PENGARUH VARIASI PENAMBAHAN SERBUK Zn PADA Al DENGAN/TANPA DIBUNGKUS Al FOIL SAAT PROSES PENGECORAN TERHADAP KOMPOSISI YANG TERBENTUK SERTA LAJU KOROSI DALAM LARUTAN 3,5% NaCl

DARIN FEBRIANI, . (2025) PENGARUH VARIASI PENAMBAHAN SERBUK Zn PADA Al DENGAN/TANPA DIBUNGKUS Al FOIL SAAT PROSES PENGECORAN TERHADAP KOMPOSISI YANG TERBENTUK SERTA LAJU KOROSI DALAM LARUTAN 3,5% NaCl. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text File Cover.pdf Download (1MB)
	Text File BAB 1.pdf Download (394kB)
	Text File BAB 2.pdf Restricted to Registered users only Download (664kB) | Request a copy
	Text File BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text File BAB 4.pdf Restricted to Registered users only Download (678kB) | Request a copy
	Text File BAB 5.pdf Restricted to Registered users only Download (377kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (370kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Aluminium (Al) adalah logam yang banyak digunakan dalam industri transportasi, termasuk perkapalan, karena ringan dan tahan korosi. Al memiliki kekuatan yang rendah sehingga perlu dipadukan dengan unsur lain. Untuk meningkatkan sifat mekaniknya, unsur Zinc (Zn) ditambahkan saat proses pengecoran. Namun, komposisi Zn cenderung hilang akibat penguapan saat pemanasan. Oleh karena itu, Al foil digunakan sebagai pembungkus untuk meminimalkan kehilangan Zn dan menjaga komposisi material. Selain itu, kapal yang terpapar air laut menghadapi risiko korosi, terutama pada bagian seperti baling-baling yang terbuat dari Al. Penelitian ini bertujuan mengevaluasi pengaruh variasi penambahan serbuk Zn pada Al, baik dengan maupun tanpa pembungkusan Al foil, terhadap komposisi dan laju korosi dalam larutan 3,5% NaCl. Metode yang digunakan dalam penelitian ini adalah eksperimen dengan fokus pada proses pengecoran Al yang dipadukan dengan serbuk Zn dengan atau tanpa dibungkus Al foil. Variasi penambahan Zn yang digunakan adalah 2wt.%, 5wt.%, dan 10wt.%. Uji komposisi dilakukan menggunakan metode X-ray Fluorescence (XRF) dan uji ketahanan korosi dilakukan dengan metode weight loss selama 960 jam dalam larutan NaCl 3,5% dan waktu pengambilan data pengurangan berat dilakukan setiap 480 jam. Hasil penelitian menunjukkan bahwa semua spesimen menunjukkan peningkatan kadar Zn seiring dengan peningkatan rasio Zn dalam paduan. Spesimen yang dibungkus dengan Al foil memiliki kadar Zn yang lebih tinggi dibandingkan dengan spesimen yang tidak dibungkus Al foil. Selain itu, spesimen Al memiliki laju korosi terendah, yaitu 0,0326 mm/y, yang menunjukkan ketahanan korosi yang baik. Penambahan Zn cenderung meningkatkan laju korosi pada paduan. Kata kunci: Gravity casting, Weight loss, X-ray Fluorescence (XRF) ***** Aluminum (Al) is a metal that is widely used in the transportation industry, including shipping, because it is lightweight and corrosion resistant. Al has low strength, so it needs to be alloyed with other elements. To improve its mechanical properties, zinc (Zn) is added during the casting process. However, the Zn composition tends to evaporate during heating. Therefore, Al foil is used as a wrapper to minimize Zn loss and maintain the material composition. Additionally, ships exposed to seawater face corrosion risks, particularly on parts like propellers made of aluminum. This study aims to evaluate the effect of varying zinc powder additions to aluminum, both with and without aluminum foil wrapping, on composition and corrosion rate in a 3.5% NaCl solution. The method used in this study is an experiment focusing on the Al casting process combined with Zn powder with or without Al foil wrapping. The variations in Zn addition used are 2wt.%, 5wt.%, and 10wt.%. Composition testing was performed using the X-ray Fluorescence (XRF) method, and corrosion resistance testing was conducted using the weight loss method over 960 hours in a 3.5% NaCl solution, with weight loss data collected every 480 hours. The results of the study showed that all specimens exhibited an increase in Zn content as the Zn ratio in the alloy increased. Specimens wrapped in Al foil had higher Zn content compared to those not wrapped in Al foil. Additionally, Al specimens exhibited the lowest corrosion rate, 0.0326 mm/y, indicating good corrosion resistance. Adding Zn tends to increase the corrosion rate in the alloy. Keywords: Gravity casting, Weight loss, X-ray Fluorescence (XRF)

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ferry Budhi Susetyo, M.T., M.Si. ; 2). Drs. H. Syamsuir, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Users 28045 not found.
Date Deposited:	30 Jul 2025 02:52
Last Modified:	30 Jul 2025 02:52
URI:	http://repository.unj.ac.id/id/eprint/56957

Actions (login required)

View Item