PEMANFAATAN PLASTIK JENIS PET DAN METAKAOLIN SEBAGAI PENGGANTI SEBAGIAN AGREGAT HALUS PADA PAVING BLOCK SEBAGAI IMPLEMENTASI MATA KULIAH PRAKTEK UJI BAHAN PROGRAM STUDI PENDIDIKAN TEKNIK BANGUNAN UNIVERSITAS NEGERI JAKARTA

WAHYU WIBOWO, . (2023) PEMANFAATAN PLASTIK JENIS PET DAN METAKAOLIN SEBAGAI PENGGANTI SEBAGIAN AGREGAT HALUS PADA PAVING BLOCK SEBAGAI IMPLEMENTASI MATA KULIAH PRAKTEK UJI BAHAN PROGRAM STUDI PENDIDIKAN TEKNIK BANGUNAN UNIVERSITAS NEGERI JAKARTA. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (479kB)
	Text BAB 1.pdf Download (105kB)
	Text BAB 2.pdf Restricted to Registered users only Download (269kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (286kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (277kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (81kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (148kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (897kB) | Request a copy

Abstract

ABSTRAK Wahyu Wibowo, Daryati, Arris Maulana, “Pemanfaatan Plastik Jenis PET dan Metakaolin Sebagai Pengganti Sebagian Agregat Halus Pada Paving block Sebagai Implementasi Mata Kuliah Praktek Uji Bahan Program Studi Pendidikan Teknik Bangunan Universitas Negeri Jakarta”. Skripsi, Jakarta: Jurusan Pendidikan Teknik Bangunan, Fakultas Teknik, Universitas Negeri Jakarta, 2023. Penelitian ini bertujuan untuk memanfaatkan plastik PET dan metakaolin sebagai bahan pengganti sebagian agregat halus sehinggan dapat menghasilkan paving block kelas mutu B sesuai ketentuan SNI 03-0691-1996. Metode yang digunakan pada penelitian ini adalah metode eksperimen dangan benda uji berupa paving block dari plastik PET dan metakaolin sebagai bahan pengganti sebagian agregat halus dengan variasi 0% (kontrol), 2,5%, 5%, 7,5% dan 10%. Benda uji setiap variasi berjumlah 10 buah yang berbentuk balok dengan dimensi 21 cm x 10,5 cm x 6 cm dan dicetak dengan mesin press vibrator. Untuk pengujian yang dilakukan adalah pengujian tampak dan ukuran, pengujian daya serap air, pengujian kuat tekan dan pengujian ketahanan aus yang mengacu pada ketentuan SNI 03-0691-1996. Hasil peneltian pengujian kuat tekan paving block dari plastik PET dan metakaolin dengan variasi 0% (kontrol), 2,5%, 5%, 7,5% dan 10% berturut-turut adalah 19,59 MPa (mutu B), 27,92 MPa (mutu B), 28,76 MPa (mutu B), 26,01 MPa (mutu B) dan 14,57 MPa (mutu C). Nilai kuat tekan tertinggi didapatkan pada variasi 5% dengan nilai sebesar 28,76 MPa. Berdasarkan hasil penelitian tersebut bisa disimpulkan bahwa pemanfaatan plastik PET dan metakaolin sebagai pengganti sebagian agregat halus pada paving block dapat mencapai mutu B yang bisa digunakan pada pelataran parkir. Kata Kunci : Agregat Halus, Metakaolin, Paving Block, Plastik PET ********** ABSTRACT Wahyu Wibowo, Daryati, Arris Maulana, “Utilization of PET and Metakaolin as a Partial Substitute for Fine Aggregates Paving block As the Implementation of Material Test Practice Courses in the Building Engineering Education Study Program, Jakarta State University. Thesis, Jakarta: Department of Building Engineering Education, Faculty of Engineering, Jakarta State University, 2023. This study aims to utilize plastic PET and metakaolin as a partial replacement for fine aggregates that can produce paving block quality class B according to the provisions of SNI 03-0691-1996. The method used in this study is an experimental method with test objects in the form of paving block of PET plastic and metakaolin as a partial replacement for fine aggregate with variations of 0% (control), 2.5%, 5%, 7.5% and 10%. The test objects for each variation amounted to 10 pieces in the form of blocks with dimensions of 21 cm x 10.5 cm x 6 cm and were printed with a machine press vibrator. The tests carried out are impact and size tests, water absorption tests, compressive strength tests and wear resistance tests referring to the provisions of SNI 03-0691-1996. Results Study This is obtained, for compressive strength testing paving block of PET plastic and metakaolin with variations of 0% (control), 2.5%, 5%, 7.5% and 10% respectively were 19.59 MPa (B quality), 27.92 MPa (B quality), 28.76 MPa (B quality), 26.01 MPa (B quality) and 14.57 MPa (C quality). The highest compressive strength value was obtained at 5% variation with a value of 28.76 MPa. Based on the results of this study it can be concluded that the use of PET plastic and metakaolin as a partial substitute for fine aggregate in paving block can reach quality B which can be used in parking lots. Keywords: Fine Aggregate, Metakaolin, Paving Block, PET Plastic

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dra. Daryati, MT ; 2). Drs. Arris Maulana, ST, MT
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 19630 not found.
Date Deposited:	06 Sep 2023 04:39
Last Modified:	06 Sep 2023 04:39
URI:	http://repository.unj.ac.id/id/eprint/40692

Actions (login required)

View Item