PENGARUH MANGAN TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK PADUAN KUNINGAN CU-29ZN-0.5AL-XMN DENGAN METODE PENGECORAN GRAVITASI.

RAHMAN FADILLAH, . (2020) PENGARUH MANGAN TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK PADUAN KUNINGAN CU-29ZN-0.5AL-XMN DENGAN METODE PENGECORAN GRAVITASI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
Cover.pdf

Download (1MB)
[img] Text
BAB I.pdf

Download (383kB)
[img] Text
BAB II.pdf

Download (685kB)
[img] Text
BAB III.pdf

Download (1MB)
[img] Text
BAB IV.pdf

Download (2MB)
[img] Text
BAB V.pdf

Download (325kB)
[img] Text
Daftar Pustaka.pdf

Download (296kB)
[img] Text
Lampiran.pdf

Download (4MB)

Abstract

ABSTRAK Rahman Fadillah. Pengaruh Mangan Terhadap Struktur Mikro dan Sifat Mekanik Paduan Kuningan Cu-29Zn-0.5Al-xMn dengan Metode Pengecoran Gravitasi. Jakarta: Program Studi Pendidikan Vokasional Teknik Mesin, Fakultas Teknik, Universitas Negeri Jakarta, 2020. Kuningan (CuZn) merupakan paduan tembaga dan seng, dengan tembaga sebagai logam paduan utama. Kuningan memiliki kekuatan, keuletan, ketahanan korosi yang tinggi dan mempunyai sifat mampu bentuk yang baik. Karena sifatnya, logam kuningan (CuZn) memiliki banyak kegunaan, misalnya untuk pembuatan selongsong munisi untuk senjata api. Selongsong munisi terbuat dari logam paduan kuningan cartridge brass, yaitu logam paduan antara unsur tembaga dan seng dengan komposisi 70% tembaga dan 30 % seng. Pada proses pembuatan selongsong munisi tingkat deformasi yang terjadi sangat tinggi. Sehingga, untuk proses ini dibutuhkan paduan kuningan dengan sifat mekanik serta sifat mampu bentuk yang baik. Sifat mekanik dan sifat mampu bentuk dapat ditingkatkan dengan menambahan unsur paduan lain. Pada penelitian ini, dikembangkan paduan kuningan Cu-29%berat Zn dengan penambahan 0.5%berat Al serta 1, 2, dan 4%berat Mn. Sampel dibuat dengan metode pengecoran gravitasi. Karakterisasi material yang dilakukan meliputi pengujian komposisi kimia menggunakan Optical Emission Spectrometry (OES), pengujian kekerasan menggunakan metode Vickers dan juga pengujian tarik dengan menggunakan standar spesimen ASTM E8. Dari hasil penelitian, penambahan 1.62% berat unsur mangan terhadap paduan kuningan Cu-28Zn-0.5Al memunculkan fasa baru yaitu fasa β. Nilai kekerasan, nilai kekuatan tarik (ultimate tensile strength), kekuatan luluh (yield strength), dan elongasi (elongation) cenderung meningkat seiring dengan peningkatan kadar Mn, dimana nilai kekerasan serta nilai kekuatan baik tarik maupun luluh tertinggi terdapat pada kandungan Mn sebesar 1.62 % berat. Kata Kunci : Paduan kuningan, cartridge brass, mangan, Pengecoran gravitasi. ABSTRACT Rahman Fadillah. Effect of Manganese on Micro Structure and Mechanical Properties of Cu-29Zn-0.5Al-xMn Brass Alloy by Gravity Casting Method. Jakarta: Mechanical Engineering Vocational Education Study Program, Faculty of Engineering, Jakarta State University, 2020. Brass (CuZn) is an alloy of copper and zinc, with copper as the main alloy. Brass has strength, tenacity, high corrosion resistance and has good formability. Because of its nature, brass metal (CuZn) has many uses, for example for the manufacture of munition casings for firearms. The munition cartridge is made of brass cartridge brass, which is an alloy of copper and zinc with a composition of 70% copper and 30% zinc. In the process of making munitions casings the level of deformation that occurs is very high. Thus, for this process, brass alloys with mechanical properties and good formability are required. Mechanical properties and formability can be improved by adding other alloying elements. In this research, Cu-29% by weight of Zn was added with 0.5% by weight of Al and 1, 2, and 4% by weight of Mn. Samples were made by gravity casting method. Material characterization includes chemical composition testing using Optical Emission Spectrometry (OES), hardness testing using the Vickers method and also tensile testing using ASTM E8 standard specimens. From the results of the study, the addition of 1.62% by weight of the manganese element to the Cu-28Zn-0.5Al brass alloy gave rise to a new phase, the β phase. The value of hardness, the value of tensile strength (ultimate tensile strength), yield strength and elongation tended to increase with increasing levels of Mn, where the value of hardness and the value of both tensile and yield strength were highest in the Mn content of 1.62% weight. Keywords: Brass alloy, cartridge brass, manganese, Gravity casting.

Item Type: Thesis (Sarjana)
Additional Information: 1). Dr. IMAM BASORI, M.T ; 2). Ir. YUNITA SARI, M. T.,M.Si
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Users 2060 not found.
Date Deposited: 09 Apr 2020 22:01
Last Modified: 09 Apr 2020 22:01
URI: http://repository.unj.ac.id/id/eprint/5743

Actions (login required)

View Item View Item