SINTESIS DAN KARAKTERISASI ZEOLIT X DARI BAUKSIT DAN ABU SEKAM PADI PADA TEMPERATUR 80°C

BRILLIANTY KUSUMAWATI, . (2017) SINTESIS DAN KARAKTERISASI ZEOLIT X DARI BAUKSIT DAN ABU SEKAM PADI PADA TEMPERATUR 80°C. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
Brillianty Kusumawati_3325136393.pdf

Download (2MB)

Abstract

Sintesis zeolit dari bauksit dan abu sekam padi pada temperatur 80°C telah berhasil dilakukan. Pengaruh waktu hidrotermal terhadap karakteristik zeolit hasil sintesis dipelajari melalui kajian waktu sintesis 1, 2, 3, 4, 5, 8, 10, dan 15 hari. Karakterisasi penentuan gugus fungsi dengan FTIR, kristalinitas dengan XRD, morfologi dengan SEM, dan luas permukaan dengan SAA dipergunakan untuk menentukan waktu optimum hidrotermal. Analisis FTIR terhadap zeolit sintetik yang diperoleh menunjukkan adanya vibrasi regangan simetri 748,38 cm-1- 664,73 cm-1 , asimetri pada 979,84 cm-1 - 974,06 cm-1 yang merupakan ciri khas zeolit pada sampel yang diperoleh mulai hidrotermal 1 hari. Analisis XRD menunjukkan bahwa sintesis yang dilakukan menghasilkan zeolit X dan A pada hidrotermal 1 sampai 8 hari, dan terbentuk zeolit X dan P pada hidrotermal 10 dan 15 hari. Zeolit X hasil sintesis memiliki kristalinitas tertinggi pada waktu hidrotermal 10 hari dan sintesis tanpa hidrotermal menghasilkan fasa amorf. Analisis SEM menunjukkan terbentuknya morfologi khas untuk zeolit X, A, dan P. Analisis SAA menunjukkan pori yang terbentuk merupakan isoterm tipe IV yaitu mesopori dengan terdapatnya histerisis. Waktu hidrotermal berpengaruh terhadap jenis dan karakteristik zeolit yang diperoleh. Zeolite X has been synthesized from bauxite and rice husk ash at temperature 80°C. The influence of hydrothermal time on characteristics of zeolite synthesis is learned through study of the synthesis of 0,1,2,3,4,5,8,10 and 15 days. Characterization of functional group determination using FTIR, crystallinity using XRD, morphology using SEM, and surface area using SAA was used to determine the optimum hydrothermal time. FTIR analysis of synthetic zeolite obtained showed vibration of symmetry strain at 664,73 cm-1-748,38 cm-1, asymmetry at 974,06 cm-1 - 979,84 cm-1 which is characteristic of zeolite in sample obtained from hydrothermal 1 day. XRD analysis showed that the synthesis resulted in zeolite X and A on hydrothermal 1 to 8 days, and formed zeolite X and P on hydrothermal 10 and 15 days. The synthesized zeolite X has the highest crystallinity at hydrothermal time 10 days and synthesis without hydrothermal form an amorphous phase. SEM analysis showed typical morphology for zeolite X, A and P. SAA analysis showed pore formed is type IV isoterm that is mesoporous with the presence of hysteresis. Hydrothermal time affect type and characteristic of zeolit obtained.

Item Type: Thesis (Sarjana)
Additional Information: 1) Dr. Yusmaniar,M.Si 2) Arif Rahman,M.Sc
Subjects: Sains > Kimia
Divisions: FMIPA > S1 Kimia
Depositing User: sawung yudo
Date Deposited: 28 Mar 2022 02:13
Last Modified: 28 Mar 2022 02:13
URI: http://repository.unj.ac.id/id/eprint/25402