PENGARUH LAJU ALIRAN GAS TERHADAP NILAI KEKERASAN BAJA KARBON RENDAH HASIL HARDFACING DENGAN PENGELASAN GTAW

A.DANIEL PANDU YUDHANTONO, . (2018) PENGARUH LAJU ALIRAN GAS TERHADAP NILAI KEKERASAN BAJA KARBON RENDAH HASIL HARDFACING DENGAN PENGELASAN GTAW. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text A.DANIEL PANDU YUDHANTONO_5315136263.pdf Download (4MB)

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh yang terjadi akibat adanya laju aliran gas 1 L/menit, 3 L/menit, dan 5 L/menit terhadap nilai kekerasan baja karbon rendah pada proses pengelasan hardfacing. Metode yang digunakan pada penelitian ini adalah metode eksperimen. Berdasarkan hasil penelitian, bahwa laju aliran gas 1 liter/menit menghasilkan nilai kekerasan paling tinggi pada baja karbon rendah yang telah di heat treatment, yaitu sebesar 88 HRB. Laju aliran gas 3 liter/menit pada karbon rendah menghasilkan nilai kekerasan sebesar 83 HRB, sedangkan laju aliran gas 5 liter/menit, menghasilkan nilai kekerasan sebesar 70 HRB. Baja tanpa heat treatment yang dilas dengan laju aliran gas 1 liter/menit menghasilkan nilai kekerasan sebesar 82 HRB. Laju aliran gas 3 liter/menit pada baja tanpa heat treatment menghasilkan nilai kekerasan sebesar 76 HRB, sedangkan laju aliran gas 5 liter/menit menghasilkan nilai kekerasan sebesar 65 HRB. ********* This study aims to determine the influence that occurs due to 1 liters/minute, 3 liters/minute, and 5 liters/minute gas flow rate to the value of low carbon steel hardness on the hardfacing weld process. The method used in this research is experimental method. Based on the research results obtained is 1 liter / min gas flow rate produces the highest hardness value on low carbon steel that has been quenching with water media, which is equal to 88 HRB. The gas flow rate of 3 liters / min on low carbon steel produces a hardness value of 83 HRB, while the gas flow rate of 5 liters / minute, resulting in a hardness value of 70 HRB.Steel without heat treatment welded with 1 liter / min gas flow rate resulted in hardness value of 82 HRB. The gas flow rate of 3 liters / min on steel without heat treatment resulted in hardness value of 76 HRB, while the gas flow rate of 5 liters / min yielded a value hardness of 65 HRB.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ferry Budhi Susetyo , S.T ,M.Si. ; 2). Siska Titik Dwiyati , S.Si.,M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 14626 not found.
Date Deposited:	13 Jun 2022 03:57
Last Modified:	13 Jun 2022 03:57
URI:	http://repository.unj.ac.id/id/eprint/30155

Actions (login required)

View Item