STUDI EKSPERIMENTAL PENGUJIAN KUAT TEKAN DAN KUAT LENTUR PADA BETON DENGAN PENGGUNAAN LIMBAH BETON DAN SERAT KAIN PERCA KATUN JEPANG (SEBAGAI IMPLEMENTASI MATA KULIAH TEKNOLOGI BETON)

WARDAH AL JUFRI, . (2025) STUDI EKSPERIMENTAL PENGUJIAN KUAT TEKAN DAN KUAT LENTUR PADA BETON DENGAN PENGGUNAAN LIMBAH BETON DAN SERAT KAIN PERCA KATUN JEPANG (SEBAGAI IMPLEMENTASI MATA KULIAH TEKNOLOGI BETON). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (999kB)
[img] Text
BAB 1.pdf

Download (338kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (520kB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (547kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (703kB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (307kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (365kB)
[img] Text
LAMPIRAN PENILITIAN.pdf
Restricted to Registered users only

Download (1MB) | Request a copy

Abstract

ABSTRAK Kegiatan pembangunan di Indonesia dapat diprediksikan akan terus meningkat setiap tahunnya, Kegiatan tersebut dapat menimbulkan adanya limbah konstruksi. Struktur bangunan yang saat ini dominan menggunakan beton sehingga membuat limbah beton semakin banyak akibat kegiatan pembongkaran bangunan. Salah satu solusi untuk mengurangi limbah konstruksi terutama beton yaitu dapat dilakukan penggunaan kembali limbah beton. Beton memiliki kuat tekan yang tinggi namun memiliki kuat tarik yang rendah. Penambahan serat dalam adukan beton dapat meningkatkan kuat tarik beton. Serat yang digunakan dapat berupa serat alami seperti selulosa, rami, bambu, kelapa dan sisal. Berdasarkan alasan tersebut, penelitian ini dilakukan untuk mengetahui nilai kuat tekan dan kuat lentur beton dengan penggunaan limbah beton sebagai pengganti agregat serta penambahan serat kain katun Jepang pada beton. Limbah beton digunakan sebagai pengganti seluruh agregat termasuk agregat kasar dan agregat halus. Variasi pemakaian serat katun Jepang dalam sampel beton adalah 0% (sebagai beton kontrol), 0,5% dan 1 % dari berat beton. Dilakukan pengujian kuat tekan umur 7 hari dan 28 hari, pengujian kuat tarik pada umur 28 hari dengan menggunakan benda uji silinder dengan diameter 3 in dan tinggi 6 in. Pada pengujian kuat tarik menggunakan benda uji berbentuk balok dengan ukuran 10 × 10 × 30 cm. Diharapkan dengan penggunaan limbah beton dan kain katun Jepang dapat meningkatkan kuat tekan dan kuat tarik pada beton. Dari hasil pengujian kuat tekan rata-rata beton umur 7 hari dengan variasi serat 0% (beton kontrol) adalah 8,97 MPa, variasi 0,5% adalah 10,27 MPa dan variasi 1% adalah 5,34 MPa. Pengujian kuat tekan rata-rata beton umur 28 hari dengan variasi serat 0% (beton kontrol) adalah 10,27 MPa, variasi 0,5% adalah 11 MPa dan variasi 1% adalah 6,23 MPa. Berdasarkan hasil uji kuat tarik rata-rata umur 28 hari didapatkan rata-rata dengan variasi serat 0% (beton kontrol) adalah 8,97 MPa, variasi 0,5% adalah 10,27 MPa dan variasi 1% adalah 5,34 MPa . Kuat lentur yang didapatkan pada beton kontrol yaitu sebesar 3,52 MPa, variasi serat 0,5% sebesar 3,76 MPa dan variasi serat 1% 2,92 MPa. Kata Kunci : Beton Serat, Katun Jepang, Kuat Tekan, Kuat Lentur, Limbah Beton ***** Abstract Development activities in Indonesia can be predicted to continue to increase every year, these activities can cause construction waste. Building structures that are currently dominantly using concrete make more concrete waste due to building demolition activities. One solution to reduce construction waste, especially concrete, is to be able to reuse concrete waste. Concrete has high compressive strength but has low tensile strength. The addition of fiber in concrete mix can increase the tensile strength of concrete. The fiber used can be natural fibers such as cellulose, hemp, bamboo, coconut and sisal. Based on these reasons, this study was conducted to determine the compressive strength and flexural strength of concrete by using concrete waste as a substitute for aggregate and the addition of Japanese cotton fabric fibers to concrete. Concrete waste is used as a substitute for the whole aggregate including coarse aggregate and fine aggregate. The variations in the use of Japanese cotton fibers in concrete samples were 0% (as control concrete), 0.5% and 1% of the weight of the concrete. Compressive strength tests were carried out at the age of 7 days and 28 days, tensile strength tests at the age of 28 days using cylindrical test specimens with a diameter of 3 in and a height of 6 in. In the tensile strength test, a block-shaped test specimen with a size of 10 × 10 × 30 cm. It is hoped that the use of waste concrete and Japanese cotton fabric can increase the compressive strength and tensile strength of concrete. From the results of the average compressive strength test of 7-day-old concrete with a 0% fiber variation (control concrete) is 8.97 MPa, a 0.5% variation is 10.27 MPa and a 1% variation is 5.34 MPa. The average compressive strength test of 28-day-old concrete with 0% fiber variation (control concrete) was 10.27 MPa, 0.5% variation was 11 MPa and 1% variation was 6.23 MPa. Based on the results of the 28-day average tensile strength test, the average was obtained with a 0% fiber variation (control concrete) of 8.97 MPa, a variation of 0.5% was 10.27 MPa and a variation of 1% was 5.34 MPa. The bending strength obtained in the control concrete was 3.52 MPa, the 0.5% fiber variation was 3.76 MPa and the 1% fiber variation was 2.92 MPa. Keywords : Fiber Concrete, Japanese Cotton, Compressive Strength, Bending Strength, Waste Concrete

Item Type: Thesis (Sarjana)
Subjects: Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions: FT > S1 Pendidikan Teknik Bangunan
Depositing User: Users 27221 not found.
Date Deposited: 05 Mar 2025 01:20
Last Modified: 05 Mar 2025 01:20
URI: http://repository.unj.ac.id/id/eprint/54638

Actions (login required)

View Item View Item