SINTESIS ZEOLIT A DARI KAOLIN BANGKA DAN APLIKASINYA SEBAGAI ECOWASH LAUNDRYBALL

NUURUR RIZQA ALIYA, . (2022) SINTESIS ZEOLIT A DARI KAOLIN BANGKA DAN APLIKASINYA SEBAGAI ECOWASH LAUNDRYBALL. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. COVER.pdf Download (229kB)
	Text 2. LEMBAR PENGESAHAN.pdf Download (464kB)
	Text 3. LEMBAR PERNYATAAN ORISINALITAS.pdf Download (322kB)
	Text 4. ABSTRAK.pdf Download (363kB)
	Text 5. ABSTRACT.pdf Download (359kB)
	Text 6. KATA PENGANTAR.pdf Download (262kB)
	Text 7. DAFTAR ISI, TABEL, GAMBAR, LAMPIRANN.pdf Download (556kB)
	Text 8. BAB 1.pdf Download (388kB)
	Text 9. BAB 2.pdf Restricted to Registered users only Download (1MB)
	Text 10. BAB 3.pdf Restricted to Registered users only Download (475kB)
	Text 11. BAB 4.pdf Restricted to Registered users only Download (1MB)
	Text 12. BAB 5.pdf Restricted to Registered users only Download (258kB)
	Text 13. DAFTAR PUSTAKA.pdf Download (506kB)
	Text 14. LAMPIRAN.pdf Restricted to Registered users only Download (2MB)
	Text 15. RIWAYAT HIDUP.pdf Restricted to Registered users only Download (373kB)
	Text 16. LEMBAR PERSETUJUAN PUBLIKASI.pdf Download (499kB)

Abstract

Tren dalam produk pembersih rumah tangga telah berkembang tidak hanya untuk memenuhi keuntungan ekonomis namun juga ramah lingkungan dan praktis sekaligus. Berdasarkan fakta tersebut, produk deterjen yang mampu menjawab semua keuntungan tersebut sangat dibutuhkan. Ecowash laundryball berbahan dasar zeolit A dinilai sebagai jawaban yang tepat karena selain ramah lingkungan, Indonesia juga memiliki kelimpahan bahan baku zeolit sintesis. Zeolit A secara luas dikenal sebagai bahan pengganti posfat pada deterjen didasari pada kemampuan sebagai penukar kation yang tinggi sertatidak membahayakan kesehatandan lingkungan. Untuk memperoleh zeolit A dengan kristalinitas optimum, zeolit A dari kaolin Bangka disintesis dengan metode hidrotermal pada 3 jam, 5 jam, 7 jam, 9 jam, dan 12 jam. Serbuk ‘Zeo Deterjen’ kemudian dipadatkan dengan campuran metakaolin teraktivasi sebagai perekat anorganik dan setaqua sebagai perekat organik untuk memperoleh ecowash laundryball dengan ketahanan mekanis yang optimum. Sampel kemudian dikarakterisasi dengan XRD, FT-IR, SEM-EDX, Uji Tekan, dan Uji Susut Massa. Didapati zeolit A dengan waktu hidrotermal 5 jam menunjukan tingkat kristalinitas optimum pada 47%, adapun ecowash laundryball dengan rasio zeolit/perekat sebesar 50:50 menunjukan kekuatan mekanik optimum pada 1,91Mpa dan susut massa minimum sebesar 3,6%. ********************************************* The trend in household cleaning products is growing not only to fulfill the economical advantages but also environtmental friendly and practical aspects. Due to those facts, detergent product that could fulfill all those adventageous is required. Ecowash laundryball made from Zeolite A is the answer of the requirement due to the eco-friendly aspect and abundanity of zeolite raw material in Indonesia.Zeolite A is widely known as posphate substitute in detergent due to its great cation exchange capacity, harmless to human body, and so for the environtment. In order to get the optimum crystallinity degree, zeolite A from Bangka Kaolin was synthesized under hydrotermal method at 3h, 5h, 7h, 9h, and 12h . The ‘zeo-detergent’ powder then compacted by combination of activated metakolin as inorganic binder and setaqua as organic binder in order to create ecowash laundryball with high mechanical strength. Samples then characterized by XRD, FT-IR, SEM-EDX, pressure test, and mass loss test. Zeolite with 5 hours hydrotermal time shows the most optimum crystallinity at 47%, while ecowash laundryball with 50:50 zeolite/binder ratio shows optimum pressure strength at 1,91Mpa and 3,6% of mass loss.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Agung Purwanto, M.Si. ; 2). Arif Rahman, M.Sc.
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	PKL .
Date Deposited:	14 Nov 2024 02:37
Last Modified:	14 Nov 2024 02:37
URI:	http://repository.unj.ac.id/id/eprint/52093

Actions (login required)

View Item