PENGARUH PENAMBAHAN ALUMINIUM TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK PADUAN KUNINGAN Cu-28Zn-2Mn-xAl.

NAGA BONAR SINAGA, . (2020) PENGARUH PENAMBAHAN ALUMINIUM TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK PADUAN KUNINGAN Cu-28Zn-2Mn-xAl. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (3MB)
[img] Text
BAB 1.pdf

Download (360kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (3MB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 5.pdf

Download (341kB)
[img] Text
DAFTAR PUSTAKA.pdf

Download (437kB)
[img] Text
LAMPIRAN.pdf

Download (5MB)

Abstract

Kuninganmerupakanlogampaduanantaratembaga(Cu)danSeng (Zn). Kuningan memilikikekuatan, keuletan, ketahanankorosi, sifatmampu bentukdan mampumesinyang baik.Cartridgebrassadalahpaduankuningandengan komposisi70%Cu dan 30%Zn.Sifat mekanisCartridge Brass dapat ditingkatkan denganmenambahkanunsur paduanlain,struktur mikro, ujikomposisikimia,uji kekerasan, dan ujitarik.Penelitianinidilakukanuntukmengetahuipengaruh penambahanvariasi aluminium(Al)0,2%Al,0,5%Al,1%Al,denganteknikpengecorangravitasipada paduankuninganCu-28Zn-2Mnterhadapstruktur mikro dansifatmekanik.Selain itupenelitianakandilanjutkandenganproseshomogenisasipadatemperatur8000C denganpenahananwaktuselama2jamdanmediapendinginanudararuang.Setelah itu dilanjutkan denganpengujian komposisikimiadengan menggunakanOptical Emission Spectrometry(OES), pengujian kekerasandengan menggunakanmetode Vickers dan pengujiantarik dengan menggunakanstandar spesimen ASTME8.Hasilpengujianmenunjukkanbahwavariasipenambahanaluminium(Al)0,2% Aldan0,5% Altidakterjadiperubahansignifikanterhadapstruktur mikro. Namunpada penambahan1% Almulaiterlihatadanyafasa β.Penambahan1% Al secarakaraktermemilikikekuatandankekerasanyangpalingtinggidibanding0,2%Aldan0,5%Al.Halinidikarenakansifatfasaβyang kerasdibandingkan denganfasa α.Nilaikekerasanpada setiapsampelmenunjukkanpenurunanpada kekerasansetelahdihomogenisasi.Haltersebutsesuaidenganteoriyang ada bahwa homogenisasi,dapatmenurunkannilaikekerasanmaterial.Darihasildata penelitiandisimpulkanbahwa penambahanAldanproseshomogenisasi mempengaruhi strukturmikro dan sifat mekanikpaduan kuningan Cu-28Zn-2Mn. Brassisanalloymetalofcopper(Cu)andzinc(Zn).Brasshasthestrength, tenacity,corrosionresistance,nature capable of shape andcapable ofgood machining.Thebrasscartridgeisanbrassalloywithacompositionof70%Cuand30%Zn.The mechanicalpropertiesof theBrassCartridgecanbeenhancedby addingotheralloyelements,microstructures,chemicalcompositiontests,hardness tests, and tensiletesting.Thisresearchwas conductedtodeterminethe effectof addingvariationsof aluminum(Al)0.2%Al,0.5%Al,1%Al,bycastinggravitytechniquesonCu-28Zn-2Mnbrassalloysonmicrostructure andmechanicalproperties.Inaddition, theresearchwillcontinuewiththehomogenizationprocessat800oCwithaholding timeof2hoursandroomaircooling media.Afterthatproceedwithchemical compositiontesting usingOpticalEmissionSpectrometry(OES),hardnesstesting usingthe Vickers method and tensile testingusingstandard ASTM E8 specimens.Thetestresultsshowedthatthevariationofaluminum(Al)additionof0.2% Aland0.5%Aldidnotmakeany significantchangestothemicrostructure,butat the additionof 1% Albegantoappear the βphase.The additionof 1%Alhasthe higheststrengthandhardnesscharacteristiccomparedto0.2%Aland0.5%Al.This isdue tothe hard nature of the βphase comparedtothe α phase.Thevalue of violenceineachsampleshowsadecreaseinviolenceafterhomogenization.Thisis consistentwiththeexistingtheory thathomogenizationcanreducethevalueof materialviolence.Fromthe resultsof the researchdata itwasconcludedthatthe additionof Alandthehomogenizationprocessaffectedthemicrostructure and mechanical properties ofthe Cu-28Zn-2Mn brassalloy

Item Type: Thesis (Sarjana)
Additional Information: 1). Dr. Imam Basori, S.T., M.T. ; 2). Siska Titik Dwiyati, S.Si., M.T.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Users 2047 not found.
Date Deposited: 11 Mar 2020 16:37
Last Modified: 11 Mar 2020 16:37
URI: http://repository.unj.ac.id/id/eprint/5672

Actions (login required)

View Item View Item