PENGARUH PENAMBAHAN VARIASI UNSUR ALUMINIUM (Al) TERHADAP STRUKTUR MIKRO, KEKERASAN, KETAHANAN KOROSI DAN SIFAT ANTI BAKTERI PADUAN KUNINGAN Cu-28Zn-1Sn-xAl

IBNU AWWALA, . (2021) PENGARUH PENAMBAHAN VARIASI UNSUR ALUMINIUM (Al) TERHADAP STRUKTUR MIKRO, KEKERASAN, KETAHANAN KOROSI DAN SIFAT ANTI BAKTERI PADUAN KUNINGAN Cu-28Zn-1Sn-xAl. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text BAB 1 PENDAHULUAN.pdf Download (136kB)
	Text BAB II LANDASAN TEORI.pdf Restricted to Registered users only Download (306kB)
	Text BAB V KESIMPULAN SARAN.pdf Restricted to Registered users only Download (115kB)
	Text COVER.pdf Download (310kB)
	Text DAFTAR PUSTAKA.pdf Download (136kB)
	Text BAB III METODOLOGI PENELITIAN.pdf Restricted to Registered users only Download (360kB)
	Text BAB IV PEMBAHASAN.pdf Restricted to Registered users only Download (259kB)

Abstract

Kuningan merupakan suatu logam paduan yang terdiri atas campuran logam tembaga dan seng. Kuningan sangat mudah untuk di bentuk ke dalam berbagai bentuk dan sebuah konduktor panas yang baik. Karena sifat-sifat tersebut, kuningan kebanyakan digunakan untuk membuat pipa, tabung, sekrup, radiator, alat musik, aplikasi kapal laut, dan casing cartridge untuk senjata api.. Sifat kuningan sangat dipengaruhi oleh unsur paduannya. Mangan, Silikon, Nikel, Aluminium, Timah Putih merupakan unsur pemadu utama dan memiliki sifat-sifat yang baik. Dalam penelitian ini dilakukan pada kuningan jenis cartridge brass dengan komposisi 70% Cu dan 30% Zn. Sifat mekanik cartridge brass dapat ditingkatkan dengan penambahan unsur paduan lain, pengujian korosi dan pengujian anti bakteri. Pengujian ini menguji pengaruh penambahan 0,5 %, 1%, dan 1,5 % wt Al pada paduan kuningan Cu-28Zn-1Sn terhadap struktur mikro dan kekerasan, kemudian dilanjutkan dengan proses pengujian korosi dan pengujian anti bakteri dengan menggunakan bakteri Escherichia Coli. Dari hasil penelitian, paduan kuningan Cu-28Zn-1Sn dengan variasi penambahan Al sebesar 0,25 %, 1%, dan 1.5% wt Al mempengaruhi nilai kekerasan dengan nilai tertinggi 73,28 VHN. Struktur mikro pada penambahan Al belum dapat diprediksikan dikarenakan diagram fasa nya belum didapatkan. Penambahan unsur aluminium terhadap paduan kuningan Cu-28Zn-1Sn mempengaruhi peningkatan zona hambat antibakteri dengan nilai 2.31 mm pada komposisi Cu-28Zn-1Sn�1.5Al. Nilai laju korosi pada paduan Cu-28Zn-1Sn-0.5Al. memiliki ketahanan korosi paling baik yaitu 1.104 mpy dengan kategori Excellent. ***** Brass is a metallic alloy which consists of a combination of metal copper and zinc. Brass is very easy to be formed into various forms and a good conductor of heat. By the reason of its properties, brass mostly used to make pipe, tube, screw, radiator, a musical instrument, on ships, and firearms cartridge cases. Brass properties is strongly influenced by its blend. Manganese, silicon, nickel, aluminium, white lead is the main blend and has good qualities. In this research, it was carried out on a type of brass which is cartridge brass with a composition of 70% Cu and 30% Zn. The mechanical properties of brass cartridges can be improved by the addition of other alloying elements, corrosion testing and anti�bacterial testing. This test tested the effect of adding 0,5 %, 1%, dan 1,5 % wt Al to the Cu�28Zn-1Sn brass alloy on the microstructure and hardness, then proceed with the process of corrosion testing and anti-bacterial testing using Escherichia Coli bacteria. From the results of the study, the brass alloy Cu-28Zn-1Sn with variations in the addition of Al of 0.25 %, 1%, and 1.5% wt Al affected the hardness value with the highest value of 73.28 VHN.. The microstructure of the addition of Al can’t be predicted because the phase diagram has not been obtained. The addition of aluminium elements to the brass alloy Cu-2 Zn-1Sn affects the increase in the antibacterial inhibition zone with a value of 2.31 mm at the composition of Cu�28Zn-1Sn-1.5Al. Corrosion rate value in Cu-28Zn-1Sn-0.5Al alloy. has the best corrosion resistance of 1,104 mpy with excellent category

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Imam Basori, M. T ; 2). Dr. Ferry Budhi Susetyo, M. T
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 14685 not found.
Date Deposited:	29 Sep 2022 06:02
Last Modified:	22 Jan 2024 05:33
URI:	http://repository.unj.ac.id/id/eprint/36513

Actions (login required)

View Item