SINTESIS KOMPOSIT SILIKA GEL DARI SEKAM PADI –3-AMINOPROPILTRIETOKSISILAN(APTES) DENGAN KARBON AKTIF DARI TEMPURUNG KELAPA DAN UJI ADSORPSI TERHADAP LOGAM Cd(II)

RATIH NOVIASARI, . (2017) SINTESIS KOMPOSIT SILIKA GEL DARI SEKAM PADI –3-AMINOPROPILTRIETOKSISILAN(APTES) DENGAN KARBON AKTIF DARI TEMPURUNG KELAPA DAN UJI ADSORPSI TERHADAP LOGAM Cd(II). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text RATIH NOVIASARI-3325122149.pdf Download (2MB)

Abstract

Pada penelitian ini dibuat adsorben komposit silika gel dimodifikasi dengan APTES dan karbon aktif. Silika gel berasal dari sekam padi dan karbon aktif berasal dari tempurung kelapa. Abu sekam padi ini diolah sedemikian rupa menjadi larutan natrium silikat hingga menghasilkan produk silika gel. Silika gel kemudian dicampurkan dengan reagen 3-aminopropiltrietoksisilan (APTES) dan karbon aktif yang telah diaktifasi sebelumnya dengan larutan ZnCl2 dan diproses menjadi komposit. Karakterisasi komposit hasil sintesis menggunakan spektroskopi FTIR menunjukkan serapan ikatan N-H, silanol (Si-OH), siloksana (Si-O-Si), dan ikatan C-H. Kandungan dari komposit silika gel dimodifikasi dengan APTES dan karbon aktif ditunjukkan melalui hasil analisis EDX bahwa komposit hasil sintesis memiliki persentase massa masing-masing atom 32.92% karbon, 25.88% nitrogen, 26.04% oksigen, dan 15.16% silika. Hasil penelitian menunjukkan bahwa pH optimum yang diperlukan untuk adsorpsi ion Cd(II) dengan komposit silika gel dimodifikasi dengan APTES dan karbon aktif yaitu 5.0 dan waktu kontak optimum 30 menit. Adsorpsi ion Cd(II) oleh komposit silika gel dimodifikasi dengan APTES dan karbon aktif mengikuti isoterm adsorpsi Freundlich. Oleh karena itu, adsorpsi terjadi membentuk lapisan monolayer yang bersifat heterogen. In this research, silica gel composite modified adsorbents were made with APTES and activated carbon. Silica gel comes from rice husk and activated carbon comes from coconut shell. This rice husk ash is processed in such a way as a sodium silicate solution to produce a silica gel product. The silica gel was then mixed with 3-aminopropylsylatedoxylic reagent (APTES) and activated carbon previously with ZnCl 2 solution and processed into composite. Characterization of composite synthesis using FTIR spectroscopy shows uptake of N-H, silanol (SiOH), siloxane (Si-O-Si), and C-H bonds. The content of the silica gel composite modified by APTES and activated carbon is indicated through EDX analysis results that the composite of the synthesis has a mass percentage of each atom of 32.92% carbon, 25.88% nitrogen, 26.04% oxygen, and 15.16% silica. The results showed that the optimum pH required for the adsorption of Cd (II) ions with silica gel composite was modified with APTES and the activated carbon was 5.0 and the optimum contact time was 30 minutes. Adsorption of Cd (II) ions by silica gel composites was modified by APTES and activated carbon followed Freundlich adsorption isotherm. Therefore, adsorption occurs forming a heterogeneous monolayer layer.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Yusmaniar, M.Si 2) Arif Rahman, M.Sc
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	13 Apr 2022 06:45
Last Modified:	13 Apr 2022 06:45
URI:	http://repository.unj.ac.id/id/eprint/26489

Actions (login required)

View Item