PENGARUH VARIASI KOMPOSISI FLY ASH, PERLITE, DENGAN TAMBAHAN POLYPROPYLENE FIBER TERHADAP KRISTALINITAS DAN KUAT TEKAN BETON GEOPOLIMER TIDAK DIBAKAR DAN DIBAKAR PADA TEMPERATUR 900°C

ABDUL GANI, . (2025) PENGARUH VARIASI KOMPOSISI FLY ASH, PERLITE, DENGAN TAMBAHAN POLYPROPYLENE FIBER TERHADAP KRISTALINITAS DAN KUAT TEKAN BETON GEOPOLIMER TIDAK DIBAKAR DAN DIBAKAR PADA TEMPERATUR 900°C. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (1MB)
[img] Text
BAB 1.pdf

Download (298kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (562kB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (256kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (282kB)
[img] Text
LAMPIRAN.pdf
Restricted to Registered users only

Download (1MB) | Request a copy

Abstract

Kebakaran merupakan bencana yang menyebabkan korban jiwa dan kerugian material. Oleh karena itu, dibutuhkan sistem proteksi kebakaran pasif untuk menahan penyebaran api dengan fokus pada ketahanan struktur bangunan melalui kompartemen kebakaran. Beton konvensional berbahan dasar semen portland menghasilkan emisi CO₂ sebesar 5-8% dari total aktivitas manusia, sehingga diperlukan pengembangan material alternatif yang ramah lingkungan. Beton geopolimer dikembangkan sebagai pengganti semen portland dengan memanfaatkan material yang mengandung silika dan alumina tinggi serta memiliki ketahanan pada temperatur tinggi. Penelitian ini menggunakan komposisi fly ash dan perlite sebagai pengganti semen portland karena bersifat pozzolan dengan kandungan silika dan alumina tinggi, ditambahkan polypropylene fiber untuk meningkatkan kekuatan mekanik, serta larutan NaOH dan Na₂SiO₃ sebagai alkali aktivator. Material yang digunakan meliputi fly ash tipe F dari PLTU Pelabuhan Ratu, perlite dari Sumatera Barat, polypropylene fiber dari PT. SIKA, dan alkali aktivator larutan natrium hidroksida 6 molar. Penelitian dilakukan dengan 5 variasi komposisi fly ash, perlite, dan polypropylene fiber yang mengalami perlakuan curing selama 28 hari dalam kondisi tidak dibakar dan dibakar pada temperatur 900°C selama 2 jam. Pengujian meliputi kuat tekan menggunakan compression testing machine dan analisis karakteristik kristalinitas menggunakan X-Ray Diffraction (XRD). Hasil penelitian menunjukkan bahwa Komposisi 2 dengan rasio 75% fly ash : 25% perlite dan tambahan polypropylene fiber merupakan komposisi terbaik berdasarkan analisis ke-lima komposisi yang direncanakan. ***** Fire is a disaster that causes both casualties and material losses. Therefore, a passive fire protection system is needed to prevent the spread of fire, focusing on the structural integrity of buildings through fire compartments. Conventional concrete based on Portland cement contributes 5–8% of total human-related CO₂ emissions, prompting the need for environmentally friendly alternative materials. Geopolymer concrete has been developed as a substitute for Portland cement by utilizing materials rich in silica and alumina and is known for its high-temperature resistance. This study uses a combination of fly ash and perlite as a substitute for Portland cement due to their pozzolanic properties and high silica and alumina content. Polypropylene fiber is added to enhance mechanical strength, while NaOH and Na₂SiO₃ solutions are used as alkaline activators. The materials used include Type F fly ash from the Pelabuhan Ratu power plant, perlite from West Sumatra, polypropylene fiber from PT. SIKA, and a 6-molar sodium hydroxide solution. Five different compositions of fly ash, perlite, and polypropylene fiber were prepared, with each sample undergoing 28 days of curing. The specimens were tested in two conditions: unheated and heated at 900°C for 2 hours. The tests included compressive strength using a compression testing machine and crystallinity analysis using X-Ray Diffraction (XRD). The results showed that Composition 2, with a ratio of 75% fly ash to 25% perlite and the addition of polypropylene fiber, was the optimal composition based on the analysis of the five planned mixtures.

Item Type: Thesis (Sarjana)
Additional Information: 1). Fransisca Maria Farida, S.T., M.T. ; 2). Dr. Eko Arif Syaefudin, S.T., M.T.
Subjects: Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Teknologi dan Ilmu Terapan > Teknik Kimia
Divisions: FT > S1 Rekayasa Keselamatan Kebakaran
Depositing User: Abdul Gani .
Date Deposited: 31 Jul 2025 03:59
Last Modified: 31 Jul 2025 03:59
URI: http://repository.unj.ac.id/id/eprint/57046

Actions (login required)

View Item View Item