KORELASI KADAR LUMPUR PASIR TERHADAP KUAT TEKAN BETON

KHAIRIYAH JUITA, . (2016) KORELASI KADAR LUMPUR PASIR TERHADAP KUAT TEKAN BETON. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text ABSTRAK BAHASA INGGRIS.pdf Download (85kB)
	Text 14. DAFTAR PUSTAKA.pdf Download (135kB)
	Text 3. Lembar Persetujuan.pdf Download (173kB)
	Text 2. Lembar Pengesahan.pdf Download (227kB)
	Text 1. COVER.pdf Download (110kB)
	Text 5. KATA PENGANTAR.pdf Download (85kB)
	Text 4. Halaman Pernyataan.pdf Download (312kB)
	Text 8. DAFTAR ISI.pdf Download (183kB)
	Text 10. BAB II.pdf Download (653kB)
	Text 9. BAB I.pdf Download (212kB)
	Text 11. BAB III.pdf Download (997kB)
	Text 12. BAB IV.pdf Download (627kB)
	Text 13. BAB V.pdf Download (132kB)
	Text 6. ABSTRAK INDONESIA.pdf Download (86kB)

Abstract

Tujuan penelitian ini adalah untuk mengetahui korelasi kadar lumpur pasir terhadap kuat tekan beton. Penelitian ini menambahkan kadar lumpur dengan variasi persentase yaitu, 1.4%, 2%, 4.3%, dan 6.5% dimana kadar lumpur 3% sebagai dasar yang dipakai pada industri readymix maupun precast. Kuat tekan rencana K-300 atau 29.42 MPa dengan FAS rencana 0.50 dan Slump rencana 100±20mm. Penelitian ini memiliki sampel 32 benda uji (uji tekan = 3 benda uji untuk setiap masing-masing variasi pada umur 7 hari, 14 hari dan 28 hari) dan menggunakan benda uji silinder berdiameter 15 cm dan tinggi 30 cm. Hasil penelitian ini menunjukkan bahwa rata-rata kuat tekan beton yang mencapai kuat tekan rencana 300 kg/cm² atau 29.42 MPa, berada pada umur beton 28 hari. Pada umur 14 hari hanya beton dengan variasi kadar lumpur 6.5% yang tidak mencapai kuat tekan rencana. Dan Hubungan antara kadar lumpur pasir terhadap kuat tekan beton pada penelitian ini, berada pada tingkat hubungan sangat rendah untuk semua umur beton yaitu umur 7 hari, 14 hari, dan 28 hari. The purpose of this study was to determine the correlation levels quicksand of compressive strength of concrete. This study adds to the mud content percentage variation that is, 1.4%, 2%, 4.3% and 6.5% whereas levels of 3% as a base mud used in readymix and precast industry. Strong press plan K-300 or 29.42 MPa with FAS plans 0.50 and Slump plans 100 ± 20mm. This study has a sample of 32 specimen (test specimen press = 3 for each individual variation at the age of 7 days, 14 days and 28 days) and use the test specimen cylinder diameter of 15 cm and 30 cm high. The results showed that the average compressive strength of concrete compressive strength reaching plan of 300 kg / cm² or 29.42 MPa, was at the age of concrete 28 days. At the age of 14 days only concrete with mud content variation of 6.5% which did not reach the compressive strength of the plan. The relationship between the levels of silt and sand of compressive strength of concrete in this study, are at very low levels of correlation for all the concrete that is the age of 7 days, 14 days and 28 days.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Gina Bachtiar, MT 2) Dra. Rosmawita Saleh, M.Pd
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	sawung yudo
Date Deposited:	11 Jun 2022 06:27
Last Modified:	11 Jun 2022 06:27
URI:	http://repository.unj.ac.id/id/eprint/30057

Actions (login required)

View Item