PENGARUH JUMLAH LAPISAN TERHADAP SIFAT KEMAGNETAN MULTILAYER BARIUM HEXAFERRITE YANG DIBUAT DENGAN METODE ULTRASONIC SPRAY PYROLYSIS

DESY RAKHMAWATI, . (2016) PENGARUH JUMLAH LAPISAN TERHADAP SIFAT KEMAGNETAN MULTILAYER BARIUM HEXAFERRITE YANG DIBUAT DENGAN METODE ULTRASONIC SPRAY PYROLYSIS. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text Skripsi_Desy Rakhmawati_3225120229.pdf Download (2MB)

Abstract

Barium heksaferrit (BHF) tipe M memiliki koersivitas dan temperatur curie yang tinggi. Sehingga, cocok digunakan sebagai media perekam densitas tinggi. Telah disintesis lapisan tipis dan tebal multilayer BaFe12O19 di atas substrat quartz menggunakan metode Ultrasonic Spray Pyrolysis (USP) yang dipanaskan pada suhu 1000°C selama 1 jam. Larutan prekursor terdiri dari Ba(NO3)2 dan Fe(NO3)3.9H2O dengan perbandingan mol sebesar 1:8, kemudian dilarutkan dengan air deionisasi dan asam sitrat sebagai pengontrol pH. Variasi jumlah lapisan mulai dari 1 lapis, 2 lapis, dan 3 lapis dilakukan untuk mengetahui pengaruhnya terhadap sifat kemagnetan multilayer Barium Heksaferrit. Hasil analisa Vibrating Sample Magnetometer (VSM) menunjukan semakin banyak jumlah lapisan pada multilayer Barium Heksaferrit, semakin besar energi produk yang dimiliki dan semakin bersifat hard magnet. M-type Barium hexaferrites has large coercivity and high curie temperature. Thus, it suitable to used as high density recording media. BaFe12O19 thin and thick films have been synthesized on quartz substrate using Ultrasonic Spray Pyrolysis (USP) method, heated at temperature 1000°C for 1 hours. The precursor solution consists of Ba(NO3)2 and Fe(NO3)3.9H2O with comparison of mol 1:8, and then diluted with deionized water and citric acid as a pH controller. The number of variations from 1 layer, 2 layers and 3 layers have been made to know its influence over the magnetic properties of Barium Hexaferrite multilayer. Vibrating Sample Magnetometer (VSM) analysis shows the more number of layers in Barium Hexaferrite multilayer, the energy products will increase and becomes hard magnet

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Erfan Handoko, M.Si 2) Dr. Iwan Sugihartono, M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	sawung yudo
Date Deposited:	24 Mar 2022 01:59
Last Modified:	24 Mar 2022 01:59
URI:	http://repository.unj.ac.id/id/eprint/25232

Actions (login required)

View Item