PEMANFAATAN ABU CANGKANG KERANG LOKAN SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN PADA BETON

FADILLAH IKHSAN NURAHMAN, . (2016) PEMANFAATAN ABU CANGKANG KERANG LOKAN SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN PADA BETON. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 4. ABSTRAK INDO.pdf Download (6kB)
	Text 5. ABSTRACT ENG.pdf Download (12kB)
	Text 9. DAFTAR RIWAYAT HIDUP.pdf Download (8kB)
	Text 3. HALAMAN PERNYATAAN.pdf Download (317kB)
	Text 6. KATA PENGANTAR.pdf Download (33kB)
	Text 7. DAFTAR ISI.pdf Download (32kB)
	Text 1. COVER.pdf Download (12kB)
	Text BAB III.pdf Download (137kB)
	Text BAB V.pdf Download (13kB)
	Text BAB II.pdf Download (110kB)
	Text BAB I.pdf Download (29kB)
	Text 2. HALAMAN PENGESAHAN.pdf Download (212kB)
	Text BAB IV.pdf Download (97kB)

Abstract

Penelitian ini bertujuan untuk mengetahui kegunaan abu cangkang kerang lokan pada pengujian kuat tekan beton dalam upaya untuk mengetahui kuat tekan maksimum pada beton dengan variasi persentase yaitu, 0%, 5%, 10%, dan 15% dari jumlah berat semen untuk rancangan beton f’c 20 MPa dengan faktor air semen 0,55 dan slump 100±20 mm. Penelitian ini dilaksanakan di Laboratorium Uji Bahan Universitas Negeri Jakarta pada bulan Mei 2016 hingga Juni 2016. Bahan tambah pembuatan beton dalam penelitian ini adalah abu cangkang kerang lokan yang dihancurkan menggunakan mesin disk mill dibakar dengan suhu 8000C selama 4 jam. Metode penelitian ini menggunakan metode eksperimen dengan benda uji silinder diameter 15 cm dan tinggi 30 cm dengan jumlah benda uji sebanyak 60 buah. Pengujian kuat tekan beton menggunakan alat CrushingTest Machine. Hasil penelitian ini menunjukkan bahwa terdapat perbedaan pada beton kontrol dan beton campuran abu cangkang kerang lokan. Semakin tinggi kadar abu cangkang kerang lokan akan semakin memperkecil kuat tekan beton. Hasil pengujian beton campuran abu cangkang kerang lokan yang optimum adalah sebesar 10% dengan kuat tekan rata-rata beton tertinggi yaitu 20,84 MPa ***** This study aim this research is to know the use of ash shell mussels lokan in testing of compressive pressing power of in order to know maximum pressing power in concrete in various percentages, that are 0 % , 5 % , 10 % , and 15 % from the weight of cement for concrete design f ' c 20 MPa with element of water cement factor of 0.55 and a slump of 100 ± 20 mm. This research was conducted at the Material Testing Laboratory , State University of Jakarta in May 2016 to June 2016. Materials added the manufacture of concrete in this study is gray seashell shells were destroyed using a machine disk mill burned at a temperature of 800ºC for 4 hours . This research method using the experimental method to the test object cylinder diameter of 15 cm and 30 cm high with the number of test objects as much as 60 pieces . Testing the compressive strength of concrete using the tool CrushingTest Machine. The results of this study indicate that there are differences in the control of concrete and concrete mixture of ash shells seashell . The higher the ash content seashell shells will further reduce the compressive strength of concrete . The test results of concrete mixture of ash shells seashell optimum is 10% with an average compressive strength of concrete high of 20.84 MPa .

Item Type:	Thesis (Sarjana)
Additional Information:	1). Anissah, M.T. ; 2). Dra. Daryati, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 14626 not found.
Date Deposited:	14 Jul 2022 01:21
Last Modified:	14 Jul 2022 01:21
URI:	http://repository.unj.ac.id/id/eprint/31743

Actions (login required)

View Item