PEMANFAATAN LIMBAH ABU TEMPURUNG KELAPA DENGAN PRESENTASE 0%, 9%, 10%, 11%, DAN 12% SEBAGAI BAHAN TAMBAH TERHADAP BERAT SEMEN DALAM PEMBUATAN PAVING BLOCK

DAFFA NABHAN, . (2025) PEMANFAATAN LIMBAH ABU TEMPURUNG KELAPA DENGAN PRESENTASE 0%, 9%, 10%, 11%, DAN 12% SEBAGAI BAHAN TAMBAH TERHADAP BERAT SEMEN DALAM PEMBUATAN PAVING BLOCK. Diploma thesis, UNIVERSITAS NEGERI JAKARTA.

	Text Cover_Draft Laporan Skripsi _Daffa Nabhan_150652001..pdf Download (930kB)
	Text Bab 1_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Download (306kB)
	Text Bab 2_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Restricted to Registered users only Download (3MB) | Request a copy
	Text Bab 3_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Restricted to Registered users only Download (883kB) | Request a copy
	Text Bab 4_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text Bab 5_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Restricted to Registered users only Download (296kB) | Request a copy
	Text Daftar Pustaka_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Download (269kB)
	Text Lampiran_Draft Laporan Skripsi _Daffa Nabhan_1506520010.pdf Restricted to Registered users only Download (4MB) | Request a copy

Abstract

Daffa Nabhan (2024) Pemanfaatan Limbah Abu Tempurung Kelapa Dengan Presentase 0%,9%,10%,11%, dan 12% Sebagai Bahan Tambah Terhadap Berat Semen Dalam Pembuatan Dalam Paving Block. Banyaknya limbah abu tempurung kelapa yang terdapat di pasar kebayoran lama untuk itu bagaimanakah pemanfaatan limbah abu tempurung kelapa tersebut dalam pembuatan paving block, apakah sesuai dengan acuan SNI 03-0691-1996 yang digunakan. Abu tempurung kelapa hasil pembakaran suhu 400°. Pembuatan di Pabrik Maju Bersama Jl. Lurah Namat No.53, Jatirangga, Kec. Jatisampurna, Kota Bekasi, dimensi 21cm x 10,5cm x 8 cm, perbandingan semen dan pasir 1: 4 : 0,3 FAS dan jumlah sampel 20 buah. Penelitian ini bertujuan untuk mengetahui penggunaan bahan tambah abu tempurung kelapa dengan presentase 0%,9%,10%,11%,dan 12% pada paving block dalam SNI 03-0691-1996. Metodologi penelitian ini RnD model 4D (Define, Design, Development, and Dissemination). Hasil penyerapan air 0% (6,402%) mutu III, 9% (5,592%) ,10% (4,771%), dan 11%( 3,870%) mutu II, dan12%(2,672%) mutu I. Uji kuat tekan 0%(18,516 Mpa),9% (18,359 Mpa),(18,594 Mpa),11%(20,156 Mpa) dan 12%(21,172 Mpa) mutu II sebagai pelataran parkir, uji natrium sulfat 0% (0,335%), 9%(0,332%), 10%(0,563%), 11%(0,396%), dan 12% (0,508%) memenuhi SNI 03-0691-1996. Uji ketahanan aus 0% (0,0725%), 9% (0,0998%), 10% (0,0766%), 11% (0,0620%), dan 12% (0,0957%) mutu I dapat digunakan untuk jalan. Penelitian pemanfaatan limbah abu tempurung kelapa yang terdapat dari pasar Kebayoran Lama dapat digunakan pada penelitian ini, dengan presentase 0%, 9%, 10%, 11% dan 12% sebagai bahan tambah terhadap berat semen dalam pembuatan paving block memenuhi SNI 03-0691-1996. Kata Kunci : Abu Tempurung Kelapa, Semen, Paving Block ***** Daffa Nabhan (2024) Utilization of Coconut Shell Ash Waste with a Percentage of 0%, 9%,10%,11%, and 12% as an Additive to the Weight of Cement in Making Paving Blocks. There is a large amount of coconut shell ash waste found in the Kebayoran Lama market, so how is the use of coconut shell ash waste in making paving blocks, is it in accordance with the SNI 03-0691-1996 reference used. Coconut shell ash resulting from burning at 400°. Manufacturing at the Maju Bersama Factory Jl. Head of Namat Village No. 53, Jatirangga, Kec. Jatisampurna, Bekasi City, dimensions 21cm x 10.5cm x 8 cm, cement and sand ratio 1: 4 : 0.3 FAS and number of samples 20 pieces. This research aims to determine the use of coconut shell ash additives with percentages of 0%, 9%, 10%, 11%, and 12% in paving blocks in SNI 03-0691-1996. The research methodology is RnD 4D model (Define, Design, Development, and Dissemination). Water absorption results were 0% (6.402%) quality III, 9% (5.592%), 10% (4.771%), and 11% (3.870%) quality II, and 12% (2.672%) quality I. Compressive strength test 0% (18,516 Mpa),9% (18,359 Mpa),(18,594 Mpa),11%(20,156 Mpa) and 12% (21.172 Mpa) quality II for parking lots, sodium sulfate test 0% (0.335%), 9% (0.332%), 10% (0.563%), 11% (0.396%), and 12% ( 0.508%) meets SNI 03-0691-1996. Wear resistance test 0% (0.0725%), 9% (0.0998%), 10% (0.0766%), 11% (0.0620%), and 12% (0.0957%) of quality I can be used for roads. Research on the use of coconut shell ash waste from the Kebayoran Lama market can be used in this research, as an added material with a percentage of 0%, 9%, 10%, 11% and 12% of the weight of cement in making paving blocks that meet SNI 03-0691- 1996. Keyword : Coconut, Shell, Ash, Cement, Paving Blocks

Item Type:	Thesis (Diploma)
Additional Information:	1). Anisah, M.T. ; 2). Lenggogeni, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > D IV Teknologi Rekayasa Konstruksi Bangunan Gedung
Depositing User:	Users 27161 not found.
Date Deposited:	05 Mar 2025 06:42
Last Modified:	05 Mar 2025 06:42
URI:	http://repository.unj.ac.id/id/eprint/54757

Actions (login required)

View Item