PEMBENTUKAN DAN KARAKTERISASI SIFAT FISIK DAN OPTIK SISTEM KACA ZnO – MgO – P2O5 DENGAN TEKNIK MELT QUENCHING

INDRA PERMANA, . (2016) PEMBENTUKAN DAN KARAKTERISASI SIFAT FISIK DAN OPTIK SISTEM KACA ZnO – MgO – P2O5 DENGAN TEKNIK MELT QUENCHING. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI INDRA PERMANA.pdf Download (2MB)

Abstract

Pembentukan kaca fosfat dengan komposisi kimia x ZnO – 30 MgO – ( 70 – x ) P2O5 dengan x = 0, 5, 10, dan 15 mol% telah dilakukan menggunakan teknik melt quenching. Sistem kaca yang dibuat dikarakterisasi menggunakan difraksi sinar-X ( XRD ) untuk menganalisa struktur kristalnya, pengujian sifat fisik dengan metode Archimedes, dan sifat optik dianalisa dengan spektrofotometer UV-Vis. Hasil pola XRD menunjukkan bahwa sistem kaca yang dibuat memiliki struktur amorf. Dari hasil pengujian sifat fisik menunjukkan bahwa densitas kaca semakin menurun sedangkan volume molar meningkat dengan bertambahnya mol% ZnO. Absorpsi optikal diukur pada panjang gelombang 200 – 800 nm menunjukkan tidak adanya berkas absorpsi yang tajam. Dari hasil spektra absorpsi optikal menunjukkan bahwa nilai energi gap semakin menurun sedangkan energi Urbach dan indeks refraktif kaca meningkat dengan bertambahnya mol% ZnO. Dari semua sampel yang telah dibuat, dapat disimpulkan bahwa sampel keempat merupakan sampel yang terbaik dari sifat fisik maupun optiknya. Phosphate glass with the chemical composition x ZnO – 30 MgO – ( 70 – x ) P2O5 with x = 0, 5, 10, and 15 mol% was done by using melt quenching technique. The glasses system were characterized with X-Ray diffraction to analyze the crystal structure, physical property was measured by using Archimedes method, and the optical properties were analyzed by using UV-Vis spectrophotometer. The result of X-Ray difraction pattern shows that the glass system has an amorphous structure. The result of physical properties show that the value of density is decreased but the molar volume is increased with the increase of mol% ZnO. The optical absorption was measured in the wavelength region 200 – 800 nm shows that there is no sharp absorption band edge. From absorption optical spectra shows that gap energy is decreased but Urbach energy and refractive index are increased with the increase of mol% ZnO. From all samples have been made, the fourth sample is the best sample in the physical and optical properties.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Esmar Budi, M.T 2) Dr. Mangasi A Marpaung, M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	sawung yudo
Date Deposited:	07 Apr 2022 01:59
Last Modified:	07 Apr 2022 01:59
URI:	http://repository.unj.ac.id/id/eprint/25971

Actions (login required)

View Item