SIFAT FISIS DAN MEKANIS PAPAN KOMPOSIT PELEPAH KELAPA SAWIT BERLAPIS BILAH BAMBU ANDONG

YOGI PRASETIYA, . (2017) SIFAT FISIS DAN MEKANIS PAPAN KOMPOSIT PELEPAH KELAPA SAWIT BERLAPIS BILAH BAMBU ANDONG. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text SKRS - Yogi Prasetiya 5415117401.pdf Download (1MB)
	Text Lembar pengesahan yogi.pdf Download (301kB)

Abstract

Penelitian ini bertujuan untuk memanfaatkan pelepah kelapa sawit dan bambu andong sebagai bahan papan komposit sesuai dengan JIS A 5908 tentang papan partikel. Sehingga dapat memanfaatkan limbah kelapa sawit dan penggunaan bambu secara maksimal. Penelitian ini menggunakan metode eksperimen, dengan populasi adalah papan komposit yang berbahan dasar pelepah kelapa sawit dan bambu andong dengan 3 variasi kadar perekat yaitu 20%, 30% dan 40% dari berat pelepah kelapa sawit. Penelitian ini melakukan 7 pengujian, yaitu: kerapatan, kadar air, pengembangan tebal, modulus patah, modulus elastisitas, kuat rekat internal dan kuat cabut sekrup. Hasil penelitian menunjukkan bahwa nilai terbaik yang didapat pada penelitian ini dihasilkan oleh papan komposit dengan kadar perekat sebesar 30%, nilai yang dihasilkan pada uji kerapatan, kadar air dan pengembangan tebal secara berturutturut sebesar 0,58 g/cm3 13% dan 49%. Rata – rata nilai modulus patah, modulus elastisitas dan kuat cabut sekrup secara berturut-turut adalah 13,914 kgf/cm2 , 20,108 kgf/cm2 , dan 32,88 kg. Berdasarkan uji statistik menunjukkan bahwa bertambahnya kadar perekat berpengaruh secara signifikan pada sebagian besar pengujian sifat fisis dan mekanis papan komposit pelepah kelapa sawit berlapis bilah bambu andong. The purpose of this study is to utilize palm fronds and andong bamboo as composite board, so it can take advantage of palm oil waste and use of andong bamboo to the fullest. This study use experimental method, the population is composite board made from palm fronds and andong bamboo with three adhesive content variations of 20%, 30% and 40% of weight of the palm fronds. This study did three tests of physical properties, namely; density, moisture content and thickness swelling and four test of mechanical properties, namely; Modulus of elasticity, modulus of rupture, internal bond and screw holding power. The result of this study showed that the best value obtained by composite board with adhesive content of 30%. With value of density , moisture content and thickness swelling were 0,58 gr/cm3 , 13% and 49%, respectively. The average modulus of rupture, modulus of elasticity and screw holding power were 13,914 kgf/cm2 , 20,108 kgf/cm2 , and 32,88 kg, respectively. Based on statistical test showed that increased adhesive content effect significantly at most test of physical and mechanical properties of palm fronds and andong bamboo composite board.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Prof. Dr. Drs. Adi Santoso, M. Si 2) Dr. Gina Bachtiar, MT
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	sawung yudo
Date Deposited:	24 Apr 2022 08:05
Last Modified:	24 Apr 2022 08:05
URI:	http://repository.unj.ac.id/id/eprint/27659

Actions (login required)

View Item