PENGARUH TINGGI TEMPERATUR PENGERINGAN TERHADAP KARAKTERISTIK COATING POLYURETHANE PADA BAJA SPCC

TEGUH WIBOWO, . (2024) PENGARUH TINGGI TEMPERATUR PENGERINGAN TERHADAP KARAKTERISTIK COATING POLYURETHANE PADA BAJA SPCC. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (159kB)
	Text BAB 2.pdf Restricted to Registered users only Download (910kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (860kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (526kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (145kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (284kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penggunaan baja SPCC pada bagian luar produk membuat lebih mudah terpapar korosi serta membuat daya tarik menjadi berkurang. Salah satu tindakan yang diperlukan adalah melakukan coating yang berkualitas. Kualitas coating dapat dilihat dari segi visual, ketebalan, daya kilap, dan daya lekat. Polyurethane merupakan salah satu jenis bahan yang digunakan dalam proses coating karena memiliki sifat yang baik. Selain itu, agar kualitas kebersihan dapat terjaga dan waktu untuk melakukan coating dapat lebih cepat maka perlu dilakukan proses pengeringan dengan oven. Namun, belum diketahui penggunaan temperatur pengeringan yang tepat untuk mendapatkan kualitas yang baik. Oleh sebab itu, Penelitian ini bertujuan untuk mengetahui pengaruh temperatur pengeringan terhadap tampilan visual, ketebalan, daya kilap, dan daya lekat coating polyurethane pada baja SPCC. Temperatur pengeringan spesimen yang digunakan yaitu 70°C, 100°C, dan 130°C dengan waktu pengeringan selama 20 menit. Hasil pengujian yang diperoleh pada tampilan visual tinggi temperatur pengeringan membuat tampilan yang diperoleh semakin gelap. Pengujian ketebalan menunjukkan bahwa pada temperatur pengeringan terkecil 70°C mendapatkan hasil ketebalan yang lebih besar yaitu 50,15 µm. Sama dengan uji ketebalan, nilai pada pengujian daya kilap juga menunjukkan bahwa tinggi temperatur 70°C yang paling rendah menghasilkan daya kilap yang lebih baik sebesar 7,33 GU. Hasil yang berbeda didapatkan pada pengujian daya lekat, di mana pada semua temperatur pengeringan mendapatkan hasil yang sama yaitu 5B atau tidak adanya cat yang terkelupas. The use of SPCC steel on the exterior of products makes them more susceptible to corrosion and reduces their aesthetic appeal. One necessary action is to apply a high-quality coating. The quality of the coating can be assessed in terms of its visual appearance, thickness, gloss, and adhesion. Polyurethane is one of the materials used in the coating process due to its favorable properties. Additionally, to maintain cleanliness and speed up the coating process, oven drying is needed. However, the appropriate drying temperature to achieve high quality is not yet known. Therefore, this research aims to determine the effect of drying temperature on the visual appearance, thickness, gloss, and adhesion of polyurethane coating on SPCC steel. The drying temperatures used in this study are 70°C, 100°C, and 130°C with a drying time of 20 minutes. The results showed that higher drying temperatures resulted in darker visual appearances. The thickness test indicated that the lowest drying temperature of 70°C produced a greater thickness of 50.15 µm. Similarly, the gloss test results showed that the lowest temperature of 70°C yielded better gloss with a value of 7.33 GU. Different results were obtained in the adhesion test, where all drying temperatures produced the same result of 5B, indicating no peeling of the coating.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Ferry Budhi Susetyo, M.T.,M.Si. 2) Rani Anggrainy, S.Pd.,M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Otomotif, Astronotika Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 22671 not found.
Date Deposited:	19 Jul 2024 00:18
Last Modified:	19 Jul 2024 00:18
URI:	http://repository.unj.ac.id/id/eprint/45702

Actions (login required)

View Item