SINTESIS MATERIAL BARIUM W-HEKSAFERRIT DENGAN SUBSTITUSI Sr PADA Ba1-xSrxCoTiFe16O27 SEBAGAI MATERIAL PENYERAP GELOMBANG MIKRO

TSANIYA MUKARROMAH, . (2015) SINTESIS MATERIAL BARIUM W-HEKSAFERRIT DENGAN SUBSTITUSI Sr PADA Ba1-xSrxCoTiFe16O27 SEBAGAI MATERIAL PENYERAP GELOMBANG MIKRO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text Tsaniya Mukarromah_3225110295_Fisika_Full Skripsi.pdf Download (3MB)

Abstract

Barium Heksaferrit tipe-W (BaMe2Fe12O27) merupakan senyawa yang paling efisien untuk tujuan penyerap gelombang mikro karena memiliki nilai temperatur curie tinggi, nilai koersivitas sangat kecil (Hc), dan magnetik saturasi (Ms) paling tinggi dibandingkan dengan material ferrite lainnya. Sintesis dan karakterisasi material Barium Heksaferrit tipe-W dengan memodifikasi nilai Ba dan Sr pada Ba1- xSrxCoTiFe16O27 (x= 0, 0.1, 0.2, 0.3, 0.4, 0.5) untuk mengetahui karakterisasi fasa dari pola difraksi sinar-x, sifat kemagnetan dan hasil dari signal gelombang mikro. Dilakukan melalui proses penghalusan serbuk bahan-bahan dasar BaCO3, Fe2O3, SrCO3, Co3O4 dan TiO2 menggunakan metode High Energy Ball Mill selama 1 jam dalam suasana basah (toluena) dengan perlakuan kalsinasi pada temperatur 750 °C dan sintering 1100 °C selama 3 jam. Hasil pengujian menunjukkan pola difraksi sinar-x dari sampel Ba1-xSrxCoTiFe16O27 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) memperlihatkan bahwa telah terbentuk dua fasa yaitu BaFe12O19 dan Fe2O3. Sifat kemagnetan yang dihasilkan telah terjadi kenaikan nilai koersivitas magnetik (Hc) mulai dari 23.45 kA/m menjadi 37.80 kA/m dengan meningkatnya penambahan strontium (Sr). Material Ba1-xSrxCoTiFe16O27 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) memberikan efek terhadap signal gelombang mikro pada frekuensi diatas 10 GHz. *********** Barium Heksaferrit-type W (BaMe2Fe12O27) are the most efficient compounds for the purpose of microwave absorption because has high value of currie temperature, very small coercivity (Hc), and the highest magnetic saturation (Ms) than the other ferrite materials. Synthesis and characterization of materials W-type Barium Hexaferrite by modify the value of Ba and Sr in Ba1-xSrxCoTiFe16O27 to determine the characterization phases of x-ray diffraction pattern, magnetic properties, and the results of the microwave signal. Conducted through the process of smoothing powders of basic materials BaCO3, Fe2O3, SrCO3, Co3O4 and TiO2 by the High Energy Ball Mill method for 1 hour in a wet condition (toluene) with calcination process at temperature of 750 °C and sintering at temperature of 1100 °C in 3 hours. The x-ray diffraction pattern result showed that Ba1-xSrxCoTiFe16O27 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) sample has formed two phases, namely BaFe12O19 and Fe2O3. There was magnetic coercivity (Hc) increase from 23.45 kA/m to 37.80 kA/m with increase doping of strontium (Sr). Materials Ba1-xSrxCoTiFe16O27 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) give effect to the microwave signal at frequencies above 10 GHz.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Erfan Handoko, M.Si. ; 2). Dr. Widyaningrum Indrasari, M.Si.
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 14614 not found.
Date Deposited:	30 May 2022 05:38
Last Modified:	30 May 2022 05:38
URI:	http://repository.unj.ac.id/id/eprint/29408

Actions (login required)

View Item