PENGARUH SERBUK ALUMUNIUM TERHADAP KEKUATAN TARIK DAN TEKAN PADA KOMPOSIT ALAMI SERBUK KAYU DAN SERAT KELAPA UNTUK BAHAN KAMPAS KOPLING SEPEDA MOTOR MATIC

ALVADILAH DEISYHA RAMADHAN, . (2024) PENGARUH SERBUK ALUMUNIUM TERHADAP KEKUATAN TARIK DAN TEKAN PADA KOMPOSIT ALAMI SERBUK KAYU DAN SERAT KELAPA UNTUK BAHAN KAMPAS KOPLING SEPEDA MOTOR MATIC. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (1MB)
	Text BAB 2.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (1MB)
	Text LAMPIRAN LAMPIRAN.pdf Restricted to Registered users only Download (3MB) | Request a copy

Abstract

Tujuan penelitian ini adalah untuk menemukan kampas kopling pengganti asbes dengan komposit yang bervariasi optimal sebagai kampas kopling sentrifugal CVT pada sepeda motor matic. Pada penelitian ini akan dibuat dari serbuk alumunium sebagai penambahan pada komposit alami serat kelapa dan serbuk kayu sengon. Komposit akan dilakukan pengujian untuk mengetahui spesifikasi komposit dengan pengujian Tarik,pengujian Tekan, dan Uji struktur mikro. Untuk mengetahui komposisi komposit yang sesuai pada nilai kekuatan tarik dan tekan serta struktur mikro yang optimal, maka penelitian ini dilakukan dengan cara memvariasikan 5 komposisi spesimen yang berbeda secara persentase kandungan. Setelah dilakukan penelitian, penulis mendapati data kekuatan tarik dan tekan serta struktur mikro pada tiap-tiap komposit. Berikut adalah data yang sudah dianalisis yaitu pada spesimen A3 memiliki nilai kekuatan tarik tinggi dibandingkan dengan spesimen uji kampas kopling komposit lainnya sebesar 15,66 Mpa.. Dengan kandungan alumunium sebesar 15%, serbuk kelapa 20% dan serbuk kayu sengon 20% menjadikan tingkat kekuatan tarik menjadi lebih kuat daripada spesimen uji lainnya Pada uji kekuatan tekan , spesimen 5 yaitu pada kode spesimen A2 memiliki nilai kekuatan tekan tinggi dibandingkan dengan spesimen uji kampas kopling komposit lainnya sebesar 105,62 Mpa.. Dengan kandungan alumunium sebesar 10%, serbuk kelapa 20% dan serbuk kayu sengon 20% menjadikan tingkat kekuatan tekan menjadi lebih kuat daripada spesimen uji lainnya ***** The purpose of this research is to find clutch that replace asbestos with composites that vary optimally as CVT centrifugal clutch on automatic motorbikes. This research will be made from alumunium powder as an addition to a natural composite of coconut fibre and sengon wood powder. The composite will be tested to determine the composite specifications with tensile testing, compressive testing, and microstructure testing. To find out the appropriate composite composition on the value of tensile and compressive strength and optimal microstructure, this research was conducted by varying 5 different specimen compositions in percentage content. After the research, the author found tensile and compressive strength data and microstructure on each composite. The following data has been analysed, namely specimen A3 has a high tensile strength value compared to other composite clutch lining test specimens of 15.66 Mpa. With an alumunium content of 15%, 20% coconut powder and 20% sengon wood powder, the tensile strength level becomes stronger than other test specimens. In the compressive strength test, specimen 5, namely specimen code A2, has a high compressive strength value compared to other composite clutch lining test specimens of 105.62 Mpa.. With an alumunium content of 10%, 20% coconut powder and 20% sengon wood powder, the compressive strength level becomes stronger than the other test specimens.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ahmad Kholil, S.T., M.T. ; 2). Dr. Eko Arif Syaefudin, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Al Vadilah Deisyha Ramadhan .
Date Deposited:	25 Jul 2024 01:47
Last Modified:	25 Jul 2024 01:47
URI:	http://repository.unj.ac.id/id/eprint/46291

Actions (login required)

View Item