KARAKTERISTIK KEKUATAN TEKAN DAN KEAUSAN PADA KOMPOSIT SERAT BATANG PISANG DAN SERBUK BAMBU

EBID WILDAN SHOLEHAN, . (2025) KARAKTERISTIK KEKUATAN TEKAN DAN KEAUSAN PADA KOMPOSIT SERAT BATANG PISANG DAN SERBUK BAMBU. Other. Ebid Wildan Sholehan.

[img] Text
COVER.pdf

Download (3MB)
[img] Text
BAB 1.pdf

Download (219kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (605kB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (614kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (944kB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (185kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (232kB)
[img] Text
LAMPIRAN.pdf
Restricted to Registered users only

Download (1MB) | Request a copy

Abstract

Penelitian ini adalah untuk menganalisis kekuatan tekan dan ketahanan keausan komposit yang terbuat dari kombinasi Serat Batang Pisang dan Serbuk Bambu, serta memahami interaksi antara kedua bahan tersebut dalam meningkatkan sifat mekanik komposit. Metode penelitian yang digunakan adalah eksperimen, di mana spesimen komposit dibuat dengan menggunakan variasi komposisi Serat Batang Pisang dan Serbuk Bambu, sementara komposisi Resin dijaga tetap sebesar 60%. Lima variasi komposisi diuji menggunakan standar ASTM D695 untuk kekuatan tekan dan ASTM G99-17 untuk keausan. Pengujian dilakukan untuk menentukan kekuatan tekan menggunakan mesin uji tekan dengan mesin Unconfined Composite Strenght (UCS), dan ketahanan keausan diuji dengan metode tribometer menggunakan mesin Pin-On-Disc.Hasil pengujian menunjukkan bahwa komposit dengan kandungan Serat Batang Pisang tertinggi komposisi 1 (K1: 40% Serat Batang Pisang) memiliki kekuatan tekan tertinggi sebesar 17,77 MPa. Sebaliknya, komposit dengan kandungan Serbuk Bambu tertinggi komposisi 5 (K5: 40% Serbuk Bambu) menunjukkan kekuatan tekan terendah, yaitu 10,69 MPa. Uji keausan menunjukkan hasil optimal pada komposisi seimbang komposisi 3 (K3: 20% Serat Batang Pisang dan 20% Serbuk Bambu) dengan rata-rata kehilangan massa sebesar 0,0183 gram. Analisis SEM mengungkapkan bahwa distribusi filler yang merata serta ikatan antarpartikel yang baik berkontribusi terhadap peningkatan sifat mekanik. Penelitian ini menunjukkan bahwa kombinasi antara Serat Batang Pisang dan Serbuk Bambu dapat menghasilkan komposit dengan performa mekanik yang optimal dan berpotensi digunakan sebagai bahan alternatif pada komponen otomotif, seperti kampas rem.***** This study aims to analyze the compressive strength and wear resistance of composites made from a combination of banana stem fibers and bamboo powder, as well as to understand the interaction between these two materials in enhancing the mechanical properties of the composite. The research method used is experimental, where composite specimens were fabricated using varying compositions of banana fiber and bamboo powder, while maintaining the Resin content at a constant 60%. Five composition variations were tested according to ASTM D695 for compressive strength and ASTM G99-17 for wear resistance. The compressive strength was measured using a compression testing machine with the Unconfined Composite Strength (UCS) method, while wear resistance was tested using a tribometer with a Pin-On-Disc apparatus. The test results showed that the composite with the highest banana fiber content, composition 1 (K1: 40% banana fiber), exhibited the highest compressive strength at 17.77 MPa. In contrast, the composite with the highest bamboo powder content, composition 5 (K5: 40% bamboo powder), showed the lowest compressive strength at 10.69 MPa. The wear test yielded optimal results in the balanced composition, composition 3 (K3: 20% banana fiber and 20% bamboo powder), with an average mass loss of 0.0183 grams. SEM analysis revealed that uniform filler distribution and good interparticle bonding contributed to improved mechanical properties. This study demonstrates that the combination of banana fiber and bamboo powder can produce composites with optimal mechanical performance and has the potential to be used as an alternative material in automotive components, such as brake pads.

Item Type: Monograph (Other)
Additional Information: 1). Dr. Siska Titik Dwiyati, M.T. ; 2). Dr. Riyadi, M.T.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Teknologi dan Ilmu Terapan > Otomotif, Astronotika
Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Ebid Wildan Sholehan .
Date Deposited: 05 Aug 2025 06:10
Last Modified: 05 Aug 2025 06:10
URI: http://repository.unj.ac.id/id/eprint/57694

Actions (login required)

View Item View Item