MODIFIKASI THIN FILM DARI VARIASI PERSEN BERAT POLIMER POLIMETIL METAKRILAT (PMMA) DENGAN MESOGEN REAKTIF RM257 MENGGUNAKAN METODE UV CURING

FITRI NULANDARI., . (2021) MODIFIKASI THIN FILM DARI VARIASI PERSEN BERAT POLIMER POLIMETIL METAKRILAT (PMMA) DENGAN MESOGEN REAKTIF RM257 MENGGUNAKAN METODE UV CURING. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 02 BAB I.pdf Download (650kB)
	Text 03 BAB II.pdf Restricted to Registered users only Download (768kB)
	Text 05 BAB IV.pdf Restricted to Registered users only Download (1MB)
	Text 01 COVER.pdf Download (1MB)
	Text 08 LAMPIRAN.pdf Restricted to Registered users only Download (690kB)
	Text 07 DAFTAR PUSTAKA.pdf Download (706kB)
	Text 06 BAB V.pdf Restricted to Registered users only Download (579kB)
	Text 04 BAB III.pdf Restricted to Registered users only Download (652kB)

Abstract

Ketertarikan pada bahan polimer telah tumbuh terus-menerus dalam beberapa dekade terakhir dan penelitian mengenai pembuatan film tipis dari mesogen reaktif yang ditambahkan dengan polimer Polimetil metakrilat (PMMA) dan juga Poliamida 6 (PA6) menggunakan metode spin coating. Penambahan kristal cair nematik dengan polimer Polimetil Metakrilat dapat menghasilkan Jaringan Polimer Kristal Cair (Liquid Crystal Network) Tujuan dari penelitian ini adalah untuk mengetahui sifat dan karakteristik dari hasil modifikasi thin film PMMA/RM257 menggunakan metode UV Curing. Thin film yang dibuat dengan perbedaan konsentrasi PMMA yaitu sebesar 15%, 25%, 35% dan 45%. Proses polimerisasi dilakukan dengan metode uv curing menggunakan lampu uv 25 watt selama 5 menit. Karakterisasi menggunakan FTIR mengkonfirmasi bahwa ikatan C=C vinyl pada monomer hilang, hasil karakterisasi XRD menunjukkan film berada pada fasa amorf, dan dari morfologi film yang dihasilkan yaitu adanya penggumpalan atau aglomerasi dari interaksi PMMA dan RM257. Interest in polymeric materials has grown steadily in recent decades and research on the manufacture of thin films from reactive mesogens added to polymers Polymethyl methacrylate (PMMA) and also Polyamide 6 (PA6) using spin coating method. The addition of nematic liquid crystals with Polymethyl Methacrylate polymer can produce Liquid Crystal Network. The purpose of this study was to determine the properties and characteristics of the modified PMMA/RM257 thin film using the UV Curing method. Thin films made with PMMA variant concentrations of 15%, 25%, 35% and 45%. The polymerization process was carried out by the uv curing method using a 25 watt uv lamp for 5 minutes. Characterization using FTIR confirmed that the vinyl C=C bond in the monomer was lost, XRD characterization results showed the film was in an amorphous phase, and from the morphology of the resulting film there was agglomeration or agglomeration from PMMA and RM257 interactions.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Afrizal, M.Si ; 2). Dr. Setia Budi, M.Sc
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	Users 14629 not found.
Date Deposited:	13 Jul 2022 03:09
Last Modified:	13 Jul 2022 03:09
URI:	http://repository.unj.ac.id/id/eprint/31716

Actions (login required)

View Item