PENGARUH COLD ROLLING DAN ANNEALING TERHADAP NILAI KEKERASAN DAN KETAHANAN KOROSI PADA LOGAM KUNINGAN CU-15ZN-1,5SN

ARIL GIRI SURYA, . (2024) PENGARUH COLD ROLLING DAN ANNEALING TERHADAP NILAI KEKERASAN DAN KETAHANAN KOROSI PADA LOGAM KUNINGAN CU-15ZN-1,5SN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text cover.pdf Download (1MB)
	Text BAB 1.pdf Download (270kB)
	Text BAB 2.pdf Restricted to Registered users only Download (572kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (542kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (495kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (259kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (379kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (405kB) | Request a copy

Abstract

Kuningan adalah logam paduan Tembaga (Cu) dan Seng (Zn). Tembaga merupakan komponen utama dari kuningan. Jumlah kandungan seng mempengaruhi warna kuningan. Kuningan mempunyai macam macam jenis yang dipengaruhi oleh kandungan seng. Jenis logam kuningan red brass 85% Cu dan 15% Zn, Cartridge brass 70% Cu dan 30% Zn, yellow brass yang mengandung 65% Cu dan 35 % Zn. Dalam penelitian ini, paduan yang digunakan yaitu Cu-15Zn-1,5Sn yang dihasilkan dengan menggunakan metode pengecoran gravitasi dan kemudian dihomogenisasi pada temperatur 800 °C selama 2 jam. Kemudian dilakukan proses pengerolan dingin dengan variasi reduksi ketebalan 20, 40, dan 70 % lalu dilanjutkan dengan proses anil dengan variasi temperatur 300, 400, 500, dan 600 °C selama 30 menit. Karakterisasi yang dilakukan dalam penelitian ini adalah uji keras metode Vickers untuk mengetahui nilai kekerasan, uji korosi metode weighloss untuk mengetahui ketahanan korosi, dan pengamatan struktur mikro dengan menggunakan mikroskop optik untuk mengetahui struktur dan morfologi dari paduan yang digunakan dalam penelitian ini. Dari hasil penelitian ini, dapat diketahui bahwa proses pengerolan dapat meningkatkan nilai kekerasan dari semula 53,9 VHN pada kondisi as-homogenized, meningkat setelah dilakukan pengerolan dingin dengan reduksi ketebalan 20, 40, dan 70 % dengan nilai kekerasan berturut-turut yaitu 124,56, 146,88, 208,76 VHN. Selain itu, proses pengerolan dingin juga meningkatkan ketahanan korosi pada paduan dari yang semula 9,54 mpy menjadi 4,77 mpy setelah dilakukan proses pengerolan dingin dengan ketiga variasi reduksi ketebalan tersebut. Proses anil yang dilakukan terbukti dapat menurunkan nilai kekerasan dan semakin menurun seiring meningkatnya temperatur yang digunakan untuk proses anil tersebut. ABSTRACT Aril Giri Surya, Effect of Cold Rolling and Annealing on the Hardness and Corrosion Resistance of Cu-15Zn-1,5Sn. Thesis. Jakarta: Mechanical Engineering Education Study Program, Faculty of Engineering, Universitas Negeri Jakarta, 2024. Brass is a copper base alloy were containing Cu and Zn. Copper is main compound of brass alloy. Amount of Zinc effecting the color of brass. There are so many types of brass alloy depending on Zinc amount such as red brass (85 % Cu and 15 % Zn), Cartridge Brass (70 % Cu and 30 % Zn), and yellow brass which contain 65% Cu and 35 % Zn. In this research Cu15Zn-1.5Sn were used and obtained from gravity casting process and then homogenized 800 °C at 2 h. And then, the samples was rolled at several thickness reduction variation at 20, 40, and 70 %, respectively. The samples was annealed at 300, 400, 500, and 600 °C for 30 minutes. Material characterization were used in this research is Vickers hardness test to obtain harness values of the samples, weight loss method to obtain corrosion resistance value, and optical microscope to know alloy structure and morphologies. As the result of this research, can be concluded that cold rolling process can affecting hardness value of the sample from 53.9 VHN at homogenized condition increased after cold rolling process at 20, 40, and 70 % thickness reduction to 124.56, 146.88, and 208.76 VHN, respectively. Furthermore, cold rolling process was effected on corrosion resistance of the alloy from 9.54 mpy at homogenized condition to 4.77 mpy at cold rolled condition. Annealing process was proved can decreasing hardness values and more decreased along increasing of annealing temperature. Keywords: red brass, cold rolling, annealing, corrosion, hardness.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Imam Basori, M.T. 2). Drs. Sopiyan, M.Pd.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 24812 not found.
Date Deposited:	06 Aug 2024 03:22
Last Modified:	06 Aug 2024 03:22
URI:	http://repository.unj.ac.id/id/eprint/48605

Actions (login required)

View Item