PENGARUH VARIASI RAPAT ARUS TERHADAP PEMBENTUKAN DAN KARAKTERISASI LAPISAN KOMPOSIT Ni-TiN DENGAN METODE ELEKTRODEPOSISI

MUHAMMAD RISHADI, . (2022) PENGARUH VARIASI RAPAT ARUS TERHADAP PEMBENTUKAN DAN KARAKTERISASI LAPISAN KOMPOSIT Ni-TiN DENGAN METODE ELEKTRODEPOSISI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI_Muhammad Rishadi_Yang sudah di sahkan (1).pdf Restricted to Registered users only Download (4MB)

Abstract

Telah dilakukan analisis pengaruh variasi rapat arus terhadap lapisan komposit Ni-TiN, variasi yang digunakan yaitu 0,4 mA/mm2, 0,6 mA/mm2, dan 0,8 mA/mm2. Proses elektrodeposisi dengan menggunakan suhu sebesar 45℃ dan waktu pelapisan selama 30 menit. Sampel dianalisis morfologi dan komposisinya menggunakan SEM-EDS. Selanjutnya sampel dianalisis dengan X-Ray Diffraction (XRD) untuk mengetahui struktur kristal dan ukuran kristal, software yang digunakan untuk mengolah data XRD adalah HighscorePlus. Kemudian dapat dianalisa bahwa struktur kristal pada fasa Ni-TiN adalah Hexagonal. Ukuran kristal Ni-TiN meningkat dari rentang rapat arus 0,4mA/mm2 sampai 0,6 mA/mm2 yaitu ukuran kristalnya dari 32,682 nm sampai 48,936 nm. Dan ukuran kristal menurun di rapat arus 0,8 mA/mm2 sebesar 24,543 nm. Selanjutnya sampel diuji kekerasan menggunakan alat uji vickers, dan mendapatkan nilai kekerasan 781,7913 HV pada rapat arus 0,4 mA/mm2, kekerasan meningkan pada rapat arus 0,6 mA/mm2 sebesar 1112,3545 HV dan menurun pada rapat arus 0,8 mA/mm2 sebesar 589,39011 HV. Dengan ini bahwa dapat dianalisa hubungan antara ukuran kristal dan kekerasan berbanding lurus. ********************************* An analysis of the effect of current density variations on the Ni-TiN composite layer has been carried out, the variations used are 0.4 mA/mm2, 0.6 mA/mm2, and 0.8 mA/mm2. The electrodeposition process uses a temperature of 45℃ and a coating time of 30 minutes. The samples were analyzed for morphology and composition using SEM-EDS. Furthermore, the samples were analyzed by X-Ray Diffraction (XRD) to determine the crystal structure and crystal size, the software used to process XRD data was HighscorePlus. Then it can be analyzed that the crystal structure of the Ni-TiN phase is Hexagonal. The crystal size of Ni-TiN increased from the current density range of 0.4 mA/mm2 to 0.6 mA/mm2, namely the crystal size from 32.682 nm to 48.936 nm. And the crystal size decreased at a current density of 0.8 mA/mm2 of 24,543 nm. Furthermore, the sample was tested for hardness using the Vickers test equipment, and obtained a hardness value of 781.7913 HV at a current density of 0.4 mA/mm2, hardness increased at a current density of 0.6 mA/mm2 by 1112.3545 HV and decreased at a current density of 0, 8 mA/mm2 of 589.39011 HV. With this it can be analyzed the relationship between crystal size and hardness is directly proportional.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Esmar Budi, M.T. ; 2). Iwan Sugihartono, M.Si.
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Pendidikan Kimia
Depositing User:	sawung yudo
Date Deposited:	14 Nov 2024 01:27
Last Modified:	14 Nov 2024 01:27
URI:	http://repository.unj.ac.id/id/eprint/52058

Actions (login required)

View Item