PEMANFAATAN LIMBAH SERBUK MARMER DAERAH TRENGGALEK SEBAGAI BAHAN TAMBAH PADA PAVING BLOCK

ERICK EKA PERKASA, . (2017) PEMANFAATAN LIMBAH SERBUK MARMER DAERAH TRENGGALEK SEBAGAI BAHAN TAMBAH PADA PAVING BLOCK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text BAB II.pdf Download (566kB)
	Text Abstract.pdf Download (86kB)
	Text BAB I.pdf Download (208kB)
	Text Cover Skripsi.pdf Download (97kB)
	Text BAB III.pdf Download (133kB)
	Text BAB V.pdf Download (85kB)
	Text BAB IV.pdf Download (570kB)
	Text DAFTAR LAMPIRAN.pdf Download (186kB)
	Text DAFTAR PUSTAKA.pdf Download (276kB)
	Text DAFTAR ISI.pdf Download (161kB)
	Text DAFTAR GAMBAR.pdf Download (84kB)
	Text HALAMAN PERSETUJUAN.pdf Download (186kB)
	Text DAFTAR TABEL.pdf Download (84kB)
	Text HALAMAN PENGESAHAN.pdf Download (239kB)
	Text HALAMAN PERNYATAAN.pdf Download (222kB)
	Text Riwayat Penulis.pdf Download (200kB)
	Text KATA PENGANTAR.pdf Download (366kB)
	Text Lampiran.pdf Download (946kB)
	Text Abstrak.pdf Download (87kB)

Abstract

Penelitian ini bertujuan untuk mengetahui berapakah nilai kuat tekan maksimum pada Paving Block dengan Limbah serbuk marmer sebagai bahan tambah berdasarkan SNI 03-0691-1996 tentang Paving Block yang meliputi penilaian fisik dan Mekanis (kuat tekan dan penyerapan air). Metode penelitian ini menggunakan metode eksperimen dengan benda uji Paving Block yang menggunakan Limbah Serbuk Marmer sebesar 0%, 5%, 10%, 15% dan 20% terhadap berat semen dengan ukuran 21 cm x 10,5 cm x 8 cm, dengan jumlah sampel sebanyak 20 buah Paving Block dari masing-masing persentase (5 buah untuk pemeriksaan sifat fisik dan 10 buah masing-masing untuk pemeriksaan sifat mekanis dan 5 buah untuk cadangan). Pengujian kuat tekan dilakukan pada saat Paving Block berumur 28 hari. Hasil penelitian menunjukkan adanya kenaikan nilai kuat tekan paving block dengan penambahan limbah serbuk marmer sampai 10%. Kuat tekan maksimal benda uji berada pada persentase penambahan limbah serbuk marmer 10% dengan kuat tekan sebesar 26,97 Mpa. Untuk daya serap air terlihat adanya penurunan dengan bertambahnya persentase penambahan limbah serbuk marmer sampai 10%. Penurunan Daya serap air maksimal benda uji berada pada persentase penambahan limbah serbuk marmer 10% dengan daya serap air sebesar 5 %. This research aimed to find out the maximum compressive strength of paving block with marble waste powder as additive based on SNI 03-0691-1996 for concrete brick class I as wall pair including outside view, physical requirement (compressive strength and water absorption). This research using experimental method to test the object that use 0%, 5%, 10%,15% and 20% of marble waste powder. The object size was 21 cm x 10,5 cm x 8 cm, with total sample was 100 paving block. Each percentage (5 samples for physical test,10 for mechanical test and 5 as reserve ). The testing performed when paving block 28 days old. The research results show to raise the value strong press paving block by the addition of waste the marble to 10 %.Strong press maximum objects test is at the percentage the addition of waste the marble 10 % with strong press of 26,97 mpa. To absorption capacity water look a decrease in with increase in the percentage the addition of waste the marble to 10 % .Power drain employ water maximum objects test is at the percentage the addition of waste the marble 10 % with absorption capacity of water amounting to 5 %.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Gina Bachtiar, MT 2) Yusfita Chrisnawati, S.Pd, T. M.Sc
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	sawung yudo
Date Deposited:	22 Jun 2022 08:43
Last Modified:	22 Jun 2022 08:43
URI:	http://repository.unj.ac.id/id/eprint/30555

Actions (login required)

View Item