PENGARUH PERBANDINGAN PATI BIJI SORGUM (SORGHUM BICOLOR (L.) MOENCH) DAN POLY LACTIC ACID (PLA) TERHADAP KARAKTERISTIK PLASTIK BIODEGRADABLE

SITI SARIFAH, . (2017) PENGARUH PERBANDINGAN PATI BIJI SORGUM (SORGHUM BICOLOR (L.) MOENCH) DAN POLY LACTIC ACID (PLA) TERHADAP KARAKTERISTIK PLASTIK BIODEGRADABLE. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text 1. skripsi_siti sarifah_kimia 2013.pdf Download (1MB)

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh Pati biji sorgum dan Poly lactic acid (PLA) terhadap karakteristik plastik yang dapat dilihat dari kekuatan tarik, ketahanan air, dan biodegradasitasnya. Penelitian ini dilakukan dengan metode blending (menyampurkan) pati biji sorgum, PLA, gliserol, asam asetat, dan maleat anhidrat. Dari hasil analisis spektrum inframerah pada film plastik terlihat puncak didaerah 2250-2300 cm-1 yang menandakan adanya penyerapan karbon dioksida. Plastik ini memiliki ketahanan air optimum sebesar 92,76% pada perbandingan Pati 0,6g:PLA 2,6g. Hasil uji tarik optimum pada perbandingan pati 0,2g:PLA 3g dengan nilai 10,58 Mpa. Hasil uji biodegradasi optimum pada perbandingan pati 0,6g:PLA 2,6g sebesar 13,61%. Berdasarkan hasil penelitian dapat disimpulkan bahwa biodegradasi dan ketahanan air mencapai optimal pada komposisi pati 0,6g:PLA 2,6g. This study aims to determine the effect of Sorghum and Poly lactic acid (PLA) on the plastic characteristics that can be seen from tensile strength, water resistance, and biodegradability. This research was done by blending (mixing) starch of sorghum seed, PLA, glycerol, acetic acid, and maleic anhydride. From the results of infrared spectrum analysis on plastic films seen peaks in the area 2250-2300 cm-1 which indicates the absorption of carbon dioxide. This plastic has an optimum water resistance of 92.76% in the ratio of Pati 0.6g: PLA 2.6g. The optimum tensile test results in a comparison of 0.2g starch: PLA 3g with a value of 10.58 Mpa. Optimum biodegradation test results in starch ratio of 0.6g: PLA 2.6g of 13.61%. Based on the result of the research, it can be concluded that biodegradation and water resistance reach optimal on starch composition 0,6g: PLA 2,6g.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Yusmaniar, M.Si 2) Dra. Zulmanelis, M.Si
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	18 Apr 2022 02:07
Last Modified:	18 Apr 2022 02:07
URI:	http://repository.unj.ac.id/id/eprint/26763