PENGARUH PENAMBAHAN SILIKA DARI ABU SEKAM PADI PADA MATERIAL KOMPOSIT CFRP (CARBON FIBER REINFORCED POLYMER) TERHADAP SIFAT TERMAL

CAHAYA ASA RAHMATILLAH, . (2022) PENGARUH PENAMBAHAN SILIKA DARI ABU SEKAM PADI PADA MATERIAL KOMPOSIT CFRP (CARBON FIBER REINFORCED POLYMER) TERHADAP SIFAT TERMAL. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (2MB)
[img] Text
BAB 1.pdf

Download (273kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (890kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (256kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (533kB)
[img] Text
LAMPIRAN.pdf
Restricted to Registered users only

Download (429kB) | Request a copy

Abstract

Komposit Carbon Fiber Reinforced Polymer (CFRP) merupakan material komposit bermatriks polimer yang diperkuat oleh serat karbon. Peningkatan penggunaan komposit CFRP untuk berbagai aplikasi, khususnya pada bidang otomotif menekankan pentingnya/signifikansinya dalam analisis sifat termal dari sistem rekayasa. Dalam upaya peningkatan sifat termal komposit CFRP, dilakukan eksperimen berupa penambahan silika dari abu sekam padi yang secara teori memiliki titik leleh yang tinggi dan dapat menurunkan laju rambat api pada material. Penelitian ini dilakukan untuk mengetahui pengaruh penambahan silika dari abu sekam padi terhadap stabilitas termal komposit CFRP. Pembuatan sampel komposit menggunakan resin epoksi, serat karbon jenis unidirectional long continous fiber, serta silika dari abu sekam padi dengan variasi komposisi: 0% (tanpa silika), 5%, 10%, 15%, 20%, dan 25%. Proses pembuatan dilakukan menggunakan metode Hand Lay-Up. Stabilitas termal semua sampel kemudian diuji menggunakan mesin Thermogravimetric Analysis (TGA). Kurva termogravimetri yang dihasilkan menunjukkan data nilai indikator stabilitas termal berupa temperatur onset ekstrapolasi, perubahan massa, dan temperatur dekomposisi. Berdasarkan hasil penelitian, dapat disimpulkan bahwa penambahan silika dari abu sekam padi sebanyak 15% merupakan sampel dengan nilai stabilitas termal tertinggi dan secara umum penambahan silika dari abu sekam padi pada komposit CFRP dapat meningkatkan sifat termalnya serta mampu menahan suhu ambien hingga 405,9 °C Carbon Fiber Reinforced Polymer (CFRP) is a polymer matrix composite material reinforced by carbon fiber. The increasing use of CFRP composites for various applications, particularly in the automotive field, emphasizes its importance in the analysis of the thermal properties in engineering systems. In the effort to improve the thermal properties of CFRP composites, an experiment was carried out in the form of adding silica from rice husk ash which theoretically has a high melting point and can reduce the rate of fire propagation of material. This research was conducted to determine the effect of the addition of silica from rice husk ash on the thermal stability of CFRP composites. Composite samples were made using epoxy resin, unidirectional long continuous carbon fiber, and silica from rice husk ash with various compositions: 0% (without silica), 5%, 10%, 15%, 20%, and 25%. The manufacturing process is carried out using the Hand Lay-Up method. The thermal stability of all samples were tested using a Thermogravimetric Analysis (TGA). The resulting thermogravimetric curve generated the data of thermal stability indicators values in the form of extrapolated onset temperature, mass change, and decomposition temperature. Based on the results of the research, it can be concluded that the addition of 15% silica from rice husk ash is the sample with the highest thermal stability value and generally, the addition of silica from rice husk ash to the CFRP composite can increase its thermal properties and can withstand ambient temperatures up to 405.9 °C

Item Type: Thesis (Sarjana)
Additional Information: 1). Dr. Himawan Hadi Sutrisno, S.T., M.T. ; 2). Ir. Yunita Sari, M.T., M.Si.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions: FT > S1 Rekayasa Keselamatan Kebakaran
Depositing User: Users 16124 not found.
Date Deposited: 07 Sep 2022 02:48
Last Modified: 07 Sep 2022 02:48
URI: http://repository.unj.ac.id/id/eprint/35144

Actions (login required)

View Item View Item