PENGARUH KONSENTRASI INISIATOR 2-HIDROKSI2-METIL-FENIL PROPANON TERHADAP SIFAT KONDUKTIVITAS DAN KARAKTERISTIK KOMPOSIT POLIMER KOLESTERIL AKRILAT-ITO

AHMAD ZAINI ASSIDIQIH, . (2017) PENGARUH KONSENTRASI INISIATOR 2-HIDROKSI2-METIL-FENIL PROPANON TERHADAP SIFAT KONDUKTIVITAS DAN KARAKTERISTIK KOMPOSIT POLIMER KOLESTERIL AKRILAT-ITO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI - Ahmad Zaini Assidiqih - 3325130962.pdf Download (2MB)

Abstract

Penelitian ini bertujuan untuk mengetahui karakteristik dan sifat konduktivitas komposit polimer kolesteril akrilat-indium tin oxide (PKA-ITO). Pembuatan komposit PKA-ITO menggunakan metode UV curing dengan konsentrasi inisiator 2- Hidroksi-2-Metil FenilPropanon (darocur 1173) yaitu 0; 0,125; 0,250; 0,375; 0,500; 0,625 % V/V. Komposit PKA-ITO dikarakterisasi dengan FTIR, XRD, SEM dan LCR Meter. Hasil karakterisasi FTIR menunjukkan adanya pergeseran bilangan gelombang antara spektrum FTIR komposit PKA-ITO dan spektrum FTIR kolesteril akrilat (KA) murninya. Hal tersebut menunjukkan adanya interaksi antara polimer kolesteril akrilat dengan indium tin oxide (ITO). Berdasarkan pola difraksi XRD terdapat puncak dengan intensitas tinggi pada 2θ=30° yang merupakan puncak khas ITO dan terdapat puncak pada 2θ=7° yang merupakan puncak kolesteril akrilat-ITO. Semakin besar konsentrasi inisiator maka ITO dan PKA mulai bercampur dan terlihat morfologi permukaaan dengan bentuk bulat-bulat yang membesar dan mengumpal. Data LCR Meter menunjukkan bahwa nilai konduktivitas komposit PKA-ITO tanpa inisiator lebih kecil jika dibandingkan dengan ditambahkannya inisiator. Nilai konduktivitas berbanding lurus dengan nilai permitivitas komposit PKA-ITO. This study aims to determine the characteristic and conductivity properties of cholesteryl acrylate polymer-indium tin oxide (PKA-ITO) composite. Composite making of PKA-ITO using UV Curing method with concentration of initiator 2- Hydroxy-2-Methyl PhenylPropanone (Darocure 1173) that is 0; 0,125; 0,250; 0,375; 0,500; 0,625 % V/V. the PKA-ITO composite is characterized by FTIR, XRD, SEM and LCR Meter. The FTIR characterization results show a shift of wave numbers between the PKA-ITO composite FTIR spectrum and its pure cholesteryl arcylate (KA) FTIR spectrum. This suggests an interaction between the cholesteryl acrylate polymer and indium tin oxide (ITO). Based on the XRD diffraction pattern thereis a high intensity peak a 2θ=30° which is the typical peak of ITO and there is a peak at 2θ=7° which is the peak of the cholesteryl acrylate-ITO. The greater the initiator concentration the ITO and PKA begin to mix and look at the morphology of the surface with englarged. The LCR Meter data show that the conductivity value of the PKA-ITO composite without the initiator is smaller when compared with the addition of the initiator. The conductivity value directly proportional to the composite permittivity value of PKA-ITO.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Afrizal, M.Si 2) Arif rahman, M.Sc
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	04 Apr 2022 02:47
Last Modified:	04 Apr 2022 02:47
URI:	http://repository.unj.ac.id/id/eprint/25728

Actions (login required)

View Item