PENGARUH SILIKA (SiO2) DARI ABU SEKAM PADI TERHADAP KETAHANAN TERMAL MATERIAL KOMPOSIT CFRP (CARBON FIBER REINFORCED POLYMER) DENGAN METODE VACUUM BAG

FARHAH AL FAIZAH, . (2023) PENGARUH SILIKA (SiO2) DARI ABU SEKAM PADI TERHADAP KETAHANAN TERMAL MATERIAL KOMPOSIT CFRP (CARBON FIBER REINFORCED POLYMER) DENGAN METODE VACUUM BAG. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Download (453kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (311kB) | Request a copy
	Text DAFTAR PUSTAKA..pdf Download (1MB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Carbon Fiber Reinforced Polymer (CFRP) merupakan material komposit bermatriks polimer diperkuat dengan serat karbon. Penggunaan komposit CFRP umum digunakan pada industri otomotif khususnya pada suku cadang kendaraan motor. Terjadinya insiden kebakaran bagian fairing sepeda motor yang terbuat dari material CFRP pada kompetisi MotoGP Mandalika tahun 2022 menunjukkan pentingnya aspek keselamatan bagi pengendara sepeda motor, sehingga diperlukan komposit yang memiliki ketahanan termal yang baik. Untuk meningkatkan ketahanan termal pada komposit CFRP, diperlukan bahan tambahan berupa ekstrak silika dari abu sekam padi. Penelitian ini dilakukan untuk mengetahui pengaruh penambahan silika terhadap ketahanan termal komposit CFRP dengan metode vacuum bag. Pembuatan sampel komposit menggunakan resin poliester, serat karbon jenis bidirectional woven fiber, serta ekstrak silika dengan variasi komposisi: 0g (tanpa silika), 5g, 15g, 25g, dan 35g. CFRP diuji menggunakan Thermogravimetric Analysis (TGA). Berdasarkan hasil penelitian, dapat disimpulkan bahwa penambahan silika dari abu sekam padi pada CFRP menunjukkan tren positif terhadap ketahanan termalnya yaitu dengan penambahan sebanyak 35g mampu menahan suhu ambien hingga 414,2 C. Carbon Fiber Reinforced Polymer (CFRP) is a polymer matrix composite material reinforced with carbon fiber. The use of CFRP composites is commonly used in the automotive industry, especially in motor vehicle parts. The occurrence of a fire incident on a motorcycle fairing made of CFRP material at the Mandalika 2022 MotoGP competition shows the importance of safety aspects for motorcyclists, so composites that have good thermal resistance are needed. To improve the thermal resistance of CFRP composites, additional materials are needed in the form of silica extract from rice husk ash. This research was conducted to determine the effect of silica addition on the thermal resistance of CFRP composites using the vacuum bag method. Making composite samples using polyesterresin, bidirectional woven carbon fiber, and silica extract with variations in composition: 0g (without silica), 5g, 15g, 25g, and 35g. CFRP was tested using Thermogravimetric Analysis (TGA). Based on the research results, it can be concluded that the addition of silica from rice husk ash to CFRP shows a positive trend towards its thermal resistance, namely with the addition of as much as 35g being able to withstand ambient temperatures up to 414,2ºC.. Keywords: Rice Husk Ash, Thermal Resistance, CFRP composites, Silica

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ir. Himawan Hadi Sutrisno, S.T., M.T. 2). Ir. Yunita Sari, M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Otomotif, Astronotika Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Rekayasa Keselamatan Kebakaran
Depositing User:	Users 21343 not found.
Date Deposited:	01 Feb 2024 05:10
Last Modified:	01 Feb 2024 05:10
URI:	http://repository.unj.ac.id/id/eprint/44129

Actions (login required)

View Item