAT HALUS PADA PAVING BLOCK (Implementasi Mata Kuliah Praktek Uji Bahan Program Studi Pendidikan Teknik Bangunan Universitas Negeri Jakarta). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (4MB)
	Text BAB 1.pdf Download (410kB)
	Text BAB 2.pdf Restricted to Registered users only Download (581kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (757kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (732kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (339kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (312kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (4MB) | Request a copy

Abstract

ABSTRAK Putri Rahmadini Utami, Anisah, R. Eka Murtinugraha. “Pemanfaatan Campuran Fly Ash dan LDPE sebagai Subtitusi Agregat Halus pada Paving block (Implementasi Mata Kuliah Praktek Uji Bahan Program Studi Pendidikan Teknik Bangunan Universitas Negeri Jakarta)”. Skripsi, Jakarta: Program Studi Pendidikan Teknik Bangunan. Fakultas Teknik. Universitas Negeri Jakarta, 2021. Paving block merupakan produk bahan bangunan dari campuran semen, agregat dan air yang digunakan sebagai perkerasan permukaan tanah. Penelitian ini bertujuan untuk mengetahui karakteristik paving block dengan memanfaatkan Fly Ash dan LDPE sebagai substitusi sebagian pasir sehingga dapat diketahui pengaruhnya terhadap syarat mutu mengacu pada SNI 03-0691-1996. Penelitian ini menggunakan metode eksperimen dengan benda uji paving block berukuran 210 mm x 105 mm x 60 mm berbentuk balok. Pemanfaatan campuran Fly Ash dan LDPE sebagai substitusi sebagian agregat halus dengan variasi persentase 0%, 5%, 7,5%, 10%, 12,5% dan 15%. Pengujian pada benda uji dilakukan pada umur 28 hari sesuai dengan SNI 03-0691-1996 tentang paving block, berupa uji kuat tekan, uji ketahanan aus dan uji penyerapan air. Hasil dari penelitian ini menunjukkan bahwa pengaruh pemanfaatan campuran Fly Ash dan LDPE terhadap paving block dapat meningkatkan mutunya dengan proporsi yang tepat. Kuat tekan optimum terdapat pada variasi 7,5% sebesar 20 MPa. Untuk kuat tekan variasi 0%, 5%, 10%, 12,5% dan 15% berturut-turut sebesar 17,3Mpa; 16 MPa; 15,3 MPa; 12 MPa dan 10 MPa. Variasi 5%, 7,5%, 10%, dan 12,5% masuk ke dalam mutu A untuk pengujian ketahanan aus. Pada uji penyerapan air variasi 7,5% dan 12,5% tergolong mutu B sedangkan variasi 5%,10 dan 15% tergolong mutu B. Kata Kunci : Abu Terbang, LDPE, Agregat Halus, Paving block ******** ABSTRACT Putri Rahmadini Utami, Anisah, R. Eka Murtinugraha. "Utilization of a mixture of Fly Ash and LDPE as Substitute for Fine Aggregate in Paving Blocks (Implementation of Material Test Practice Courses in the Jakarta State University Building Engineering Education Study Program)". Thesis, Jakarta: Building Engineering Education Study Program. Faculty of Engineering. Jakarta State University, 2021. Paving blocks are a product of building materials from a mixture of cement, aggregate and water used as ground pavement. This study aims to determine the characteristics of paving blocks by utilizing Fly Ash and LDPE as a partial sand substitution so that it can be seen their effect on quality requirements referring to SNI 03-0691-1996. This study uses a experiment method with paving block specimens measuring 210 mm x 105 mm x 60 mm in the form of a beam. Utilization Fly Ash and LDPE as a partial substitution of fine aggregate with various percentages of 0%, 5%, 7.5%, 10%, 12.5% and 15%. Tests on the specimens were carried out at the age of 28 days in accordance with SNI 03-0691-1996 regarding paving blocks, in the form of compressive strength tests, wear resistance tests and water absorption tests. The results of this study indicate that the effect of using Fly Ash and LDPE on paving blocks can improve its quality with the right proportions. The optimum compressive strength is found in variations of 0% and 7.5%, respectively, of 17.2 MPa and 20 MPa. For compressive strength variations of 5%, 10%, 12.5% and 15%, respectively, of 16 MPa; 15.2 MPa; 12 MPa and 10 MPa. Variations of 5%, 7.5%, 10%, and 12.5% fall into grade A for wear resistance testing. In the water absorption test, the variation of 7.5% and 12.5% is classified as B quality, while the variation of 5%, 10 and 15% is classified as B quality. Keywords : Fly ash, LDPE, Fine Aggregate, Paving Blocks

Item Type:	Thesis (Sarjana)
Additional Information:	1). Anisah, M.T.; 2). R. Eka Murtinugraha, M.Pd.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 13596 not found.
Date Deposited:	15 Mar 2022 09:54
Last Modified:	04 Nov 2022 01:28
URI:	http://repository.unj.ac.id/id/eprint/24416

Actions (login required)

View Item