SETYO PRABOWO, . (2025) ANALISIS PENGARUH UKURAN MESH DAN TEMPERATUR SAMPAH PLASTIK HDPE (HIGH DENSITY POLYETHYLENE) TERHADAP UJI TEKAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.
![]() |
Text
cover.pdf Download (1MB) |
![]() |
Text
BAB 1.pdf Download (776kB) |
![]() |
Text
BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy |
![]() |
Text
BAB 3.pdf Restricted to Registered users only Download (806kB) | Request a copy |
![]() |
Text
BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy |
![]() |
Text
BAB 5.pdf Restricted to Registered users only Download (705kB) | Request a copy |
![]() |
Text
DAFTAR PUSTAKA.pdf Download (772kB) |
![]() |
Text
LAMPIRAN DAN RIWAYAT HIDUP (2).pdf Restricted to Registered users only Download (1MB) | Request a copy |
Abstract
Masalah sampah plastic semakin penting untuk ditangani seiring dengan meningkatnya populasi dan konsumsi manusia. Sampah dibagi menjadi organik dan anorganik, dengan plastik sebagai masalah utama karena proses dekomposisinya yang lambat. Berbagai inovasi, seperti pengembangan mesin pencetak plastik, telah dikembangkan untuk mengatasi limbah plastik secara lebih efektif. Fokus penelitian ini adalah untuk menganalisis pengaruh ukuran 2 mm (mesh 10), 4 mm (mesh 5), 6 mm (mesh 3), 8 mm (mesh 2) dan temperatur pemanasan (110°C, 120°C, 130°C) terhadap kekuatan tekan produk plastik HDPE yang sudah didaur ulang. Dengan pemahaman yang lebih baik mengenai pengaruh faktor-faktor ini, diharapkan dapat ditemukan cara yang optimal dalam meningkatkan kualitas produk daur ulang plastik HDPE. Tujuan dari penelitian ini adalah untuk mengidentifikasi dan menganalisis pengaruh variasi ukuran mesh dan temperatur terhadap kekuatan tekan material HDPE yang didaur ulang. Metode penelitian yang digunakan adalah pendekatan eksperimen kuantitatif, di mana sampel plastik HDPE dipotong dengan variasi ukuran mesh dan dipanaskan pada tiga temperatur yang berbeda, kemudian diuji dengan mesin uji tekan kompresi sesuai dengan standar ISO 604. Penelitian ini juga mengevaluasi interaksi antara ukuran mesh dan temperatur pemanasan dalam mempengaruhi hasil uji tekan. Hasil penelitian menunjukkan bahwa ukuran yang lebih kecil (2 mm dan 4 mm) menghasilkan kekuatan tekan yang lebih tinggi dibandingkan ukuran mesh yang lebih besar (6 mm dan 8 mm). Selain itu, temperatur pemanasan optimal untuk kekuatan tekan terbaik ditemukan pada suhu 120°C, di mana material HDPE memiliki struktur yang lebih homogen dan padat. Suhu yang lebih tinggi (130°C) menyebabkan degradasi material yang mengurangi kekuatan tekan. Berdasarkan temuan ini, penelitian ini menyarankan penggunaan ukuran mesh 4 mm pada temperatur 120°C sebagai kondisi yang optimal untuk menghasilkan produk dengan kekuatan tekan terbaik. Kata Kunci: High-Density Polyethylene (HDPE), Mesh, Plastik, Tekan, Temperatur.******The problem of plastic waste is increasingly important to address along with the increasing population and human consumption. Waste is divided into organic and inorganic, with plastic being the main problem due to its slow decomposition process. Various innovations, such as the development of plastic molding machines, have been developed to deal with plastic waste more effectively. The focus of this study is to analyze the effect of mesh size 2 mm (mesh 10), 4 mm (mesh 5), 6 mm (mesh 3), 8 mm (mesh 2) and heating Temperature (110°C, 120°C, 130°C) on the compressive strength of recycled HDPE plastic products. With a better understanding of the influence of these factors, it is hoped that an optimal way can be found to improve the quality of recycled HDPE plastic products. The purpose of this study was to identify and analyze the effect of variations in mesh size and Temperature on the compressive strength of recycled HDPE materials. The research method used is a quantitative experimental approach, where HDPE plastic samples were cut with various mesh sizes and heated at three different Temperatures, then tested with a compression test machine according to ISO 604 standards. This study also evaluated the interaction between mesh size and heating Temperature in influencing the results of the compression test. The results showed that smaller sizes (2 mm and 4 mm) produced higher compressive strength than larger mesh sizes (6 mm and 8 mm). In addition, the optimal heating Temperature for the best compressive strength was found at 120°C, where the HDPE material has a more homogeneous and dense structure. Higher Temperatures (130°C) cause material degradation which reduces the compressive strength. Based on these findings, this study suggests the use of a 4 mm mesh size at a Temperature of 120°C as the optimal condition to produce products with the best compressive strength. Keywords: High-Density Polyethylene (HDPE), Mesh, Plastic, Press, Temperature.
Item Type: | Thesis (Sarjana) |
---|---|
Additional Information: | 1). Dr. Eko Arif Syaefudin, S.T. M.T. ; 2). Ahmad Kholil, S.T., M.T. |
Subjects: | Teknologi dan Ilmu Terapan > Manufaktur |
Divisions: | FT > D IV Teknologi Rekayasa Manufaktur |
Depositing User: | Users 27172 not found. |
Date Deposited: | 05 Mar 2025 05:02 |
Last Modified: | 05 Mar 2025 05:02 |
URI: | http://repository.unj.ac.id/id/eprint/54668 |
Actions (login required)
![]() |
View Item |