PENGARUH SUBSTITUSI Ti DAN Co PADA La0,7Ca0,3Mn1- xCoxO3 DAN La0,7Ca0,3Mn1-xTixO3 TERHADAP SIFAT KEMAGNETAN MATERIAL UNTUK APLIKASI EFEK MAGNETOKALORIK

ANGGITA PRASANTI, . (2015) PENGARUH SUBSTITUSI Ti DAN Co PADA La0,7Ca0,3Mn1- xCoxO3 DAN La0,7Ca0,3Mn1-xTixO3 TERHADAP SIFAT KEMAGNETAN MATERIAL UNTUK APLIKASI EFEK MAGNETOKALORIK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text PDF-SKRIPSI-ANGGITA PRASANTI-3225110215.pdf Download (5MB)

Abstract

Material Perovskite Manganat La1-xAxMnO3 telah banyak dikembangkan untuk aplikasi material efek magnetokalorik. Telah disintesis bahan LaCaMnO3 dengan subtitusi Co dan Ti terhadap Mn melalui metode mechanical alloying. La0,7Ca0,3Mn1- xTixO3 dan La0,7Ca0,3Mn1-xCoxO3 dengan komposisi x = 0; 0,1; 0,2; 0,5 disintesis menggunakan high energy milling selama 1 jam. Bahan dikalsinasi pada temperature 750°C selama 3 jam dan disinterring pada suhu 1100°C selama 3 jam. Karakterisasi dengan difraksi sinar-x menghasilkan fasa tunggal terhadap masing- maisng komposisi, material ini memiliki system Kristal kubik dan orthorombik sesuai dengan analisis kualitatif difraksi sinar-x. pengukuran sifat kemagnetan dilakukan menggunakan permagraph dan diperoleh kurva histerisis paramagnetic untuk setiap doping Co dan Ti pada komposisi x = 0; 0,1; 0,2; 0,5 pada material La0,7Ca0,3Mn1- xTixO3 dan La0,7Ca0,3Mn1-xCoxO3. Pengambilan gambar struktur permukaan pada material La0,7Ca0,3Mn1-xTixO3 dan La0,7Ca0,3Mn1-xCoxO3. dilakukan menggunakan alat SEM (Scanning Electron Microscope) didapat dengan perbesaran 200x. Manganate perovskite La1-xAxMnO3 being widely developed for apllication magnetocaloric effect. Material LaCaMnO3 has been synthesized with Ti and Co substitution to Mn with mechanical alloying method. La0,7Ca0,3Mn1-xCoxO3 and La0,7Ca0,3Mn1-xTixO3 with x = 0; 0,1; 0,2; 0,5 synthesized using high energy milling for 1 hour. Caltination proses at 750°C and then sintering at 1100°C for 1 hour. Characterization with x-ray diffraction produces single phase for each compotition. Materials has a cubic crystal system and orthorombik in qualitative analysis of x -ray diffraction. The magnetic measurement by permagraph and the result show that materials produces paramagnetic histerysis curve for each doping at x = 0; 0,1; 0,2; 0,5. Capture surface structure of materials using SEM and produces 200x magnification images.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Erfan Handoko, M.S. 2). Riser Fahdiran, M.Si.
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 8922 not found.
Date Deposited:	19 Apr 2022 01:13
Last Modified:	19 Apr 2022 01:13
URI:	http://repository.unj.ac.id/id/eprint/26972

Actions (login required)

View Item