STUDI PENGARUH HMT DAN NH3 TERHADAP MORFOLOGI NANOSTRUCTURE ZnO YANG DISINTESIS MENGGUNAKAN METODE HIDROTERMAL DAN PENGARUHNYA TERHADAP FOTODEGRADASI RHODAMINE-6G

SHAFA RAHMA CYRILLA, . (2024) STUDI PENGARUH HMT DAN NH3 TERHADAP MORFOLOGI NANOSTRUCTURE ZnO YANG DISINTESIS MENGGUNAKAN METODE HIDROTERMAL DAN PENGARUHNYA TERHADAP FOTODEGRADASI RHODAMINE-6G. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER - DAFTAR GAMBAR.pdf Download (2MB)
	Text BAB I.pdf Download (1MB)
	Text BAB II.pdf Restricted to Repository staff only Download (2MB) | Request a copy
	Text BAB III.pdf Restricted to Repository staff only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Repository staff only Download (4MB) | Request a copy
	Text BAB V.pdf Restricted to Repository staff only Download (464kB) | Request a copy
	Text LAMPIRAN & DAFTAR RIWAYAT HIDUP.pdf Restricted to Repository staff only Download (4MB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (3MB)

Abstract

ABSTRAK Pada penelitian ini, dilakukan sintesis tiga nanostruktur ZnO melalui dua tahapan. Tahapan pertama yaitu deposisi lapisan benih (seeding layer) menggunakan metode Ultrasonic Spray Pyrolysis (USP) dan tahapan kedua adalah deposisi nanostruktur ZnO dengan metode hidrotermal. Hasil karakterisasi FE-SEM menunjukkan bahwa nanostruktur ZnO yang terbentuk memiliki morfologi nanofower, nanorod, dan flower-rod ZnO. Hasil karakterisasi XRD mengonfirmasi bahwa struktur kristal ZnO adalah polikristal heksagonal wurtzite. Hasil karakterisasi Spektrofotometer UV-Vis yaitu semua nanostructures ZnO menunjukkan penyerapan yang kuat dan reflektansi yang rendah di wilayah UV, serta reflektansi yang kuat pada wilayah cahaya tampak. Adapun celah pita energi flower-rod menunjukkan nilai tertinggi. Selanjutnya hasil uji fotokatalis menunjukkan bahwa nanoflower ZnO merupakan fotokatalis terbaik untuk mendegradasi rhodamine-6G, sedangkan flower-rod ZnO tidak terlalu efektif sebagai fotokatalis *****   ABSTRACT In this research, the synthesis of three ZnO nanostructures was carried out through two stages. The first stage is seeding layer deposition using Ultrasonic Spray Pyrolysis (USP) method and the second stage is ZnO nanostructure deposition using hydrothermal method. FE-SEM characterization results show that the ZnO nanostructures formed have nanofower, nanorod, and flower-rod ZnO morphologies. XRD characterization results confirmed that the ZnO crystal structure is hexagonal wurtzite polycrystal. The UV-Vis Spectrophotometer characterization results are that all ZnO nanostructures show strong absorption and low reflectance in the UV region, as well as strong reflectance in the visible light region. The energy band gaps of flower-rod show the largest value. Furthermore, the photocatalyst test results show that nanoflower ZnO is the best photocatalyst to degrade rhodamine-6G, while flower-rod ZnO is not very effective as a photocatalyst.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Prof. Dr. Iwan Sugihartono, M.Si 2). Rahmat Setiawan Mohar, S.T, M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 24730 not found.
Date Deposited:	15 Aug 2024 04:23
Last Modified:	15 Aug 2024 04:23
URI:	http://repository.unj.ac.id/id/eprint/50020

Actions (login required)

View Item