PENGARUH PROSES PENGEROLAN DINGIN DAN ANIL TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KETAHANAN KOROSI PADA PADUAN KUNINGAN CU-28ZN-1SN

DIMAS HADI PRAHASTO, . (2025) PENGARUH PROSES PENGEROLAN DINGIN DAN ANIL TERHADAP STRUKTUR MIKRO, KEKERASAN DAN KETAHANAN KOROSI PADA PADUAN KUNINGAN CU-28ZN-1SN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (816kB)
	Text BAB I.pdf Download (221kB)
	Text BAB II.pdf Restricted to Registered users only Download (588kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (197kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (212kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (323kB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh proses pengerolan dingin dan anil terhadap struktur mikro, kekerasan, dan ketahanan korosi pada paduan kuningan Cu-28Zn-1Sn. Sampel kuningan diberikan perlakuan pengerolan dingin dengan variasi reduksi ketebalan 20 %, 40 % dan 70%, kemudian dilakukan proses anil pada temperatur 300 ℃, 400 ℃, 500 ℃, dan 600 ℃ masing-masing selama 30 menit. Analisis struktur mikro dilakukan menggunakan mikroskop optik, kekerasan diuji menggunakan metode Vickers, dan ketahanan korosi dianalisis dengan uji weight loss menggunakan media korosi larutan H2SO4. Hasil penelitian menunjukkan bahwa pengerolan dingin meningkatkan kekerasan material akibat pengerolan dingin diikuti dengan meningkatnya ketahanan korosi. Nilai kekerasan paduan meningkat seiring bertambahnya deformasi plastis saat pengerolan dingin 20, 40 dan 70 % masing-masing bernilai 185,4 VHN, 247,2 VHN, dan 254,8 VHN. Sedangkan ketahanan korosi juga meningkat setelah perlakuan anil, ditunjukkan oleh penurunan laju korosi dari 0,119 mmpy (20 %) menjadi 0,112 mmpy (40 %) dan 0,077 mmpy (70 %)., dan Perlakuan anil menurunkan kekerasan secara signifikan pada semua tingkat deformasi, seperti pada deformasi 70% yang turun dari 243,3 VHN (300 °C) menjadi 89,9 VHN (600 °C), serta menurunkan laju korosi, di mana setiap tingkat deformasi menunjukkan penurunan tertinggi pada anil 600 °C dan tertinggi pada 300 °C. Proses anil terbukti mampu mengembalikan ketahanan korosi dan memperbaiki struktur mikro melalui rekristalisasi. ***** This study aims to investigate the effect of cold rolling and annealing processes on the microstructure, hardness, and corrosion resistance of Cu-28Zn-1Sn brass alloy. The brass samples underwent cold rolling with thickness reduction levels of 20%, 40%, and 70%, followed by annealing at temperatures of 300 °C, 400 °C, 500 °C, and 600 °C for 30 minutes each. Microstructural analysis was conducted using an optical microscope, hardness was using the Vickers method, and corrosion resistance was evaluated via weight loss testing in an H₂SO₄ solution. The results showed that cold rolling increased the material's hardness due to plastic deformation and also enhanced corrosion resistance. The alloy's hardness increased with greater deformation during cold rolling 20, 40 and 70 % respectively worth 185.4 VHN, 247.2 VHN, and 254.8 VHN. Corrosion resistance also improved after annealing, as indicated by a decrease in corrosion rate from 0.119 mmpy (20%) to 0.112 mmpy (40%) and 0.077 mmpy (70%). Annealing significantly reduced hardness across all deformation levels—for example, at 70% deformation, the hardness dropped from 243.3 VHN (300 °C) to 89.9 VHN (600 °C)—while also reducing the corrosion rate. Each deformation level showed the lowest corrosion rate at 600 °C and the highest at 300 °C. Annealing was proven to restore corrosion resistance and refine the microstructure through recrystallization.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Imam Basori, M.T. ; 2). Dr. Ferry Budhi Susetyo, M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Dimas Hadi Prahasto .
Date Deposited:	08 Aug 2025 03:25
Last Modified:	08 Aug 2025 03:25
URI:	http://repository.unj.ac.id/id/eprint/59063

Actions (login required)

View Item