PENGUJIAN ENERGI FRAKTUR PADA BETON NORMAL STRUKTURAL MUTU K-175 DENGAN METODE THREE POINT BENDING TEST

FARHAN SEPTIANTO, . (2023) PENGUJIAN ENERGI FRAKTUR PADA BETON NORMAL STRUKTURAL MUTU K-175 DENGAN METODE THREE POINT BENDING TEST. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (979kB)
	Text BAB 1.pdf Download (448kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (697kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (613kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (318kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (543kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (3MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui kuat tekan dan energy fraktur pada beton normal structural mutu K-175 menggunakan takikan (notch). Takikan (notch) yang diterapkan yaitu kedalaman 50 mm dan lebar 5 mm. Adanya takikan (notch) bertujuan untuk mengalokasikan retak supaya dapat terukur dengan jelas dan mudah dicermati. Campuran beton yang digunakan berupa beton instan (drymix) dengan mutu K-175. Metode penelitian yang digunakan dalam penelitian ini yaitu menggunakan metode eksperimen dengan benda uji silinder yang berdimensi lebar 100 mm, tinggi 200 mm yang berjumlah 3 benda uji, dan benda uji silinder yang berdimensi lebar 100 mm, tinggi 100 mm, panjang 850 mm yang berjumlah 1 benda uji. Pengujian kuat tekan silinder mengacu pada SNI 1974-2011, sedangkan pengujian energy fraktur balok mengacu pada RILEM TC 50-FMC. Pada penelitian ini didapatkan hasil pengujian kuat tekan beton silinder mutu K-175 pada umur 7 hari sebesar 12, 525 MPa, 8,510 MPa, dan 9,301 MPa. Dari nilai tersebut dikonversi ke umur 28 hari yang menghasilkan kuat tekan sebesar 19,270 MPa; 13,092 MPa; dan 14,309 MPa. Sedangkan nilai energy fraktur pada beton balok bertakik 5 mm mutu K-175 didapat sebesar 41,854 N/m. Nilai energy fraktur didapat melalui interpolasi dengan benda uji mutu K-175 bertakik 6 mm dan mutu K-250 bertakik 5 mm dan 6 mm. Hal ini dilakukan karena benda uji mengalami kegagalan sebelum dilakukan pengujian yang diakibatkan keropos dan berongganya benda uji. ***** This study aims to determine the compressive strength and fracture energy of normal structural concrete of K-175 quality using notches (notch). Notch (notch) that is applied is a depth of 50 mm and a width of 5 mm. There is a notch (notch) aims to allocate cracks so that they can be measured clearly and easily observed. The concrete mixture used is instant concrete (drymix) with quality K-175. The research method used in this study was to use the experimental method with cylindrical test objects with dimensions of 100 mm wide, 200 mm high, totaling 3 test objects, and cylindrical test objects with dimensions of 100 mm wide, 100 mm high, 850 mm long, totaling 1 test object. The cylinder compressive strength test refers to SNI 1974-2011, while the beam fracture energy test refers to RILEM TC 50-FMC. In this study, the compressive strength test results for cylindrical concrete of K-175 quality at 7 days of age were 12.525 MPa, 8.510 MPa and 9.301 MPa. From this value it is converted to a 28 day age which produces a compressive strength of 19.270 MPa; 13.092 MPa; and 14.309 MPa. Meanwhile, the fracture energy value of 5 mm notched concrete beams of K-175 quality was 41.854 N/m. Fracture energy values were obtained by interpolating with test specimens of K-175 quality with 6 mm notches and K-250 quality with 5 mm and 6 mm notches. This is done because the test object failed before the test was carried out due to the porousness and hollowness of the test object.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Anisah, MT ; 2). Dra. Daryati, MT
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 19987 not found.
Date Deposited:	04 Sep 2023 23:53
Last Modified:	05 Sep 2023 01:29
URI:	http://repository.unj.ac.id/id/eprint/41101

Actions (login required)

View Item