PENGARUH DAYA LAMPU UV TERHADAP KARAKTERISTIK DAN SIFAT KONDUKTIVITAS KOMPOSIT POLIMER KOLESTERIL AKRILAT-ITO

LINGGAR AJI PANGESTU, . (2017) PENGARUH DAYA LAMPU UV TERHADAP KARAKTERISTIK DAN SIFAT KONDUKTIVITAS KOMPOSIT POLIMER KOLESTERIL AKRILAT-ITO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI LINGGAR AJI PANGESTU FINAL.pdf Download (3MB)

Abstract

Monomer KA dan ITO telah berhasil menjadi komposit pada proses fotopolimerisasi menggunakan metode UV curing dengan berbagai variasi daya lampu UV yaitu 10, 25, 40 dan 55 watt, yang bertujuan untuk mengetahui pengaruh karakteristik dan sifat konduktivitasnya. Hasil karakterisasi menunjukan bahwa daya lampu mempengaruhi karakteristik dan sifat konduktivitas PKAITO. Hal ini didukung dengan analisa instrumen yaitu FTIR, XRD,SEM-EDX dan LCR meter. Pada analisa gugus fungsi dengan FTIR menunjukan vibrasi ikatan In-OH dengan C-O pada bilangan gelombang 1056,99 cm-1 . Pola XRD menunjukan puncak khas ITO pada 2θ= 30o dengan intensitas yang tinggi. Data SEM-EDX memperlihatkan bahwa semakin besar daya lampu UV diberikan proses fotopolimerisasi maka semakin teraglomerasi antara PKA dengan ITO terlihat pada morfologi komposit PKA-ITO 25 watt telah terjadi aglomerasi antara PKA dengan ITO membentuk gumpalan-gumpalan yang mana ITO sebagai filler (pengisi) pada matriks polimer. Kandungan unsur yang terdapat pada komposit PKA-ITO yaitu C 76,91%, O 3,13% dan In 5,13%. Nilai konduktivitas komposit PKA-ITO memiliki nilai lebih besar dibandingkan nilai konduktivitas KA-ITO sebesar 4,0783x10-10 S/m. Monomer KA and ITO have succeeded in becoming a composite with photopolymerization process with UV curing method with variation of UV lamp power that is 10, 25, 40 and 55 watt, purposes to determine the effect of conductivity characteristics and properties. The result of characterization shows that the power of lamp influences the characteristic and conductivity properties of PKA-ITO. This is supported by instrument analysis of FTIR, XRD, SEM-EDX and LCR meter. In functional group analysis with FTIR showed vibration of InOH bond with C-O at wave number 1056,99 cm-1 . XRD pattern shows the typical peak of ITO at 2θ = 30o with high intensity. The SEM-EDX data show that the greater the UV lamp power given the photopolymerization process, the more agglomerated between PKA and ITO seen in the 25 watt PKA-ITO composite morphology there has been agglomeration between PKA and ITO to form clots where ITO as filler Polymer matrix. The content of the elements contained in the composite PKA-ITO is C 76.91%, O 3.13% and In 5.13%. The value of PKA-ITO composite conductivity has a value greater than the value of KA-ITO conductivity of 4,0783x10-10 S/m.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Afrizal, M.Si 2) Arif Rahman, M.Sc
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	08 Apr 2022 07:30
Last Modified:	08 Apr 2022 07:30
URI:	http://repository.unj.ac.id/id/eprint/26126

Actions (login required)

View Item