ANALISIS PENGARUH VARIASI MEDIA PENDINGIN PROSES HEAT TREATMENT PADA BAJA AISI 4140 TERHADAP KETAHANAN KOROSI DAN KEKERASAN UNTUK APLIKASI HYDRAULIC CYLINDER RODS (PENELITIAN PADA MAHASISWA SEMESTER VIII TAHUN AKADEMIK 2024/2025 JURUSAN PENDIDIKAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS NEGERI JAKARTA)

TEGAR FIRMAN PAMUNGKAS, . (2025) ANALISIS PENGARUH VARIASI MEDIA PENDINGIN PROSES HEAT TREATMENT PADA BAJA AISI 4140 TERHADAP KETAHANAN KOROSI DAN KEKERASAN UNTUK APLIKASI HYDRAULIC CYLINDER RODS (PENELITIAN PADA MAHASISWA SEMESTER VIII TAHUN AKADEMIK 2024/2025 JURUSAN PENDIDIKAN TEKNIK MESIN FAKULTAS TEKNIK UNIVERSITAS NEGERI JAKARTA). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. Cover.pdf Download (780kB)
	Text 2. Bab 1.pdf Download (289kB)
	Text 3. Bab 2.pdf Restricted to Registered users only Download (560kB) | Request a copy
	Text 4. Bab 3.pdf Restricted to Registered users only Download (542kB) | Request a copy
	Text 5. Bab 4.pdf Restricted to Registered users only Download (637kB) | Request a copy
	Text 6. Bab 5.pdf Restricted to Registered users only Download (277kB) | Request a copy
	Text 7. Daftar Pustaka.pdf Download (252kB)
	Text 8. Lampiran dan Daftar Riwayat Hidup.pdf Restricted to Registered users only Download (557kB) | Request a copy

Abstract

Baja AISI 4140 merupakan baja paduan yang banyak digunakan dalam aplikasi teknik karena memiliki kombinasi kekuatan dan ketahanan aus yang baik. Salah satu metode untuk meningkatkan sifat mekanik dan ketahanan korosi baja ini adalah melalui proses perlakuan panas (heat treatment), khususnya quenching. Penelitian ini bertujuan untuk menganalisis pengaruh variasi media pendingin terhadap kekerasan dan ketahanan korosi baja AISI 4140 untuk aplikasi hydraulic cylinder rods. Proses perlakuan panas dilakukan dengan pemanasan pada suhu 850°C selama 60 menit menggunakan tungku listrik, kemudian dilanjutkan dengan proses quenching menggunakan tiga jenis media pendingin, yaitu aquadest, oli SAE 10W-40, dan larutan garam 5%. Setelah proses quenching, dilakukan pengujian struktur mikro menggunakan mikroskop optik, pengujian kekerasan menggunakan metode Vickers, serta uji korosi dengan metode weight loss dalam larutan NaCl 3,5%. Hasil penelitian menunjukkan bahwa media larutan garam 5% menghasilkan kekerasan tertinggi sebesar 762,4 HV dan laju korosi terendah sebesar 76,03 mpy. Hal ini disebabkan oleh laju pendinginan yang lebih cepat sehingga membentuk struktur martensit yang lebih banyak dan merata. Dengan demikian, larutan garam 5% dinilai sebagai media pendingin paling efektif untuk meningkatkan sifat kekerasan dan ketahanan korosi baja AISI 4140 pada aplikasi hydraulic cylinder rods. ***** AISI 4140 steel is a widely used alloy steel in engineering applications due to its excellent combination of strength and wear resistance. One effective method to enhance its mechanical properties and corrosion resistance is through heat treatment, particularly quenching. This study aims to analyze the effect of different quenching media on the hardness and corrosion resistance of AISI 4140 steel for hydraulic cylinder rod applications. The heat treatment process was conducted by heating the samples at 850°C for 60 minutes using an electric furnace, followed by quenching in three types of media: distilled water, SAE 10W-40 oil, and 5% saline solution. After quenching, the microstructure was examined using an optical microscope, hardness was tested using the Vickers method, and corrosion resistance was evaluated using the weight loss method in 3.5% NaCl solution. The results showed that the 5% saline solution produced the highest hardness value of 762.4 HV and the lowest corrosion rate of 76.03 mpy. This is attributed to the faster cooling rate, which led to a greater and more uniform formation of martensitic structure. Therefore, the 5% saline solution is considered the most effective quenching medium to improve both hardness and corrosion resistance of AISI 4140 steel for hydraulic cylinder rod applications.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Sopiyan, M.Pd. ; 2). Drs. Syaripuddin, M.Pd.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Tegar Firman Pamungkas .
Date Deposited:	06 Aug 2025 00:12
Last Modified:	06 Aug 2025 00:12
URI:	http://repository.unj.ac.id/id/eprint/58214

Actions (login required)

View Item