PEMANFAATAN BUBUK KACA SEBAGAI PENGGANTI SEBAGIAN SEMEN PADA PEMBUATAN PAVING BLOCK

DINI AZMI HANIFAH, . (2016) PEMANFAATAN BUBUK KACA SEBAGAI PENGGANTI SEBAGIAN SEMEN PADA PEMBUATAN PAVING BLOCK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text BAB I.pdf Download (143kB)
	Text BAB III.pdf Download (125kB)
	Text BAB II.pdf Download (695kB)
	Text BAB IV.pdf Download (584kB)
	Text COVER.pdf Download (52kB)
	Text BAB V.pdf Download (63kB)
	Text Halaman Pernyataan.pdf Download (423kB)
	Text DAFTAR ISI, GAMBAR, TABEL, LAMPIRAN.pdf Download (68kB)
	Text LEMBAR PENGESAHAN.pdf Download (379kB)
	Text LEMBAR PERSETUJUAN.pdf Download (351kB)
	Text Riwayat Hidup Penulis.pdf Download (70kB)
	Text ABSTRACT.pdf Download (57kB)
	Text DAFTAR PUSTAKA.pdf Download (88kB)
	Text ABSTRAK.pdf Download (73kB)
	Text KATA PENGANTAR.pdf Download (57kB)

Abstract

Penelitian ini bertujuan untuk memanfaatkan bahan alternatif yaitu bubuk kaca yang dapat digunakan untuk mengganti sebagian semen. Gagasan awal berpedoman pada pemikiran bahwa unsur kimia yang ada pada kaca beberapa diantaranya sama seperti yang ada pada semen, yaitu silika (SiO2). Penelitian ini menggunakan bubuk kaca sebagai bahan tambah dengan mengganti sebagian dari berat semen. Penelitian ini menggunakan lima macam varian persentase penambahan bubuk kaca yaitu 0%, 10%, 20%, 30% dan 50% dengan jumlah sampel tiap varian adalah 15 sampel. Pengujianpun dilakukan tiga tahap uji yaitu kuat tekan, ketahanan aus, dan penyerapan air sebagai syarat untuk mengetahui mutu yang sesuai dengan SNI 03-0691-1996 tentang Bata Beton Paving Block. Paving block diuji setelah melalui masa perawatan 28 hari. Dari hasil penelitian menunjukan bahwa penggunaan bubuk kaca pada paving block memang mengalami penurunan pada nilai rata – rata uji kuat tekan dan ketahanan ausnya dibanding paving block tanpa bubuk kaca. Akan tetapi pada persentase 30% dengan nilai rata – rata kuat tekan dan ketahanan ausnya adalah 40,18 Mpa dan 0,068 mm/menit masih termasuk kedalam kelas mutu yang sama dengan paving block persentase bubuk kaca 0% yaitu kelas mutu A. Untuk penyerapan airnya pada persentase bubuk kaca 30% adalah varian yang nilai rata – rata penyerapan airnya termasuk yang paling baik yaitu 4,12% termasuk kedalam kelas mutu B. Maka varian persentase bubuk kaca 30% adalah varian bubuk kaca yang paling baik untuk bahan alternatif dalam penggantian sebagian semen pada pembuatan paving block. This study aims to take advantage of an alternative that is the powder of glass that can be used to replace the most cement. The idea of the early based on the idea that the elements of chemicals are there in the same as some of them are there in cement, namely silica (SiO2). This study using the powder as material added to replace the most of the weight of cement. This study using five of variants percentage of additional powder glass are 0%, 10%, 20%, 30%, and 50% with the number of samples every variants are 15 samples. Testing done three the tests are compressive strength, wear resistance, and water absorption as qualified to know the quality of in accordance with the SNI 03-0691-1996 about the brick of concrete paving block. Paving block were tested after a period of treatment of 28 days. From the results of the study showed that the use of powdered glass in paving blocks are decreasing in value - average compressive strength test than paving blocks without glass powder. But the percentage of 30 % by value - average compressive strength and the wear resistance is 40.18 MPa and 0.068 mm / min still belongs to the same quality as the percentage of powdered glass paving blocks 0 % which are quality A. For water absorption in the percentage of 30 % glass powder is a variant of the value - average absorption of water , including the most good , namely 4.12% including into quality B. Then the variance percentage 30 % glass powder is a glass powder variant is best for partial replacement of alternative materials in cement on the manufacture of paving blocks.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Sitati Mussalammah, MT 2) Dra. Rosmawita Saleh, M. Pd
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	sawung yudo
Date Deposited:	26 Jun 2022 07:33
Last Modified:	26 Jun 2022 07:33
URI:	http://repository.unj.ac.id/id/eprint/30697

Actions (login required)

View Item