KARAKTERISTIK KOMPOSIT SERBUK BAMBU DAN SERAT KELAPA SEBAGAI MATERIAL PEREDAM SUARA

RAFLI IRFANSYAH, . (2025) KARAKTERISTIK KOMPOSIT SERBUK BAMBU DAN SERAT KELAPA SEBAGAI MATERIAL PEREDAM SUARA. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (163kB)
	Text BAB II.pdf Restricted to Registered users only Download (422kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (539kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (76kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (159kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penelitian ini adalah untuk menganalisis karakteristik peredaman suara dan nilai koefisien absorbsi pada komposit yang terbuat dari kombinasi serbuk bambu dan serat kelapa serta memahami interaksi antara kedua bahan tersebut dalam meningkatkan sifat mekanik komposit. Metode penelitian yang digunakan adalah eksperimental, dimana spesimen komposit dibuat dengan menggunakan variasi komposisi serbuk bambu dan serat kelapa, sementara komposisi resin tetap sebesar 37,5 %. Tiga variasi komposisi diuji dengan menggunakan standar ASTM E1050 untuk absorbs suara. Hasil pengujian menunjukkan bahwa komposit dengan kandungan Serbuk Bambu tertinggi komposisi 1 (K1 : 62,5% Serbuk Bambu) memiliki koefisien absorbs suara sebesar 0,34 di frekuensi 3500 Hz. Sebaliknya, komposit dengan kandungan Serat Kelapa terendah di komposisi 3 (K3: 62,5% Serat Kelapa) memiliki koefisien absorbsi suara sebesar 0,18 di frekuensi 3500 Hz. Analisis mikro struktur menunjukkan bahwa distribusi filler yang merata serta ikatan antarpartikel yang baik berkorelasi terhadap peningkatan absorbsi suara. Nilai koefisien absorbsi bunyi yang tinggi dimiliki oleh material dengan pori-pori yang lebih kecil. Penelitian ini menunjukkan bahwa kombinasi antara serbuk bambu dan serat kelapa dapat menghasilkan komposit dengan performa absorbsi suara yang optimal dan berpotensi digunakan sebagai bahan alternatif untuk pengganti bahan peredam suara yang sudah ada. *********** This study is to analyze the sound damping characteristics and absorption coefficient values of composites made from a combination of bamboo powder and coconut fiber and to understand the interaction between the two materials in improving the mechanical properties of the composite. The research method used is experimental, where composite specimens were made using various compositions of bamboo powder and coconut fiber, while the resin composition remained at 37.5%. Three composition variations were tested using the ASTM E1050 standard for sound absorption. The test results showed that the composite with the highest Bamboo Powder content, composition 1 (K1: 62.5% Bamboo Powder) had a sound absorption coefficient of 0.34 at a frequency of 3500 Hz. Conversely, the composite with the lowest Coconut Fiber content in composition 3 (K3: 62.5% Coconut Fiber) had a sound absorption coefficient of 0.18 at a frequency of 3500 Hz. Microstructural analysis showed that even distribution of fillers and good interparticle bonds correlated with increased sound absorption. High sound absorption coefficient values were possessed by materials with smaller pores. This research shows that the combination of bamboo powder and coconut fiber can produce a composite with optimal sound absorption performance and has the potential to be used as an alternative material to replace existing soundproofing materials.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Siska Titik Dwiyati, M.T. ; 2). Dr. Riyadi, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Lingkungan, Teknik Sanitasi Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Rafli Irfansyah .
Date Deposited:	08 Aug 2025 01:10
Last Modified:	08 Aug 2025 01:10
URI:	http://repository.unj.ac.id/id/eprint/58383

Actions (login required)

View Item