PENGARUH ORIENTASI SUDUT PRINTING TERHADAP KEKUATAN TARIK HASIL 3D PRINTING DENGAN BAHAN ACRYLONITRILE BUTADINE STYRENE (ABS) DAN POLYATIC ACID (PLA)”

MUNZIR HAKIM, . (2023) PENGARUH ORIENTASI SUDUT PRINTING TERHADAP KEKUATAN TARIK HASIL 3D PRINTING DENGAN BAHAN ACRYLONITRILE BUTADINE STYRENE (ABS) DAN POLYATIC ACID (PLA)”. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (205kB)
	Text BAB 2.pdf Restricted to Registered users only Download (521kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (754kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (742kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (120kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (206kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (3MB) | Request a copy

Abstract

3D printing adalah salah satu proses manufaktur aditif untuk mewujudkan produk atau objek padat dengan struktur dan geometri yang kompleks dari hasil desain digital tiga dimensi dengan sistem komputerisasi dan dicetak lapis demi lapis secara berurutan. Tujuan daripada penelitian ini untuk mengetahui pengaruh orientasi sudut printing terhadap kekuatan tarik pada spesimen Acrylonitrile Butadine Styrene (ABS) dan Polyatic Acid (PLA). Serta untuk mengetahui seberapa besar kekuatan tarik maksimum dan minimum berdasarkan orientasi sudut yang berbeda-beda. Metode penelitian ini dirancang dengan pendekatan eksperimen atau uji coba pada 18 sampel spesimen. Pencetakan spesimen ini mengacu pada standar ASTM D638 dengan parameter layer thickness 0,1mm dan orientasi sudut objek 0°, 45° dan 90°. Pengujian kuat tarik dilakukan dengan mesin uji Tensile. Hasil penelitian menunjukkan bahwa orientasi sudut objek memiliki pengaruh terhadap kekuatan tarik spesimen ABS dan PLA. Semakin besar orientasi sudut objek, maka semakin kecil kekuatan tarik yang dimiliki spesimen tersebut. Kekuatan tarik tertinggi terdapat pada orientasi sudut 0° yang mencapai 24,99 MPa untuk ABS dan 35,12 MPa untuk PLA. Sedangkan kekuatan tarik spesimen terendah berada pada sudut orientasi 90° yang hanya sebesar 13,86 MPa untuk ABS dan 16,57 MPa untuk PLA. Ini menunjukkan bahwa spesimen PLA memiliki kekuatan tarik lebih baik dibanding spesimen ABS. ***** 3D printing is an additive manufacturing process for creating solid products or objects with complex structures and geometries from the results of a three-dimensional digital design with a computerized system and printed layer by layer sequentially. The purpose of this research is determine the effect of the orientation angle of printing on the tensile strength at specimen ABS and PLA. And then to find how much maximum and minimum tensile strength is based on different angle orientations. This research method was designed with an experimental or trial approach on 18 specimen samples. This specimen printing refers to the ASTM D638 standard with parameter layer thickness 0.1mm and object angle orientation of 0°, 45° and 90°. The tensile strength test was carried out with a Tensile machine. The results showed that angle orientation of the object has influence on tensile strength at ABS and PLA specimens. The greater angle orientation of the object, the smaller tensile strength of the specimen. The highest tensile strength is at 0° angle orientation which reaches 24.99 MPa for ABS and 35.12 MPa for PLA. Meanwhile, the lowest specimen tensile strength was at an orientation angle of 90° which was only 13.86 MPa for ABS and 16.57 MPa for PLA. This shows that PLA specimens have better tensile strength than ABS specimens.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ahmad Kholil, S.T.,M.T. ; 2). Dr. Eko Arif Syaefudin, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 17374 not found.
Date Deposited:	03 Mar 2023 02:01
Last Modified:	03 Mar 2023 02:01
URI:	http://repository.unj.ac.id/id/eprint/37492

Actions (login required)

View Item