AGAM RIZKIE TEO, . (2020) UJI KUAT TEKAN BETON RINGAN AGREGAT BATU APUNG DICOATIN DENGAN PENAMBHAAN SILICA FUME. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.
![[img]](http://repository.unj.ac.id/style/images/fileicons/text.png) |
Text
1. COVER.pdf Download (2MB) |
|
Text
2. BAB 1.pdf Download (2MB) |
|
Text
3. BAB 2.pdf Restricted to Registered users only Download (2MB) | Request a copy |
|
Text
4. BAB 3.pdf Restricted to Registered users only Download (2MB) | Request a copy |
|
Text
5. BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy |
|
Text
6. BAB 5.pdf Download (461kB) |
|
Text
7. DAFTAR PUSTAKA.pdf Download (507kB) |
|
Text
8. LAMPIRAN.pdf Download (14MB) |
Abstract
ABSTRAK AGAM RIZKIE TEO, Uji Kuat Tekan Beton Ringan Agregat Batu Apung di-coating Dengan Penambahan Silica Fume. Skripsi. Jakarta: Program Studi Pendidikan Teknaik Bangunan Universitas Negeri Jakarta. Beton merupakan bahan bangunan utama yang sering digunakan pada gedung bertingkat karena memiliki kuat tekan yang tinggi. Namun beton memiliki kelemahan pada beratnya sendiri yang cukup besar. Untuk itu diciptakan beton ringan dengan menggantikan agregat kasar pada beton dengan agregat ringan, salah satunya batu apung. Selain itu, beton ringan juga memiliki kekurangan, yaitu kuat tekannya yang rendah. Inovasi yang dilakukan untuk meningkatkan kuat tekan beton ringan adalah dengan melakukan pelapisan agregat batu apung dengan pasta semen dan menggunakan silica fume sebagai bahan tambah beton ringan. Tujuan dari penelitian ini adalah untuk mengetahui apakah beton ringan agregat batu apung yang di-coating dengan penambahan silica fume sebagai bahan tambah dengan persentase penambahan 0% sebagai kontrol, 5%, 10%, 15% dan 20% dari berat semen dapat digunakan sebagai dinding struktural sesuai SNI 03-3449-2002. Penelitian ini dilakukan di Laboratorium Bahan Universitas Negeri Jakarta, menggunakan metode eksperimen. Dalam penelitian ini agregat batu apung di-coating dengan pasta semen dengan perbandingan 1:1 dan disimpan selama 2 minggu sebelum digunakan. Silica fume yang digunakan pada penelitian ini mempunyai ukuran yang lolos ayakan no. 200. Menggunakan benda dengan bentuk silinder berdiameter 100 mm dan tinggi 200 mm, yang mana kuat tekan rencana fc’ 20 MPa, FAS 0,3 dan slump 25 mm – 100 mm. Pengujian kuat tekan beton mengacu pada SNI 03-1974-2011. Hasil penelitian menunjukkan penambahan silica fume pada kuat tekan beton ringan dengan variasi persentase 0%, 5%, 10%, 15% dan 20% terhadap berat semen berturut – turut sebesar 12,31 MPa, 15,27 MPa, 15,88 MPa, 16,55 MPa dan 19,20 MPa. Dengan demikian diperoleh kuat tekan optimum pada variasi 20% sebesar 19,20 MPa. Kata Kunci : Beton Ringan, Batu Apung, Coating, Silica Fume, Kuat Tekan Beton Ringan. ABSTRACT AGAM RIZKIE TEO, Compressive Test of Coated Pumice Lightweight Concrete with Silica Fume Addition. Thesis. Jakarta: Building Engineering Education Study Program, Faculty of Engineering, State University of Jakarta, 2019. Concrete is the most common used material in construction industry activities because it has advantages such as high compressive strength. However, it has a weakness in its own weight which is quite heavy. For this reason, lightweight concrete was created by replacing the coarse aggregate with lightweight aggregate, one of which is pumice. But lightweight concrete also has a disadvantage, that is low compressive strength. To improve the compressive strength of lightweight concrete, the pumice aggregates are coated with cement paste and using silica fume as an addition material. This research aims to determine the effect of silica fume as an addition material on compressive strength of lightweight concrete with a number of variations 0%, 5%, 10%, 15% and 20% of the weight of cement. This research was conducted at the Laboratory of Materials, State University of Jakarta, using an experimental method. In this study the pumice aggregate was coated with cement paste in ratio of 1:1 and stored for two weeks before use. Silica fume used in this study was sized to pass the sieve no. 200, using cylindrical specimens with a dimeter of 100 mm and a height of 200 mm, which is the compressive strength of the plan is fc’ 20 MPa, FAS 0,3 and slump 25 mm – 100 mm. The compressive strength testing refers to SNI 03-1974-2011. The results showed the addition of silica fume of compressive strength of lightweight concrete of 0%, 5%, 10%, 15% and 20% to the weight of cement respectively 12.31 MPa, 15.27 MPa, 15.88 MPa, 16.55 MPa and 19.20 MPa. Thus the optimum compressive strength is obtained at a variation of 20% of 19.20 MPa. Keywords : Lightweight Concrete, Pumice, Coating, Silica Fume, Compressive Strength
| Item Type: | Thesis (Sarjana) |
|---|---|
| Additional Information: | 1). Kusno Adi Sambowo, S.T, Ph.D. ; 2). Ririt Aprilin S, M.Sc.Eng |
| Subjects: | Teknologi dan Ilmu Terapan > Teknik Sipil |
| Divisions: | FT > S1 Pendidikan Teknik Bangunan |
| Depositing User: | Users 1056 not found. |
| Date Deposited: | 05 Mar 2020 11:49 |
| Last Modified: | 05 Mar 2020 11:49 |
| URI: | http://repository.unj.ac.id/id/eprint/3989 |
Actions (login required)
 |
View Item |