PENGARUH PENAMBAHAN SILIKA SINTETIS & BIO-SILIKA TERHADAP SIFAT MEKANIK MATERIAL CFRP (CARBON FIBER REINFORCED POLYMER)

ADIB MUCHTAR HUZAEFAH, . (2022) PENGARUH PENAMBAHAN SILIKA SINTETIS & BIO-SILIKA TERHADAP SIFAT MEKANIK MATERIAL CFRP (CARBON FIBER REINFORCED POLYMER). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
Cover.pdf

Download (894kB)
[img] Text
BAB 1.pdf

Download (219kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (654kB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (603kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (857kB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (146kB) | Request a copy
[img] Text
Daftar Pustaka.pdf

Download (211kB)
[img] Text
Lampiran.pdf
Restricted to Registered users only

Download (794kB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui hubungan antara penambahan silika sintetis dan bio-silika pada matriks komposit untuk melihat pengaruh nya terhadap sifat mekanik CFRP, untuk melihat hasil penambahan silika sintetis yaitu sodium silikat dan penambahan bio-silika yaitu ekstraksi abu sekam padi pada matriks komposit maka akan dilakukan beberapa pengujian, yaitu pengujian tarik, pengujian bending, dan pengujian tekan. Metode penelitian ini adalah metode eksperimental. Metode ini membandingkan hasil data pengujian yang didapatkan pada mesin pengujian tarik, bending, dan tekan. Dari hasil penelitian ini. Hasil penambahan Bio-silika 10ml memiliki hubungan positif dan signifikan dalam kekuatan tarik memiliki nilai 305.85 N/mm2, Pada hasil penambahan Bio-silika 20ml memiliki hubungan positif dan menurunkan nilai dalam kekuatan tarik menjadi 272.15 N/mm2, Lalu pada penambahan Bio-silika 30ml kekuatan tarik turun menjadi 108.62 N/mm2. Hasil penambahan Silika sintetis dan Bio-silika 10ml, 20ml, dan 30ml, memiliki hubungan pada pengujian bending yaitu menurunkan nilai modulus of rupture pada material tersebut. semakin banyak pemberian silika dan bio-silika maka akan menurunkan nilai modulus of rupture material tersebut. Hasil penambahan Silika sintetis dan Bio-silika 10ml, 20ml, dan 30ml, memiliki hubungan pada pengujian tekan yaitu menaikkan nilai regangan pada material tersebut, semakin banyak banyak pemberian silika dan bio-silika maka akan menaikan nilai regangan material tersebut. **** This study aims to determine the relationship between the addition of syhntetic silica and biosilica in the composite matrix to see its effect on the mechanical properties of CFRP, to see the results of the addition of silica and biosilica in the composite matrix, several tests will be carried out, namely tensile testing, bending testing, and compression testing. This research method is an experimental method. This method compares the results of the test data obtained on tensile, bending, and pressing testing machines. From the results of this study. The result of adding bio-silica 10ml has a positive and significant relationship in tensile strength has a value of 305.85 N/mm2 at the addition of bio-silica 10ml, In the result of adding bio-silica 20ml has a positive relationship and lowers the value in tensile strength to 272.15 N/mm2, Then at the addition of bio-silica 30ml tensile strength drops to 108.62 N/mm2. The results of the addition of syhntetic silica and bio-silica of 10ml, 20ml, and 30ml, have a relationship in bending testing, Reducing the value of the modulus of rupture in the material. the more silica and bio-silica are given it will reduce the modulus value of the material rupture. The results of the addition of syhntetic silica and bio-silica 10ml, 20ml, and 30ml, have a relationship in compressive testing, its increasing the strain value of the material, the more silica and bio-silica are given, the more strain the material will increase. Keywords : Test, Tensile, Bending, Press, Silica, Bio-silica

Item Type: Thesis (Sarjana)
Additional Information: 1). Drs. Tri Bambang AK. M.Pd. 2). Dr. Himawan Hadi Sutrisno M.T.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Users 15862 not found.
Date Deposited: 06 Sep 2022 02:57
Last Modified: 06 Sep 2022 02:57
URI: http://repository.unj.ac.id/id/eprint/35045

Actions (login required)

View Item View Item