PENGARUH KONSENTRASI PENAMBAHAN UNSUR Cu-Al TERHADAP STRUKTUR KRISTAL DAN SIFAT OPTIK DARI NANOSTRUKTUR ZnO

MEGA LIALITA MAHARANI, . (2016) PENGARUH KONSENTRASI PENAMBAHAN UNSUR Cu-Al TERHADAP STRUKTUR KRISTAL DAN SIFAT OPTIK DARI NANOSTRUKTUR ZnO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI.pdf Download (1MB)

Abstract

Telah dilakukan penumbuhan nanostruktur ZnO dengan dua tahapan yaitu tahap pendeposisian lapisan benih di atas subtrat Indium Tin Oxide (ITO) menggunakan metode Ultrasonic Spray Pyrolisis dan tahap penumbuhan nanostruktur ZnO menggunakan metode hidrotermal. Nanostruktur ZnO disintesis dengan variasi penambahan unsur Cu (4 % dan 7 %) dan Al 4%. Karakterisasi nanostruktur ZnO berupa morfologi permukaan oleh Scanning Electron Microscopy (SEM), struktur kristal oleh X-Ray Diffraction (XRD), dan sifat optik oleh Ultraviolet-Visible Spectroscopy (UV-Vis) dan Fotoluminisen (PL). Hasil dari penelitian ini menunjukkan penambahan konsentrasi unsur Cu - Al membuat ukuran kristal dan densitas nanostruktur ZnO semakin besar. Penambahan konsentrasi unsur Cu-Al meningkatkan nilai bandgap nanostruktur ZnO. Hasil luminisen menjelaskan bahwa penambahan konsentrasi unsur Cu – Al menurunkan cacat alamiah yang ada di nanostruktur ZnO. Synthesis of ZnO nanostructure has done by two phases, they are deposition of layers on IndiumTin Oxide (ITO) substrat using UltrasonicSpray Pyrolisis(USP) method and synthesis of ZnO using hydrotermal method. ZnO nanostructure synthesized by doping variation of Cu (4% and 7%) and Al 4%. The characterization of ZnO nanostructure are structure morphology by Scanning ElectronMicroscop (SEM), crystal structure by X-Ray Diffraction (XRD) and optic characteristic by Ultraviolet-VisibleSpectroscopy UV-Vis and PL. The result shows increasing concentration doping Cu-Al make the size of crystal and density of ZnO nanostructure bigger. Increasing concentration doping Cu-Al increase band gap value ZnO nanostructure. Result of PL describes that increasing concentration doping Cu-Al decrease native defect of ZnO nanostructure.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Iwan Sugihartono, M.Si 2) Dr. Vivi Fauzia M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	sawung yudo
Date Deposited:	11 Apr 2022 02:06
Last Modified:	11 Apr 2022 02:06
URI:	http://repository.unj.ac.id/id/eprint/26229

Actions (login required)

View Item